http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
다공성 임플란트 제조를 위한 3D 프린팅 응용 금형기술
이성희,김미애,윤언경,이원식,Lee, Sung-Hee,Kim, Mi-Ae,Yun, Eon-Gyeong,Lee, Won-Sik 한국금형공학회 2017 한국금형공학회지 Vol.11 No.1
In this study, the mold technology for manufacturing of porous implant was investigated. Firstly, we considered the concept of insert molding technology with 3D printing of porous inert part. The part on implant was designed in the end region of the implant. And then main implant bodies were manufactured using conventional machining method. The other porous parts were designed and optimized with molding simulation. As the feature size of porous implant was so small that perfect feature of it using 3D printing technology could not be obtained. So, we proposed another scheme for manufacturing of the porous implant in the replace of the former approach. Polymer mold cores with 3D printing technology were considered. The effects of addictive manufacturing process parameters on the properties of mechanical and dimensional accuracy were investigated. Direct 3D printed polymer mold cores were designed and manufactured under the simulation of thermal and molding analysis. It was shown that 3D printed mold core with polymer could be adapted to the injection molding for porous implant.
SLS 3D 프린터를 이용하여 제작된 PA2200의 단축 반복 인장하중에 따른 피로 특성에 관한 연구
박준수,정의철,최한솔,김미애,윤언경,김용대,원시태,이성희,Park, Jun-Soo,Jeong, Eui-Chul,Choi, Han-Sol,Kim, Mi-Ae,Yun, Eon-Gyeong,Kim, Yong-Dae,Won, Si-Tae,Lee, Sung-Hee 한국금형공학회 2020 한국금형공학회지 Vol.14 No.1
In this study, the fatigue behavior and fatigue life characteristics of PA2200 specimens fabricated by SLS 3D printer were studied. Fatigue tests were performed according to the standard specification (ASTM E468) and fatigue life curves were obtained. In order to perform the fatigue test, mechanical properties were measured according to the test speed of the simple tensile test, and the self-heating temperature of the specimen according to the test speed was measured using an infrared temperature measuring camera in consideration of heat generation due to plastic deformation. There was no significant difference within the set test speed range and the average self-heating temperature was measured at 38.5 ℃. The mechanical strength at the measured temperature showed a relatively small difference from the mechanical strength at room temperature. Fatigue test conditions were established through the preceding experiments, and the loading conditions below the tensile strength at room temperature 23 ℃ were set as the cyclic load. The maximum number of replicates was less than 100,000 cycles, and the fracture behavior of the specimens with the repeated loads showed the characteristics of Racheting. It was confirmed that SLS 3D printing PA2200 material could be applied to the Basquin's S-N diagram for the fatigue life curve of metal materials. SEM images of the fracture surface was obtained to analyze the relationship between the characteristics of the fracture surface and the number of repetitions until failure. Brittle fracture, crazing fracture, grain melting, and porous fracture surface were observed. It was shown that the larger the area of crazing damage, the longer the number of repetitions until fracture.
고현준(Hyun-Jun Ko),이상철(Sang-Chul Lee),김옥래(Ok-Rae Kim),김성규(Sung-Gyu Kim),윤언경(Eon-Gyeong Yun) 한국생산제조학회 2011 한국생산제조시스템학회 학술발표대회 논문집 Vol.2011 No.4
Machine tool industry to influence the competitiveness of the manufacturing core of capital goods, industrial precision equipment industry, as Germany and Japan as well as developed countries to recognize the key industries of the country through cutting edge technology and striving for national competitiveness is the main area. In order to process the inside of those artifacts, such as a laser or grinding tool with a processing device to processing inside to the workpiece. In this paper, solving the problem of processing devices and users inside the processing device can be machined into the desired shape is intended to design.