http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
이진혁,조남주,배종우,김정수,황태준,박성두,박성한,여태민,김원호 한국고분자학회 2011 Macromolecular Research Vol.19 No.6
Intermittent compression stress relaxation (CSR) testing was used to examine the degradation of a large scale chloroprene rubber (CR) O-ring, rather than a reduced scale copy, as well as predict its life-time. An intermittent CSR jig was designed by considering the O-ring’s environment during use. The testing allowed the observation of the effects of friction, heat loss and stress relaxation by the Mullins effect. Degradation of O-rings by thermal aging was observed between 40 and 120 ℃. In the high temperature range of 80-120 ℃, the O-rings exhibited linear degradation behavior and satisfied the Arrhenius relationship. The activation energy was approximately 72.7 kJ/mol. From the Arrhenius plots, the predicted life-times were 22.8 years and 34.5 years for the 50% and 40% failure conditions,respectively. Using the time-temperature superposition (TTS) principle, full predictions of failure at 40 ℃could be made, saving considerable testing time. Between 40 and 80 ℃, the activation energy decreased to 58.9 kJ/mol. William-Landel-Ferry (WLF) plotting confirmed that the O-rings show non-linear degradation behavior under 80 ℃. The life-time of the O-rings predicted by the TTS principle was 11.1 years and 18.1 years for each failure condition. The life-time predicted by the TTS principle was more conservative than that from the Arrhenius relationship.
정재영(Jaeyoung Chung),강한성(Hansung Kang),고수빈(Subin Ko),김재욱(Jaewook Kim),여태민(Taemin Yeo),이건희(Gunhee Lee) 한국과학영재교육학회 2011 과학영재교육 Vol.3 No.3
본 연구에서는 고등학교 수준에서 다루어질 수 있는 주제로서 문제 해결력을 위한 좋은 과제인 함수방정식을 다루고 있다. 이 분야에서 특히 중요한 위치를 차지하고 있는 방정식인 코시함수방 정식과 그리고 이와 연관된 젠센함수방정식, 펙시드함수방정식, 로그함수방정식 등이 제한된 영역 에서 만족할 때 이 방정식들의 일반해와 정칙해를 구한다. In this paper the authors deal with functional equations which is a good research topic for high school students. In particular, they consider the Cauchy equation, Pexider equation, Jensen equation and logarithmic functional equation satisfied in the complements of rhombi or in the half planes, and find the general solutions and the regular solutions of the equations.
황용석(Yongseok Hwang),이지형(Jihyung Lee),이경훈(Kyunghun Lee),김광연(Kwangyun Kim),이성웅(Sungwoong Lee),여태민(Taemin Yeo) 한국추진공학회 2011 한국추진공학회 학술대회논문집 Vol.2011 No.11
알루미늄 분말과 물의 연소 특성을 연구하기 위한 장치를 고안하였다. 알루미늄 분말의 점화를 포함한 연소특성은 초기온도, 압력, 당량비등에 의존하게 되므로 이러한 인자를 변화시켜 연소환경을 적응시킬 수 있는 장치를 설계하였다. 연소 시험 장치는 메탄 연소기, 물공급장치, 알루미늄 분말 정량 공급장치, 선형 형태의 연소기 및 제어장치로 구성되어 있다. 각각의 장치들은 필요한 물질을 정량적으로 공급할 수 있는 기능을 가지고 있으며, 정해진 시험 과정에 따라 자동으로 제어될 수 있도록 설계되었다. 제작된 장치를 시운전하여 각 구성품이 정상작동하였을 때, 알루미늄 분말이 연소되는 것을 확인할 수 있었다. The device for studying combustion characteristic of aluminum powder and water was developed. The device has ability to adjust temperature, pressure, and equivalent ratio to some specified value which effect on combustion characteristic of aluminum and water mixture. Methane combustor, water supply device, aluminum powder feeder, and linear combustor are assembled to aluminum combustion test device. Each device has the ability to supply matter to combustor on steady and quantitatively controlled manner and test sequence specified by user can be automatically controlled. The combustion of aluminum powder was observed when integrated device was operated normally.
간헐 압축응력 완화와 시간-온도 중첩 원리를 이용한 FKM 오링의 수명 예측 연구
이진혁 ( Jin Hyok Lee ),배종우 ( Jong Woo Bae ),김정수 ( Jung Su Kim ),황태준 ( Tae Jun Hwang ),박성두 ( Sung Doo Park ),박성한 ( Sung Han Park ),여태민 ( Yeo Tae Min ),김원호 ( Won Ho Kim ),조남주 ( Nam Ju Jo ) 한국고무학회 2010 엘라스토머 및 콤포지트 Vol.45 No.4
간헐 CSR 측정법을 이용하여 FKM 오링의 노화 거동과 수명 예측에 관하여 연구하였다. Intermittent CSR 지그는 오링의 실제 사용환경을 고려하여 설계 제작하였다. 각 측정 조건에 따른 마찰 영향, 열 손실 영향 및 Mullins 효과에 의한 간헐 CSR의 응력 거동 변화를 관찰하였다. 오링의 노화 거동은 60~160 ℃에서의 가속 노화 연구를 통하여 관찰하였다. 고온 영역(100~160 ℃)에서 오링은 선형 노화 거동을 나타내었으며, 아레니우스 관계를 만족시켰다. 이때의 활성화 에너지는 60.2 kJ/mol로 나타났다. 아레니우스 도식으로 부터, 오링의 예측 수명은 고장 조건 50%와 40%에 대하여 각각 43.3 년과 69.6 년으로 나타났다. 시간-온도 중첩 원리를 이용하여 60 ℃에서의 노화 거동을 관찰하였으며, 실험 시간을 절약 할 수 있었다. 60~100 ℃의 저온 영역에서의 활성화 에너지는 48.3 kJ/mol로 감소하였다. WLF(William-Landel-Ferry) 도식을 통하여 FKM 오링은 100 ℃ 이하에서 비선형 노화 거동을 나타내 는 것을 확인하였다. 시간-온도 중첩 원리로부터, FKM 오링의 수명은 고장 조건 50%와 40%에 대하여 각각 19.1년 과 25.2년으로 나타났다. 시간-온도 중첩 원리를 이용하여 예측한 오링의 수명이 아레니우스 관계에 의한 수명 보다 보수적인 것으로 나타났다. Intermittent CSR testing was used to investigate the degradation of an FKM O-ring, also the prediction of its life-time. An intermittent CSR jig was designed taking into consideration the O-ring`s environment under use. The testing allowed observation of the effects of friction, heat loss, and stress relaxation by the Mullins effect. Degradation of O-rings by thermal aging was observed between 60 and 160 ℃. In the high temperature of range (100-160 ℃) O-rings showed linear degradation behavior and satisfied the Arrhenius relationship. The activation energy was about 60.2 kJ/mol. From Arrhenius plots, predicted life-times were 43.3 years and 69.9 years for 50% and 40% failure conditions, respectively. Based on TTS (time-temperature superposition) principle, degradation was observed at 60 ℃, and could save testing time. Between 60 and 100 ℃ the activation energy decreased to 48.3 kJ/mol. WLF(William-Landel-Ferry) plot confirmed that O-rings show non-linear degradation behavior under 80 ℃. The life-time of O-rings predicted by TTS principle was 19.1 years and 25.2 years for each failure condition. The life-time predicted by TTS principle is more conservative than that from the Arrhenius relationship.