열형광선량계에 관한 연구

채건식,김영국,손인호,노경석 경남대학교 신소재연구소 1995 論文集 Vol.5 No.-

본 연구에서는 CaSO₄에 활성체로 전이원소인 Tm, Dy, V, Mo을 첨가하여 CaSO₄ : Tm, Dy, V, Mo 열형광에를 제작하였다. 주 peak는 불순물의 농도와 온도에 따라 CaSO₄ : Tm, Dy, V, Mo의 열형광 glow curve에서 구하였다. 활성화에너지는 peak shape 법으로 구하였는데 각각의 불순물에서 1.5eV, 1.25eV, 0.8eV, 1.17eV를 얻었다. 그리고 CaSO₄: Tm, Dy, V, Mo 열형광체는 peak shape 법으로 분석해 본 결과가 모두 2차 발광이었다. CaSO₄: V, Mo 열형광체가 X-선에 가장 감도가 좋았으며, 1-100 Rad의 X-선을 조사하였을 때 열형광감도는 선량의존성을 보였다. The principle of dose measurement by thermoluminescent dosimeter(TLD) was investigated. CaSO₄:Tm. Dy. V. Mo thermoluminescent phosphor has been prepared by sintering the CaSO₄after doping the transition elements Tm, Dy. V. Mo. The maximum peaks are found in the measured CaSO4 Tm. Dy. V. Mo TL glow curve at impurity mol% and annealing temperature. The activation energy of main peak has been estimated by the peak shape method. The estimated activation energies are 1.5 eV. 1.25 eV. 0.8 eV. and 1.17 eV. respectively. The thermoluminescence process in CaSO₄: Tm. Dy. V. Mo are found t o the 2nd order when the main peak of the glow curve is analyzed by the peak shape method. CaSO₄: V. Mo thermolunescent phosphor is the most sensitive to X-rays among the other materials. The dose responses of CaSO₄: Tm. Dy. V. Mo TLD are linear up to 1 - 1000 Rad of X-rays.

이상적인 측정환경이 아닌 장소에서 Headphone Audiocup의 부착유무가 현장 근로자의 청력검사에 미치는 영향

채경석,구정완,이원철 가톨릭대학교 산업의학센터 2000 韓國의 産業醫學 Vol.39 No.4

The purpose of this study was to assess the effect of headphone audiocup. The subjects were composed of workers of noise-exposed population. The noise level of workplace was over 85 dB. They were examined otoscopic test and audiometry of 1,000 Hz and 4,000 Hz. The data were analysed according to wearing audiocups for 612 subjects in -59 years of age and major results are as follows : 1.Hearing thresholds of group audiocups were significantly decreased than that of non-audiocups in -19, 20-29, 40-49 and 50-59 years of age on left ear of male workers and in -19, 20-29 years of age on left ear of female for 1,000 Hz. 2.Hearing thresholds of group audiocups were significantly decreased than that of non-audiocups in 20-29, 40-49 and 50-59 years of age on right ear of male and in -19, 20-29 and 40-49 years of age on right ear of female for 1,000 Hz. 3.Hearing thresholds of group audiocups were significantly decreased than that of non-audiocups in 20-29, 30-39 and 40-49 years of age on left ear of male worriers and in 20-29 years of age on left ear of female for 4,000 Hz. 4.Hearing thresholds of group audiocups were significantly decreased than that of non-audiocups in 20-29, 30-39 and 50-59 years of age on right ear of male and in 20-29 and 40-49 years of age on right ear of female for 4,000 Hz.

十二變에 대한 考察 : 六元正紀大論을 중심으로

채영진,남호현,이석모,여성원,한성규,이재원,안민식,정헌영,금경수 한국전통의학연구소 2003 한국전통의학지 Vol.13 No.1

The six kinds of natural factors(It refers to wind, cold, summer-heat, dampness, dryness and fire.) is constantly moving to maintain the balance of whole climate of one year. Four seasons are the largest mediation of whole climate of one year. The cold and the heat have the relationship of mutual intervention. The dampness and the dryness have it also. In this process they raise various climate appearance. And that various climate appearance influence the whole lives on the earth. This paper is concerned with the classification of them.

Mg₂SiO₄: Tb, Nd, Dy 열형광선량계에서 활성제 농도가 Glow Curve에 미치는 영향

노경석,채근식,오재근,김영국,이은숙,설정식,손인호 慶南大學校 附設 基礎科學硏究所 1996 硏究論文集 Vol.8 No.-

The Mg₂SiO₄: Tb, Nd, Dy thermoluminescent phospher has been prepared by sintering Mg₂SiO₄after doping the transition elements Tb, Nd and Dy. The heating rate is 10℃/sec at this thermoluminescent phospher are heated. From the results of this study, the following conclusions were obtained. The maximum peaks are found in the measured Mg₂SiO₄: Tb, Nd, Dy, and TL glow curve at 289℃, 252℃ and 220℃ when the 1wt.% ∼ 5wt.%. Glow curve of TLD increased TL intensity and temperature of peak appears to the high temperature when the heating rate is 10℃/sec∼25℃/sec. The activation energy of the main peak has been estimated by the peak shape method. The estimated activation energies are 1.26 eV, 0.53 eV and 0.80 eV respectively. The thermoluminiscence process in Mg₂SiO₄: Tb, Nd, Dy are found to the 2nd order when the main peak of the glow curve is analyzed by peak shape method. The Mg₂SiO₄: Tb thermoluminescent phosphor is the most sensitive to X-rays among the other materials. The dose responses of Mg₂SiO₄: Tb, Dy TLD are linear up to intensity of X-ray.

식물추출물의 Tyrosinase 활성 억제효과

이정숙,채은경,계경채,문석식,조순장,김창덕,박장규,이증훈 大韓皮膚硏究學會 2003 大韓皮膚硏究學會誌 Vol.10 No.4

CaSO₄ 열형광체의 제작과 열형광 특성에 관한 연구

김영국,손인호,채건식,노경석 경남대학교 환경문제연구소 1993 환경연구 Vol.15 No.-

CaSO₄ thermoluminescent phosphor has been prepared by sintering the CaSO₄ after doping the transition elements. The maximum peaks are found in the measured CaSO₄, TL glow curve at 130℃, 110℃ when the heating rate is 5℃. The activation energy of the main peak has been estimated by the peak shape method. The estimated activation energies are 1.02 eV, 1.32 eV respectively. The thermoluminescence process in CaSO₄, are found to the 2nd order when the main peak of the glow curve is analyzed by peak shape method.

축구선수의 Detraining과 Retraining이 혈청지질 및 호르몬농도에 미치는 영향

정정화,박재현,채종훈,성혜련,황지인,윤미숙,노금선,윤종관,윤영학,노순덕,정경숙,박일규,김은희,박현태,박상갑 대한스포츠의학회 1999 대한스포츠의학회지 Vol.17 No.1

The purpose of this study was to investigate the effects of detraining and retraining on serum lipid and hormones in soccer players. Subjects were seven male high-school soccer players. V˙O_2max was determined for each subjects by administering a treadmill test(initial speed: 90m/min, grade: 5%, increasing speed per 3 min: 30m/min). Serum lipid(T-C, TG, HDL-C LDL-C) and hormones(epinephrine, norepinephrine, growth hormones, cortisol) were assayed pre and post detraining in 10, 20, 30 days after retraining. The repeated ANOVA was used to determine significant differences. The 0.05 level of significance was as critical level for the study. The results of the study were as follows: 1. V˙O_2max(ml/min) were 3576.3±204.2ml/min pre detraining, 3234.1±198.9 ml/min post detraining. There are significant(p<.05) difference between pre and post detraining. In 10, 20, 30 days after retraining, V˙O_2max(ml/min) were 3601.4±170.9 ml/min. There were significantly(p<.05) increased in retraining periods. 2. V˙O_2max(ml/kg/min) were significantly(p<.05) decreased from 62.3±2.9 ml/kg/min to 55.9±4.7 ml/kg/min in detraining. In 10, 20, 30 days after retraining, V˙O_2max(ml/kg/min) were 62.4±3.4ml/kg/min, 62.7±2.3ml.kg/min, 67.3±7.2ml/kg/min respectively. There were significantly(p<.05) increased in retraining periods. 3. T-C were significantly (p<.05) increased from 166.6±8.5mg/dl to 175.3±10.3 mg/dl in detraining. In 10, 20, 30 days after retraining, T-C were 160.1± 3.2mg/dl, 156.7±3.7mg/dl, 140.3±9.0mg/dl. There were significantly(p<.05) decreased in retraining periods. 4. HDL-C were 61.4±6.6mg/di pre detraining, 5.3±6.6mg/dl post detraining. There are significant(p<.05) difference between pre and post detraining. In 10, 20, 30 days after retraining, HDL-C were 56.9±7.1mg/dl, 56.4±9.2mg/dl, 57.7±9.1mg/dl respectively. There were no significant difference in retraining periods. 5. The hormones(epinephrine. norepinephrine, growth hormone, cortisol) were changed as same patterns. Epinephrine were 26.0±7.0[g/ml pre detraining, 24.6±3.2pg/ml post detraining. In 10, 20, 30 days after retraining, epinephrine were 26.9±5.6pg/ml, 30.6±6.2pg/ml, 29.4±5.6pg/ml respectively. There were no significant difference in retraining periods. In conclusion, HDL-C, epinephrine, norepinephrine, growth hormone and cortisol were decreased, T-C, LDL-C and TG were increased in detraining. But HDL-C, epinephrine, norepinephrine, growth hormone and cortisol were increased, T-C, LDL-C and TG were decreased in retraining.

Mg₂SiO₄ : La, Ho 열형광선량계에서 활성제 농도가 글로우 커브에 미치는 영향 La, Ho TLD on Activation Concentration

김영국,손인호,채건식,노경석,오재근,이은숙 경남대학교 신소재연구소 1996 論文集 Vol.6 No.-

본 연구에서는 Mg₂SiO₄에 활성화 물질로 La, Ho를 첨가하여 열형광체를 제작하였고 불순물의 농도를 1wt.% ∼5 wt.%까지 변화시키면서 열평광강도의 glow curve를 측정하였다. 도한 열형광체의 glow curve를 peak shape법으로 분석해서 TL특성에 대한 포획 매개변수와 활성화 에너지, 발광차수, 선량의존성등을 조사하였으며, 그 물리적 특성을 조사하고 선량계로서 타당성과 실용성을 확인하였다. The Mg₂SiO₄: La, Ho thermoluminescent phospher has been prepared by sintring Mg₂SiO₄after doping the transition elements La and Ho. The heating rate is 10℃/sec at this thermoluminescent phospher are heated. The maximum peaks are found in the measured Mg₂SiO₄: La and Ho. TL glow curve at 229℃ and 345 C when the 1 wt.%-5 wt.%. The glow curve of TLD increased TL intensity and temperature of peak appears to the high temperature when the heating rate is l0℃/sec-25℃/sec. The activation energy of the main peak has been estimated by the peak shape method. The estimated activation energies are 1.77 eV. 1.52 eV respectively. The thermoluminescence process in Mg₂SiO₄: La and Ho are found to the 2nd order when the main peak of the glow curve is analyzed by peak shape method. The dose responses of Mg₂SiO₄: La and Ho TLD are linear up to intensity of X-ray.

MgB₄O7 熱螢光體의 특성과 低에너지 X線의 線量測定

김영국,손인호,설정식,채건식,노경석 慶南大學校 附設 基礎科學硏究所 1997 硏究論文集 Vol.11 No.-

To develope the thermoluminescent radiation sensors and low energy X-ray of dosimetry. The TL phosphors of MgB₄O7 are prepared and their physical characteristics are investigated. MgB₄O7 : Tb. Tm. Dy. La. Ho. and Nd phosphors have been prepared by sintering around 580℃ for 2 hours followed by flowing Ar gas. Ar gas. Activation energy and kinetic order of main peak of glow curve were studied by two methods peak shape method and initial rise method. By these methods, the estimated activation energies were 0.76±0.02eV(Tb doped). 0.94±0.03(Tm doped). 0.72±0.02 (Dy doped). respectively. The activation energy frequency factor and kinetic order of thermoluminescent process for each TL phosphors are measured by analyzing the glow curve by initial rise. peak shape. different heating rate. isothermal decay method. And The emission spectra of TL phosphors are also measured. The TL phosphors prepared in this work may be utilized to radiation sensor elements becaue of their high sensitivity to low energy X-ray.

CaSO₄: Dy 열형광선량계에서 활성제 Dy가 Glow 피크에 미치는 영향

손인호,김영국,노경석,채건식,이은숙 慶南大學校 附設 基礎科學硏究所 1995 硏究論文集 Vol.7 No.-

CaSO ₄ thermoluminescent phosphor has been prepared by sintering the CaSO ₄ after doping the transition element Dy. The maximum peaks are found in the measured CaSO ₄ TL glow curve at 210℃, 240℃ when the 0.01-0.1 mol % and 0.2-0.5 mol %. The activation energy of the main peak has been estimated by the peak shape method. The estimated activation energies are 1.26 eV respectively. The dose responses of CaSO₄TLD are linear up to 1-800 rad of X-rays.