This study investigated the effects of self-efficacy and marital conflict as a mediator, and self-efficacy as a moderator of the relationship between parenting stress and depression among married women with infants. In addition, this study aimed to test the moderated mediation effect of self-efficacy by integrating the process of mediation and moderation. Based on related theoretical models and empirical research, two models, including parallel mediating effects and sequential medicating effects of self-efficacy and marital conflict as well as moderating effect of self-efficacy, were proposed and tested. For this study, a survey was conducted to a sample of 600 mothers of infants in daycare centers and kindergartens using measures of parenting stress, self-efficacy, marital conflict, and depression. According to the data analysis, the sequential mediation of self-efficacy and marital conflict and moderation moderated mediation of self-efficacy were found. Based on the findings, the implications and limitations of the current study were discussed. 본 연구는 영유아기 자녀를 둔 기혼여성의 양육스트레스와 우울 간의 관계에서 자기효능감과 부부갈등의 매개효과와 자기효능감의 조절효과를 알아보고, 매개효과와 조절효과 과정을 통합한 자기효능감의 조절된 매개효과를 알아보고자 하였다. 관련된 이론적 모델과 선행연구를 바탕으로 자기효능감의 조절효과와 함께 자기효능감과 부부갈등의 병렬적 매개효과와 순차적 매개효과를 각각 가정한 연구모형을 설정하고 검증하고자 하였다. 이를 위해 어린이집과 유치원에 재원중인 영유아를 양육하는 어머니 600명을 대상으로 양육스트레스 척도, 자기효능감 척도, 부부갈등 척도, 우울 척도를 사용하여 설문을 실시하였다. 검증결과, 양육스트레스와 우울 간의 관계에서 자기효능감과 부부갈등의 순차적 매개효과와, 자기효능감의 조절효과 및 조절된 매개효과를 확인하였다. 이러한 결과를 바탕으로 본 연구의 시사점 및 제한점을 논의하였다.
알콕사이드로부터 Sialon-SiC계 복합분말의 합성과 분말특성(I)
전명철,이홍림 한국세라믹학회 1990 한국세라믹학회지 Vol.27 No.2
Fine Si-Al-OH-C coprecipitate powders were prepared from Si(OC2H5)4, Al(i-OC3H7)3, and carbon black by a hydrolysis method before fabrication of Sialon-SiC composite powder by carbothermal reduction at 1350$^{\circ}C$ for 10h under N2/H2 mixed atmosphere. The characterization of the synthesized Sialon-SiC composite powders was performed using XRD, BET, SEM, TEM and particle size analysis methods. The average particle size and specific surface area of the synthesized Sialon-SiC composite powder were 0.13$\mu\textrm{m}$ and 20.1㎡/g, respectively when Z=1 and N2 : H2=50 : 50.
중국 초고층 건축물의 형태구성 특성과 영향요인에 관한 연구
전명철,김민경,이정수 대한건축학회지회연합회 2010 대한건축학회연합논문집 Vol.12 No.3
본 연구에서는 중국의 현재 건립되었거나, 최근 시공 및 제안중인 초고층 건축물에 관한 외부디자인 결정요소인 형태구성 특성을 반영하는 사례들을 분석함으로서, 형태구성에 따른 영향요인을 구체적으로 밝히는 것을 그 목적으로 한다. 이러한 분석결과를 바탕으로 나타난 중국 초고층 건축물의 형태구성 특성 및 영향요인은 다음과 같이 정리할 수 있다. 첫째, 매스의 측면에서는 평면에 의해 그 기본적 특성이 나타난다. 시각적 구조를 구체화하는데 있어 평면은 매스의 형태와 규모를 영역으로 한정하므로 시각적 측면에서 평면은 건축형태에 가장 중요한 요소라 할 수 있다. 둘째, 입면의 측면에서는 주로 평면형 유형이 외부 패턴을 결정하는 초기의 요소로 사용되었지만 재료의 다양화와 경량화 등에 의해 수평형, 수직형, 격자형 등의 패턴이 면의 분할을 통해 다양성이 추구되며, 유리의 사용에 의한 주위환경의 투영은 건축물이외의 새로운 입면을 형성하게 된다. 셋째, 마감이나 장식요소의 시기별 표현 양상을 살펴보면 주로 유리의 사용에 의해 재료자체의 색보다는 주변 환경에 의해 건물의 이미지가 형성된다. 넷째, 본 연구의 주요 분석대상인 형태구성은 기술적 요인뿐만 아니라 또 다른 측면의 사회?문화적이고 법규적 요인에 의하여 영향 받고 있음을 알 수 있다. 결과적으로 중국 초고층 건축물의 형태구성 특성은 시기에 따라 다양한 양상을 띠고 전개되어 왔으며 이러한 변화에 여러 가지의 구성요소들이 변화의 요인으로 영향을 미치고 있는 것으로 나타난다.
알콕사이드로부터 Sialon-SiC계 미분말의 합성과 분말특성
이홍림,전명철,이형복 연세대학교 산업기술연구소 1988 논문집 Vol.20 No.2
Fine Si-Al-OH coprecipitate powder was prepared from Si- and Al-alkoxides by a hydrolysis method. Sialon-SiC composite powder was then fabricated from the Si-Al-OH coprecipitates by carbothermal reduction, nitridation and carbiding reaction method in nitrogen-hydrogen atmospheres. The average size of alpha silicon nitride was about 1㎛ and that of beta sialon was about 0.2-0.3㎛. However, the average size of Sialon-SiC composite powder was about 0.13㎛. Sialon/SiC(45/55) composite powder was hot-pressed at 1750℃ for 60 min in a nitrogen atmosphere. Bending strength, fracture toughness and microhardness were 494.6 MPa, 3.8 MN/m?? and 13.9 GPa. respectively.
알콕사이드로부터 Si-Al-O-N계 분말합성 II. 알콕사이드로부터 합성한 Si3N4 및 $\beta$-Sialon의 분말 및 소결체의 특성
이홍림,전명철 한국세라믹학회 1989 한국세라믹학회지 Vol.26 No.2
Fine Si-Al-OH coprecipitate powders were prepared from Si- and Al-alkoxides by the hydrolysis method. $\beta$-Sialon powder was obtained from prepared Si-Al-OH coprecipitate by the simultaneous reduction and nitridation method. The syntehsized Sialon powder was pressureless sintered at 175$0^{\circ}C$ for 90 min in N2 atmosphere. The characterization of the Sialon powder was performed with XRD, BET, SEM, TEM and particle size analysis. The sinterability and mechanical properties of sintered bodies were investigated in terms of relative density, M.O.R., fracture toughness, hardness and the morphology of microstructure. The highest values of their mechanical properties were obtained for the $\beta$-Sialon ceramics at Z=1 and those values are as follows : M.O.R., KIC and HV of $\beta$-Sialon ceramics(Z=1) are 499.1 MPa, 5.9MN/m3/2 and 18.7GPa, respectively.
김용상,이성규,전명철,박진석,한민구 한국전기전자재료학회 1994 電氣電子材料學會誌 Vol.7 No.2
The purpose of this work is to investigate the interface characteristics of hydrogenated amorphous silicon thin films prepared by PECVD and photo-induced CVD and to examine the annealing effects of ultraviolet irradiation on hydrogenated amorphous silicon thin films which were degraded by visible light illumination. The interface layer thickness of films deposited by photo-induced CVD was about 600-900.angs. while that by PECVD was about 1000-1300.angs.. These results can show that the quality of interface layer in photo induced CVD film is better than that in PECVD sample. The electrical properties are improved by ultraviolet irradiation on visible light soaked a-Si:H films using photo-CVD light sources, probably due to the fact that UV generates phonons in a-Si:H films and anneal the meta stable defects.