부유대역 용융응고법으로 제조된 YBa_2Cu_3O_x 산화물초전도체의 미세구조와 전기적 특성

노태형,송정환,장규철,한이섭,김소정,구본급,김호기 대전산업대학교 반도체기술연구소 2000 半導體技術硏究所報 Vol.2 No.-

The YBa_2Cu_3O_x-20 wt% Y_2BaCuO_5 composition designed in YBCO system was synthesized by solid state reaction method. The optimum condition of hot zone temperature and growth rate in floating-zone melt were 1080 ℃ and 2.5 mm/hour, respectively. In samples growth as these condition, the low angel boundaries in grain direction and small amount of amorphous phase known as decreasing characteristics of superconducting materials between grain boundaries in microstructure are investigated by polarized light microscopy on the whole. The critical current density(Jc) at 77k of sample using powder fabricated with no CeO_2 and doped 5 wt%CeO_2 were 8,000 A/㎠(Jc : 561A) and 12,000 A/㎠(Jc: 826A) at 0 T by direct current transport method, respectively.

V₂O-B₂O₃-PbO 유리의 전자 상자성 공명연구

노태호,전인,박영민,강재필,김성재,박현진,송승기 명지대학교 자연과학연구소 1996 자연과학논문집 Vol.14 No.-

V₂O??-B₂O₃-PbO 유리의 VO??에 관한 전자 상자성 (EPR) 스펙트럼으 연구하였으며, vanadium이온의 스핀해밀토니안 상수들을 구하였다. 유리시료안의 V₂O??양을 증가시킴에 따라 g??과 g??값은 증가하였으나 A??과 A??값은 감소하였다. 이는 V₂O??수가 증가하면 동일 평면상의 vanadium과 oxygen배위간 결합의 공유성이 증가함을 의미한다. 유리내의 vanadium 4가이온은 정방형 일그러진 8면체를 한 vanadyl착물로 존재한다. Electron Paranmagnetic Resonance(EPR) SPECTRA OF (VO)?? in V₂O??-B₂O₃-PbO glasses have been studied and spin hamiltonian paramenters of vanadium ion have been calculated. It is found that the value of g??and g?? increases while the value of A?? and A?? decreases with an increase of V₂O?? content in the glass samples, showing that the covalency in the in-plane vanadium -oxygen ligand bonds increase with increasing the concentration of V₂O??. The tetravalent vanadium ions exist as vanadyl complexes with tetragonally distorted octahedral sites in the glasses.

7차 초등학교 과학 교과서의 삽화에 나타난 성역할 고정관념 분석

노태희,차정호,왕혜남 한국초등과학교육학회 2004 초등과학교육 Vol.23 No.1

이 연구는 제7차 교육과정기의 과학 교과서와 실험관찰 교과서에 제시된 삽화를 성역할 고정관념 측면에서 분석하고 6차 교육과정기의 과학 교과서와 비교하였다. 교재에 나타난 삽화에서 성별에 따른 등장인물의 빈도를 세고, 활동 유형을 분석하였다. 연구 결과는 다음과 같다. 1) 과학 교과서의 전체 삽화 수는 6차에 비해 7차에서 2배 정도 증가하였다. 2) 아동의 경우 학습활동에서는 성에 관계없이 등장 빈도가 대체적으로 균형을 이루었지만, 학습의 활동에서는 남학생의 등장 빈도가 여학생보다 더 높았다. 3) 행동 특성에서는 남녀 학생 모두 적극적으로 묘사되었고, 소극적으로 묘사되는 여학생의 비율은 6차 과학 교과서에 비해 감소하였다. 4) 성인의 경우에는 남성의 등장 빈도가 여성보다 높게 나타났다. 5) 가사 활동을 하는 모습에서는 여성의 등장 빈도가 40%로 높게 나타난 반면, 남성은 드물게 나타났다. The illustrations in elementary science textbooks and experimental workbooks based on the 7th national curriculum were analyzed for gender-role stereotyping, and compared with those of the 6th curriculum. The frequencies of men and women who appeared on text illustrations were counted and the types of roles assigned to males and females were investigated. The results were as follows. 1) The 7th national curriculum textbooks contained double the number of illustrations in the textbooks based on the 6th curriculum. 2) Boys and girls were illustrated in 'learning activities' with equal frequency, but boys were more frequently represented than girls in illustrations of 'other' activities. 3) Both boys and girls were generally depicted in 'active' processes and the ratio of 'passive girl' illustrations decreased as compared with the 6th national curriculum. 4) Male adults were more frequently represented than female adults in both textbooks and experimental workbooks. 5) 40% of female adults were illustrated doing housework, while male adults were rarely illustrated in such a role.

사회적 구성주의 학습이론에 기초한 예비 교사의 온라인 토론 분석

차정호,노태희 한국컴퓨터교육학회 2005 컴퓨터교육학회 논문지 Vol.8 No.1

림프절에 발생한 모반세포 봉입체 - 2예 보고 -

송지선,노태웅,김윤미,조상호,이광길 대한병리학회 2001 Journal of Pathology and Translational Medicine Vol.35 No.3

용매의 선택에 따른 전도성 Polyaniline의 자기적 성질변화

오응주,서정선,노태호,류광선,정상국,송승기 명지대학교 자연과학연구소 1994 자연과학논문집 Vol.11 No.-

Polyaniline(emeraldine base:EB)를 pH에 따라 HCI로 1차 doping을 한후ESR을 사용하여 자기적 성질을 조사했다.또한 emeraldine base를 camphorsulfonic acid(HCSA), dodecylbenzene sulfonic acid(HDBSA)등의 산으로 1차 doping 시키고 이것을 m-cresol, acetic acid, 및 formic acid에 녹여 2차 doping을 한 후 SQUID 를 이용하여 자기적 성질을 측정하였다. Doping에 사용된 HCI용액의pH가 감소함에 따라 ESR 신호의 강도가 증가하였으며, 이로부터 doping에 따라 상자성을 나타나게 하는 화학종이 가타다는 것을아타내고 있다.m-cresol내에서 HCSA 및 HDBSA로 각각 doping된 EB-CSA/m-cresol 과 EB-DBSA/m-cresol 시료 무두 상자성을 나타내었고, 온도가 증가함에 따라 자하율값이 감소하는 경향을 나타내었다.χ?값은 2.18x10?과 7.87x10?emu/mol2-rings unit 보이며 두 스핀에 대한 Fermi 에너지 level(E?)에서의 상태밀도를 나타내는 N(E?)는 0.67과 0.24 상태(eV/2-rings unit?)로 나타났다.Camphorsulfonic ascid(HCSA)로 doping 된 EB를 m-cresol, acetic acid 및 chloroform 등 다른 용매에서 처리시 관찰된 자화율의 변화를 온도에 의존하지 않는 χ?값과 온도에 의존하는 χ? 값으로 구분하여 curie spin의 온도의존성을 규명하였다. Dependency of magnetic properties of polyaniline(emeraldine base:EB)on the pH of HCI used in doping was inverstigated by electron spin resonance spectroscopy. Emeraldine base doped with functionalized acid (primary dopant) such as camphorsulfonic acid (HCSA), dodecylbenzene sulfonic acid(HDBSA) was processed in various solvents (m-cresol, acetic acid, formic acid etc.)into homogeneous solution and free standing film and its magnetic properties were measured by SQUID. The intensity of ESR signal was increased with decrese in pH of HCL solution and paramagnetic behavior of doped polyaniline due to the formation of polaron upon doping could be confoirmed from these results. The same g value of 2.004±0.001 measured for all of the samples means that the chemical species which show paramagnetism are sasme. Polyanilines doped with HCSA and HDBSA in m-cresol showed paramagnetism and decrease in susceptibility with increase in temperature. χ? value was appered 2.18x10? and 7.87x10? emu/mol2-rings unit and N(E?) which is density of states at Fermi energy level for two spins was 0.67 and 0.24 state eV? 2rings unit? respectively. The changes in susceptibility of polyanilines doped with HCSA in m-cresol, acetic acid, formic acid etc. were divided into temperature independent χ? term and temperature dependent χ? term and temperature dependency of curie spin concentration was examined.

Glycol Oleates의 합성과 절삭유제로서의 물성

최형기,이호식,이치우,강신춘,노시태 한양대학교 공학기술연구소 1993 공학기술논문집 Vol.2 No.1

Glycololeates for the application of cutting fluid were synthesized from oleic acid and glycols such as ethylene glycol, diethylene glycol and triethylene glycol. The ratio of glycol-monooleate and dioleate in product according to the reaction condition was analyzed by TLC, CC and HPLC. Properties of glycololeates as cutting fluid were examined by various testing methods such as profile test, pH test, anti-foaming test friction coefficient test and emulsion stability test to compare those of base oil and cutting fluid trading in the market. Non-catalytic reaction of glycololeates synthesis was showed too low conversion rate, but too fast conversion rate and deep color deterioration of products was obtained with acid-catalyses reaction. Using the SnCl2 catalyst, conversion rate was medium range and products which suitable for the application of cutting fluid with mild colored and with desirable mono- and di-oleate composition was obtained. Cutting fluidal properties of glycololeates with SnCl2 catalyst were better than those of base oil, and were similar level to those of cutting fluid containing various additives.

고온 초전도체 Y Pr Zn Ba₂Cu₃O의 자기적 성질

김성재,박영민,노태호,전인,강재필,송승기 명지대학교 자연과학연구소 1995 자연과학논문집 Vol.12 No.-

전이 온도가 72K인 Y?Pr?-Zn?Ba?Cu?O?고온 초전도체에 초전도성을 약화시키는 Pr 원소와 Zn를 적절한 비율로 치환하여 자기적 특성을 연구하였다. Zn가 첨가되었을 때의 임계온도(전이온도)는 35~ 44K의 값을 나타내었다. 온도에 대한 비저항의 측정으로 구한 전기적 임계온도와 온도 대 자기 모우먼트 측정으로 구한 자기적 임계온도 값은 거의 비슷했다. 자기이력 곡선으로부터 H?(저임계자기장), H?(고임계자기장)와 반자성 정도를 구했으며, Bean의 모델을 이용하여 임계전류밀도를 구하였다.이러한 자기적 성질들은 시료에 Zn가 첨가되자 급격히 감소되었다. 임계전류밀도의 경우 x=0.0인 시료가 1.6x 10?A/㎠으로 계산되었고, Zn가 첨가된 다른 시료의 임게전류밀도는 3.5x10?~1.3x10?A/㎠범위의 값을 나타내었다. 이것은 시료내에서 Znr가 초전도성을 급격하게 감소시킴을 의미한다. We have studied magnetic property as a substitute appropriate propertation of Zn element for Pr element which reduces superconducting property in high-temperature superconductor Y?Pr??Zn?Ba?Cu?O?? of transition temperature 72K, When Zn is put into it, critical temperature showed the value of measurement at th range of 35 ~44K. The electric critical temperature determinded by the temperature dependence of resistivity had a similar data to the magnetic citical temperature determinded by the temperature dependence of at the range of 35 ~ 44K. The electric critical temperature determined by the temperature dependence of resistivity had a similar data to the magnetic critical temperature determined by the temperature vs. magnetic moment. H?(critical low mgnetic field ), H?(critical high magnetic field), diamagnetic ratio and critical current density calulated by Bean's model from the magnetic hysterisis curve. These properties were abruptly decreased with adding Zn in the samples, Especially , the critical current desity of x=0.0 sample was calculated at 1/6x 10?A/㎠.These mean that Zn in the sample decreases superconduting properties in the sample.

소아청소년기에 치수치료를 받은 제1대구치의 술전 상태 조사

이순영,이경호,노홍석,정태성,김신 大韓小兒齒科學會 2011 大韓小兒齒科學會誌 Vol.38 No.4

제1대구치는 막중한 역할을 함에도 불구하고, 청소년 이전에 건강을 상실하는 경우가 드물지 않다. 본 연구는 청소년기 이 전에 치수치료를 받게 된 제1대구치의 우식 및 수복 상태와 분포를 파악할 목적으로 시도되었다. 최근 5년간 부산대학교 치 과병원에서 치수치료를 받은 18세 이하 106명 환자의 135개 제1대구치를 대상으로 의무기록에 대한 조사를 시행하여 다음 과 같은 결과를 얻었다. 1. 평균 연령은 11.9세(남 11.5세, 여 12.5세)였고 유의한 성차를 보였으며(p<0.05), 악별로는 상악 47개, 하악 88개로 하악 치아가 더 많았다. 2. 치수 치료 전 치료 기왕력이 없는 치아는 74개, 치수 또는 수복 치료를 받은 치아는 61개였다. 그 중 재치수치료를 받게 된 경우는 22개로 치수절제술-치수절단술의 순이었으며, 단순 수복치료를 받았던 치아는 39개로 복합레진-아말감-GI- 인레이-수복물 탈락 후 미치료-열구전색 및 주조 전장관의 순이었다. 3. 병소 위치가 분류 가능한 73개의 병소 중에서는 근심면 병소가 22개, 교합면 혹은 협설면 병소 39개, 원심면 병소가 12 개를 차지하였다. In clinical dentistry, it is not difficult to meet the permanent first molars with severe coronal caries lesions in children or adolescents. The circumstances surrounding the first molars of children and adolescents are so immature and imperfect compared with those of adults. So we thought it significant to understand the status of these teeth at the moment of endodontic treatment and immediate cause of it. 106 patients with 135 permanent molars necessitating endodontic treatment in childhood and adolescence were included in this study, and the dental records and radiographs were examined. 1. The mean age was 11.9 year (male 11.5, female 12.5) and the result shows significant difference between gender(p<0.05). The mandibular teeth took more than half percentage than maxillary teeth. 2. Of 135 teeth, 45.2 percent of teeth had history of dental treatment previously and 16.3 percent of teeth showed necessity of re-endodontic treatment. 3. Of 73 teeth, 22 teeth had mesial-wall cavity causing endodontic treatment, 39 had occlusal cavity, and 12 had distal cavity.

고온 초전도체 Y₁Ba₂Cu₃O_7-δ(CdO)_x의 핵사중극 상호작용 연구

전인,김복수,노태호,김영훈,서용문,송승기,박영민 명지대학교 자연과학연구소 2000 자연과학논문집 Vol.19 No.-

CdO가 첨가된 고온 초전도체 Y1Ba2CU3O7-δ(CdO)x(x=0.00,0.09,0.22,0.34,0.42,0.49)를 고상 반응법으로 제작하여 상온에서 Cu 핵사중극 공명 실험을 하였다. 구리-산소 평면에 있는 63Cu(2)의 핵사중극 공명 진동수는 31.13∼31.39 MHz이고, 65Cu(2)의 공명 진동수는 28.82∼29.06 MHz이었다. 이러한 공명 진동수는 χ가 증가할수록 높은 진동수 방향으로 이동하였다. 63Cu(2)과 65Cu(2)의 NQR 공명 진동수의 비는 모든 시료가 1.08로 63Cu과 65Cu의 핵 사중극 모멘트의 비와 같았다. 구리-산소 사슬에 있는 63Cu(1)의 공명 진동수는 22.15~22.36 MHz에서 관측되었는데, χ에 따른 공명 진동수의 이동 경향은 63Cu(2)과 65Cu(2)의 경우와 비슷하였다. 선폭은 63Cu(2)과 65Cu(2)그리고 63Cu(1)의 경우 모두 약 200∼300 kHz고, 전반적으로 χ가 증가할 수록 감소하였다. 스핀-에코 방법으로 구한 스핀-스핀 이완 시간 T2는 χ가 증가함에 따라 약간씩 증가하였다. We have studied Cu-NQR in CdO-mixed high-Tc superconductor Y1Ba2Cu3O7-δ(CdO)x(x=0.00, 0.09, 0.22, 0.34, 0.42, 0.49) at room temperature prepared by solid state reaction method. In the Cu-O plane, 63Cu(2)-NQR frequencies were measured to be in the range of 31.13-31.39 MHz and those of 65Cu(2) were in the range of 28.82-29.06 MHz. The position of spectrum-peaks shifted to the higher frequency with increasing χ. The ratio of 63Cu(2) and 65Cu(2)-NQR frequencies have the value of 1.08 which is equal to the ratio of 63Cu(2) and 65Cu(2) nuclear quadrupole moment for all samples. The resonance frequencies of 63Cu(1) in the Cu-O chain have been observed in the range of 22.15-22.36 MHz and the tendency of resonance frequency behaviour with χ were nearly the same for both 63Cu(2) and 65Cu(2). The line-widths of 63Cu(2), 65Cu(2) and 63Cu(1) were observed to the value of 200∼300 kHz and they decreased with increasing χ. The spin-spin relaxation time T2 obtained by spin-echo method increased slightly with increasing χ.