수열합성법에 의한 반도성 나노 (Ba<sub>1-x</sub>Sb<sub>x</sub>)TiO<sub>3</sub> 분말제조 및 PTCR 특성평가
최용각,이종현,이혁희,원창환,Choe, Yong-Gak,Lee, Jong-Hyeon,Lee, Hyeok-Hui,Won, Chang-Hwan 한국재료학회 2002 한국재료학회지 Vol.12 No.3
Semiconductive nano $(Ba_{1-x}Sb_x)TiO_3$ powders were synthesized by the hydrothermal process and Sb was simultaneously doped in the hydrothermal condition. $(Ba_{1-x}Sb_x)TiO_3$ powders obtained from optimum condition(at 20$0^{\circ}C$ for 3hr) exhibited spherical shape, high purity and nano size. The PTCR characteristics was observed when 0.1 and 0.2 mole% Sb were added and sintered at over 130$0^{\circ}C$ for 1 hour, respectively. And The ceramics exhibit the PTCR characteristics with a resistively jump $ratio($\rho$_{max}/$\rho$_{min})$ of about $10^4$. Also we found that PTCR characteristics were dependent on the microstructure.
산 침출$Mg^{++}$액으로부터 $Mg(OH)_2$및 MgO 粉末의 製造
최용각,이종현,원창환,이갑호 한국자원리싸이클링학회 2001 資源 리싸이클링 Vol.10 No.5
자전연소고온반응법(SHS)에 의한 고순도 분말의 제조시에 주로 얻어지는 $Mg^{++}$ 유 부산물로부터 초미분 $Mg(OH)_2$및 MgO분말을 제조하였다 $Mg(OH) _2$제조시 최적의 실험 조건은 0.7M의 $Mg^{++}$ 을 함유하는 pH 1.42의 산침출 용액중에 9M의 KOH를 pH조절제로 첨가한 경우이다. 이때 pH는 약 13.0을 나타내며, 모든 $Mg^{++}$ 이 $Mg(OH)_2$로 침전되었다. $Mg(OH)_2$의 탈수반응을 조사하기 위하여 DSC를 사용하였으며, 그 결과를 하소공정에 사용하였다. MgO분말은 건조된 Mg(OH)2 분말을 $400-450^{\circ}C$로 하소함으로써 제조되었으며, 제조된 $Mg(OH)_2$및 MgO분말의 크기 및 형상은 상용 분말과 유사하였다. Ultrafine $Mg(OH)l_2$and MgO powders were recovered from the waste solution containing $Mg^{++}$ which was a by-product of SHS (Self-propagating High temperature Synthesis)process. The optimum experimental conditions to prepare $Mg(OH)_2$were 13.0 of pH and 0.7M of $Mg^{++}$ content with addition of 9M of KOH as a pH regulator in acid leaching solution. Complete pre-cipitation of Mg(OH)$_2$from $Mg^{++}$ was realized at that condition. The dehydration reaction of the prepared Mg(OH)$_2$was studied by DSC, and the result was used for calcination process. In order to obtain MgO powder, dried Mg(OH)2 powder was calcined at $400~450^{\circ}C$. Particle size and shape of the prepared $Mg(OH)_2$and MgO powder was similar to those of the commercial powders.
E-4WD HEV의 전, 후륜 모터 동력분배에 대한 연구
최용각(Yongkak Choi),김철수(Chulsu Kim),박종진(Jeonjin Park) 한국자동차공학회 2004 한국자동차공학회 춘 추계 학술대회 논문집 Vol.- No.-
In the Toyota ESTIMA HEV with E-4WD system, it was necessary to determine the rear motor torque about front motor torque to allow practical 4WD performance. This paper discusses the torque distribution ratio of front and rear motor. <br/> In the energy efficiency, the rear motor can increase regenerative braking energy and in the vehicle stability. ESTIMA HEV applies rear motor to be practical 4WD. In this paper, we discuss the power distribution of rear motor fur assisting and regenerating of E-4WD HEV.
하이브리드차량의 연비향상을 위한 경제 운전 제어 기술 개발에 관한 연구
최용각(Yongkak Choi),정원영(Wonyoung Jeong),박일권(IlKwon Park),양채모(Chaemo Yang),강재훈(Jaehoon Kang) 한국자동차공학회 2010 한국자동차공학회 부문종합 학술대회 Vol.2010 No.5
Hybrid vehicles, which have higher fuel economy and system efficiency than conventional vehicles, have been an attracting attention worldwide including various advantages. These advantages include low emissions of greenhouse gases and, little influence, on the ozone layer directly or indirectly. LPI HEV recently developed by HMC performs with torque and fuel economy of the same level as conventional gasoline hybrid vehicles by employing the world’s first liquid-state-injection system for exclusive use of LPG. In particular, control strategy improving fuel economy of the HEV is expected to help cope with future regulations relating to environmental protection from exhaust fumes
수열합성법에 의한 정방정 BaTiO<sub>3</sub> 분말의 생성속도 및 유전특성
이종현,최용각,원창환,김채성 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.7
Formation rate of tetragonal BaTiO$_3$powder by hydrothermal synthesis and its dielectric property were studied. Submicron tetragonal BaTiO$_3$ powders were prepared hydrothermally, using Ba(OH)$_2$.8$H_2O$, TiO$_2$(anatase) and KOH as starting chemicals. Characterization via X-ray diffractometry, field emission scanning electron microscopy confirmed that increasing calcination temperatures(from 1100 to 130$0^{\circ}C$) promotes the formation of tetragonal BaTiO$_3$. Tetragonal BaTiO$_3$ ceramics, obtained by calcining at 1200 for 3 h after hydrothermal synthesis at 200 for 168 h, exhibited submicron size of 0.5 ~ 0.7 ${\mu}{\textrm}{m}$ and high relative permittivity. 수열합성법에 의한 정방정 BaTiO$_3$ 분말의 생성속도 및 유전특성에 대해서 연구하였다. 초미립 BaTiO$_3$분말의 합성을 위한 출발물질로는 Ba(OH)$_2$. 8$H_2O$, TiO$_2$(anatase)가 사용되었으며, 광화제로써 KOH가 사용되었다. 수열합성은 20$0^{\circ}C$의 온도에서 1~168시간동안 이루어 졌으며, 정방정상으로의 상전이를 관찰하기 위하여 1100~130$0^{\circ}C$의 온도로 하소처리 하였다. 최적의 조건(20$0^{\circ}C$에서 168시간동안 수열합성 된 분말을 120$0^{\circ}C$에서 3시간 하소한 분말)에서 얻어진 분말은 0.5~0.7$mu extrm{m}$ 정도의 분말이었으며, 유전특성 평가결과 고유전율 재료로써 적합함을 알 수 있었다.
수열합성법에 의한 정방정 BaTiO3 분말의 생성속도 및 유전특성
이종현,최용각,원창환,김채성 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.7
Formation rate of tetragonal BaTiO3 powder by hydrothermal synthesis and its dielectric property were studied. Submicron tetragonal BaTiO3 powders were prepared hydrothermally, using Ba(OH)2·8H2O, TiO2(anatase) and KOH as starting chemicals. Characterization via X-ray diffractometry, Field emission scanning electron microscopy confirmed that increasing calcination temperatures(from 1100 to 1300 ) promotes the formation of tetragonal BaTiO3. Tetragonal BaTiO3 ceramics, obtained by calcining at 1200 for 3hrs after hydrothermal synthesis at 200 for 168hrs, exhibited submicron size of 0.5∼0.7 ㎛ and high relative permittivity. 수열합성법에 의한 정방정 BaTiO3 분말의 생성속도 및 유전특성에 대해서 연구하였다. 초미립 BaTiO3 분말의 합성을 위한 출발물질로는 Ba(OH)2·8H2O, TiO2(anatase)가 사용되었으며, 광화제로써 KOH가 사용되었다. 수열합성은 200 의 온도에서 1∼168시간동안 이루어 졌으며, 정방정상으로의 상전이를 관찰하기 위하여 1100∼1300 의 온도로 하소처리 하였다. 최적의 조건(200 에서 168시간동안 수열합성 된 분말을 1200 에서 3시간 하소한 분말)에서 얻어진 분말은 0.5∼0.7 ㎛정도의 분말이었으며, 유전특성 평가결과 고유전율 재료로써 적합함을 알 수 있었다.