플라즈마 용사용 $Al_2O_3/SS316$ 복합 분말 제조 및 경사 코팅충의 제조에 관한 연구
민재웅,송병길,김삼중,노재승,서동수 대한용접접합학회 2002 대한용접·접합학회지 Vol.20 No.2
In the case of using high temperature by coating ceramic/metal, large stress was produced due to difference of thermal expansion coefficient between those. And then lead to delamination. In order to relaxation of the stress A1$_2$O$_3$/SS316 composite powders with $10wt.%Al_2O_3$ compositional gradient and $10wt.%Al_2O_3$ agglomerated powder were made by spray drying method. These powders were sintered to improve the strength and to be plasma sprayed in order to fabricate the FGC(functionally graded coating). The influence of gun power, working distance and Ar pressure on the microstructure of the coating layer was studied in order to optimize the plasma spray conditions. It was proven that the optimum conditions were 40kw gun power, 5cm working distance and $100ft^3/h$ Ar flow for both powders. FGC with 10 compositional steps was fabricated and the total thickness was 1.3mm. FGC was heat treated at $1100^{\circ}C$for 10hours to evaluate the heat resisting characteristics.
분무건조법에 의한 용사용 원적외선 세라믹/AI 복합분말제조 및 용사층의 특성
홍성준,김병희,민재웅,송병길,노재승,서동수,Hong, Seong-Jun,Kim, Byeong-Hui,Min, Jae-Ung,Song, Byeong-Gil,No, Jae-Seung,Seo, Dong-Su 한국재료학회 1999 한국재료학회지 Vol.9 No.12
분무건조법으로 용사용 원적외선 세라믹/알루미늄 복합분말을 제조하여 플라즈마 용사법으로 알루미늄 모재에 용사한 후, 미세구조, 결정상, 열충격저항성 그리고 분광복사율을 조사하였다. 분무건조된 복합분말의 입형은 구형으로 34~105${\mu}m $. 영역에서 높은 복사율을 보였다. 그러나 알루미늄 첨가량이 증가할수록 원적외선 방사특성은 감소하였다. 결과적으로 용사법으로 원적외선 방사특성의 큰 손실 없이 방사체를 제조하기 위해서는 20~30%wt%Al를 첨가하여 복합분말을 제조하는 것이 가장 효율적이라고 판단된다. Far infrared ceramic/aluminum composite powders for thermal spray were fabricated by spray drying method and investigated the characteristics of the plasma sprayed coating layers, I.e. microstructure, phases, thermal shock resistance and spectral emissivity. The shape of the spray dried composite powder was spherical and the particle size distribution was 34~105${\mu}m $. Aluminum was distributed homogeneously in the spray dried composite powder. Spectral emissivity of the plasma sprayed coating layer ranges from 3 to 14${\mu}m $ whereas spectral emissivity of the raw ceramic powder ranges from 8 to 14${\mu}m $. And then spectral emissivity of the coatings was better than that of the raw powder but spectral emissivity was decreased with increasing aluminum content. It was found that aluminum content ranging from 20 to 30wt% was suitable for fabricating far-infrared radiator by plasma spraying method.