녹색 발광의 $CaZrO_3:\;HO_{3+}$ 축광성 형광체의 합성 및 발광 특성

박병석,최종건,Park, Byeong-Seok,Choi, Jong-Keon 한국결정성장학회 2008 韓國結晶成長學會誌 Vol.18 No.3

새로운 녹색의 $CaZrO_3$ : $HO_{3+}$ 축광성 형광체를 고온의 약한 환원 분위기에서 전통적인 고상 반응법으로 합성하였다. $CaZrO_3$ : $HO_{3+}$ 축광성 형광체에 첨가 된 융제 $H_3BO_3$의 역할과 부활제의 적정농도에 대하여 연구하였으며, 합성한 축광성 형광체의 형광 분석 및 광 발광 분석을 행하였다. 고온의 질소 분위기에서 합성한 $CaZrO_3$ : $HO_{3+}$ 축광성 형광체는 546nm의 발광 피크가 나타남을 확인 하였으며, 장잔광 스펙트럼 또한 폭이 좁은 546 nm의 발광 피크가 나타남에 따라 순수한 녹색의 발광색을 띄고 있음을 확인하였다 녹색의 $CaZrO_3$ : $HO_{3+}$ 축광성 형광체의 발광 지속시간은 254 nm UV lamp로 여기 시킨 후 어두운 곳에서 5시간 이상 발광이 유지되었다. 발광 피크는 $HO_{3+}$ 이온의 $^5F_4$, $^5S_2{\to}^5I_3$ 전이에 의한 것이며, 잔광 특성은 $CaZrO_3$ 격자 내에 trap center가 생성됨 의하여 발생되는 것으로 판단된다. Novel green long persistent phosphors of $CaZrO_3$ : $HO_{3+}$ have been synthesized at high temperature with weak reduction atmosphere by traditional solid state reaction method. The role of $H_3BO_3$ as flux and the suitable concentration of Ho as activator on the $CaZrO_3$ : $HO_{3+}$ long persistent phosphors has been investigated. Crystals of $HO_{3+}$ doped $CaZrO_3$ long persistent phosphores were characterized by fluorescence spectrophotometer and photoluminescence (PL). The main emission spectra of 546 nm peak was revealed through synthesizing at high temperature in $N_2$ gas atmosphere. The after glow emission spectra of $CaZrO_3$ : $HO_{3+}$ long persistent phosphores arise at 546 nm peak of narrow range. because that revealed pure green color. Green long persistent phosphors have been observed in the system for over 5 h after UV irradiation (254 nm). The main emission peak was ascribed to $HO_{3+}$ ions transition from $^5F_4$, $^5S_2{\to}^5I_3$, and the after glow may be ascribed to the trap centers in the $CaZrO_3$ host lattice.

$Er^{3+}$를 첨가한 $CaZrO_3$ 축광성 형광체의 합성 및 발광 특성 분석

박병석,최종건,Park, Byeong-Seok,Choi, Jong-Koen 한국결정성장학회 2008 韓國結晶成長學會誌 Vol.18 No.1

새로운 $CaZrO_3:Er^{3+}$ 축광성 형광체를 전통적인 고상반응법으로 제조하였으며, 분쇄한 축광성 형광체를 X 선 회절 분석, 광발광 분석, 열발광 분석과 휘도계를 통하여 장잔광 특성을 분석하였다. X 선 회절 분석 결과 순수한 $CaZrO_3$ 결정상을 확인 하였으며, 고온의 질소 분위기에서 합성한 경우 446 nm 와 550 nm의 넓은 발광 피크가 나타났다. 합성한 장잔광 특성의 형광체의 발광 지속시간은 254 nm UV lamp로 여기 시킨 후 어두운 곳에서 6시간 이상 스스로 발광 하였다. 발광 피크는 $Er^{3+}$ 이온의 $^5D_{5/2}{\rightarrow}^4F_{9/2},\;^2H_{12/2},\;^4S_{3/2}{\rightarrow}^4I_{13/2}$ 그리고 $^2G_{9/2}{\rightarrow}^4I_{13/2}$ 전이에 의한 것이며, 잔광 특성은 $CaZrO_3$ 격자 내에 적당한 trap center가 형성 된 것으로 판단된다. Novel long persistent phosphors of $CaZrO_3:Er^{3+}$ have been synthesized by traditional solid state reaction method. The long persistent phosphor crystalline particles were characterized by the X-ray diffraction (XRD), photoluminescence spectrophotometer, thermoluminescence (TL) and luminance meter. The results reveal that the samples are composed of single $CaZrO_3$ phase. The broadband emission spectra of 446 nm peak and 550 nm peak was revealed by synthesized at high temperature in $N_2$ gas. Green long persistent phosphors have been observed in the sys_em for over 6 h after UV irradiation (254 nm). The main emission peak was ascribed to $Er^{3+}$ ions transition from $^5D_{5/2}{\rightarrow}^4F_{9/2},\;^2H_{12/2},\;^4S_{3/2}{\rightarrow}^4I_{13/2}\;and\;^2G_{9/2}{\rightarrow}^4I_{13/2}$, and the afterglow may be ascribed to the suitable trap centers in the $CaZrO_3$ host lattice.

새로운 $Tb^{3+}$ 이온 활성 축광성 형광체의 발광 특성

박병석,최종건,Park, Byeong-Seok,Choi, Jong-Geon 한국결정성장학회 2009 韓國結晶成長學會誌 Vol.19 No.3

새로운 $CaZrO_3$, 축광성 형광체를 고온의 약한 환원 분위기에서 전통적인 고상반응법으로 합성하였다 광발광 분석 결과 $Tb^{3+}$ 이온을 첨가한 $CaZrO_3$ 축광성 형광체는 $^5D_3$, $^5D_4$ 에너지 준위에서 $^7F_1{\sim}^7F_6$ 준위로의 전이에 의해 황녹색의 발광을 나타내며, 고온의 질소분위기에서 합성한 경우의 축광성 형광체에 대한 스펙트럼의 주 피크는 $^5D_4{\rightarrow}^7F_5$ 전이에 의한 542 nm의 발광 피크가 생성되었다. $CaZrO_3:Tb^{3+}$ 축광성 형광체의 잔광 발광 스펙트럼은 좁은 영역의 546 nm의 피크가 강하게 생성되었다 잔광 휘도는 254 nm 자외선을 조사하고 전원을 끈 후에 측정하였으며, 녹황색의 축광성 형광체가 사람이 어두운 곳에서 인지 가능한 $0.32\;mcd/m^2$까지 8시간 지속됨을 관찰하였다. A new long persistent phosphors of $CaZrO_3$ was synthesized at high temperature with weak reduction atmosphere by a traditional solid state reaction method. Photoluminescence spectra analysis showed that the $CaZrO_3$ doped with $Tb^{3+}$ emitted green-yellow emission caused by the energy level transition from the $^5D_3$ and $^5D_4$ to $^7F_1{\sim}^7F_6$. The main emission spectra of 542 nm peak by the $^5D_4{\rightarrow}^7F_5$ transition was revealed through synthesizing at high temperature in $N_2$ gas atmosphere. The afterglow emission spectra of $CaZrO_3:Tb^{3+}$ long persistent phosphores arise at 546 nm peak of narrow range. After the 254 nm ultraviolet light excitation source was switched off, the green-yellow long persistent phosphor can be observed which could last for 8 h in the limit of light perception of dark-adapted human eyes ($0.32\;mcd/m^2$).

PLC(전력선 통신) 기술개발 및 표준화 동향

박병석,Park, Byeong-Seok 대한전기협회 2012 전기저널 Vol.426 No.-

변색효과 cubic zirconia의 단결정 성장과 특성평가

박병석,최종건,Park, Byeong-Seok,Choi, Jong-Keon 한국결정성장학회 2007 韓國結晶成長學會誌 Vol.17 No.3

Cubic Zirconia single crystals having changeable color with light source were grown by skull melting method. Strong absorption of yellow color region light by Co and Nd and the absorption in violet color region by Fe led the color change from blue-green to red-purple with the light source from fluorescent to incandescent lamp. Color of crystals varied not only by the dopants but yttria contents and the conditions far heat treatment. 광원에 따라 색상이 변화하는 cubic zirconia 단결정을 skull melting 법으로 성장하였다. Co와 Nd에 의해서 황색 영역의 강한 흡수가 일어나며, Fe에 의해 보라색 영역의 흡수가 일어남에 따라 광원이 형광등에서 백열등으로 변화할 때 청-녹색에서 적-자색으로 변화가 발생한다. 첨가물에 의해서 뿐만 아니라 yttria 함량과 열처리 조건 변화에 의해서도 결정의 색이 변화하였다.

10 MV 이상 고에너지 치료 시 발생되는 광중성자의 영향

박병석,안종호,권동열,서정민,송기원,Park, Byoung Suk,Ahn, Jong Ho,Kwon, Dong Yeol,Seo, Jeong Min,Song, Ki Weon 대한방사선치료학회 2013 대한방사선치료학회지 Vol.25 No.1

목 적: 10 MV 이상 고에너지 방사선 치료 시 광핵반응을 통해 광중성자가 발생된다. 광중성자는 방사선하중계수가 X선 보다 커 작은 선량에도 인체에 미치는 영향이 크므로 정확한 선량계산 및 고려가 필요하다. 이에 광자선 에너지 크기와 치료방법에 따른 광중성자의 선량변화를 공간적인 측면에서 비교 분석하였다. 대상 및 방법: 광자선의 에너지 크기에 따른 광중성자의 선량 변화를 측정하고자 동일한 치료부위의 환자를 대상으로 치료 계획을 10 MV와 15 MV conventional plan으로 각각 만들었다. 그리고 치료방법에 따른 차이에 대해 측정하고자 10 MV conventional plan과 10 MV IMRT plan을 각각 만들었다. 검출기의 위치는 광자선원으로부터 isocenter까지의 거리를 100 cm으로 정한 기준점을 $^3He$비례계수기의 중심점에 위치시키고 광중성자 선량을 측정하였다. 또한 중심점을 기준으로 couch의 longitudinal 방향으로 상방, 하방 50 cm 방향으로 각각 $^3He$비례계수기를 위치시켜 위치변화에 따른 선량변화를 측정하여 상용프로그램을 이용하여 분석하였다. 결 과: 에너지 크기에 따른 광중성자의 평균 누적선량은 10 MV, 15 MV conventional RT시 각각 $220.27{\mu}Sv$, $526.61{\mu}Sv$로 15 MV conventional RT가 평균 2.39배의 선량이 증가하였다. 동일한 에너지의 conventional RT와 IMRT의 광중성자의 평균 누적선량은 Conventional RT, IMRT 시 각각 $220.27{\mu}Sv$, $308.27{\mu}Sv$로 IMRT가 1.40배의 선량이 증가하였다. 측정위치에 따른 광중성자의 누적선량은 Conventional RT시 point 2가 3보다 10 MV에서는 약 7.1%, 15 MV에서는 3.0%로 유의하게 높게 측정되었다. 결 론: 고에너지 방사선 치료 시 광중성자에 의한 불필요한 선량을 줄이기 위해 에너지의 선택, 치료 방법의 결정 및 환자의 position을 고려해야 할 것이다. 또한 광중성자의 선량 데이터를 체계화하여 전산화계획 프로그램에 적용되는 방안을 모색하여야 할 것이다. 이는 환자에게 불필요한 선량을 최소화하고 방사선 치료로 인한 2차 암 발생확률과 부작용을 감소시킬 수 있을 것으로 사료된다. Purpose: High-energy radiotherapy with 10 MV or higher develops photoneutron through photonuclear reaction. Photoneutron has higher radiation weighting factor than X-ray, thus low dose can greatly affect the human body. An accurate dosimetric calculation and consultation are needed. This study compared and analyzed the dose change of photoneutron in terms of space according to the size of photon beam energy and treatment methods. Materials and Methods: To measure the dose change of photoneutron by the size of photon beam energy, patients with the same therapy area were recruited and conventional plans with 10 MV and 15 MV were each made. To measure the difference between the two treatment methods, 10 MV conventional plan and 10 MV IMRT plan was made. A detector was placed at the point which was 100 cm away from the photon beam isocenter, which was placed in the center of $^3He$ proportional counter, and the photoneutron dose was measured. $^3He$ proportional counter was placed 50 cm longitudinally superior to and inferior to the couch with the central point as the standard to measure the dose change by position changes. A commercial program was used for dose change analysis. Results: The average integral dose by energy size was $220.27{\mu}Sv$ and $526.61{\mu}Sv$ in 10 MV and 15 MV conventional RT, respectively. The average dose increased 2.39 times in 15 MV conventional RT. The average photoneutron integral dose in conventional RT and IMRT with the same energy was $220.27{\mu}Sv$ and $308.27{\mu}Sv$ each; the dose in IMRT increased 1.40 times. The average photoneutron integral dose by measurement location resulted significantly higher in point 2 than 3 in conventional RT, 7.1% higher in 10 MV, and 3.0% higher in 15 MV. Conclusion: When high energy radiotherapy, it should consider energy selection, treatment method and patient position to reduce unnecessary dose by photoneutron. Also, the dose data of photoneutron needs to be systematized to find methods to apply computerization programs. This is considered to decrease secondary cancer probabilities and side effects due to radiation therapy and to minimize unnecessary dose for the patients.

α - Lactalbumin 이 인지질 vesicle 과 결합하는 데에 관한 연구

박병석,김형만 ( Byoung Seok Park,Hyung Man Kim ) 생화학분자생물학회 1985 BMB Reports Vol.18 No.4

The pH dependent binding of α-lactalbumin to the unilamellar phospholipid vesicles was studied by sedimenting the vesicles after the chemical equilibrium was reached. The binding reactions were carried out in 10 mM buffers at pH values ranging from 2 to 7 with and without added NaCl. The amount of bound α-lactalbumin at low ionic strength showed α-maximum at pH 4. However, at 100 mM ionic strength (90 mM NaCl and 10 mM buffer), the binding affinity increased with decreasing pH value. The binding was found to be reversible at pH 4 but it was partially irreversible at pH 2. It appears therefore, that, hydrophobic interaction is involved in the binding reaction at low pH, The pH dependent structural changes of secondary and tertiary structure of α-lactalbumin were also studied by monitoring the circular dichroism spectra and the difference ultraviolet spectra. The structural change correlated well with the binding behavior. The fluorescense study indicated a change in the environment of tryptophan residue of α-lactalbumin upon binding.

전립선암의 영상유도방사선치료 시 격일 콘빔 CT 적용의 유용성 평가

박병석,안종호,김종식,송기원,Park, Byoung Suk,Ahn, Jong Ho,Kim, Jong Sik,Song, Ki Won 대한방사선치료학회 2014 대한방사선치료학회지 Vol.26 No.2

목 적 : 영상유도방사선치료 시 사용하는 콘빔 CT는 치료자세 오차를 확인하는 중요한 수단이지만 피폭선량을 증가 시키는 단점이 있다. 이에 본 연구는 콘빔 CT의 시행주기를 격일로 하는 시나리오를 만들어 유용성을 평가하고자 한다. 대상 및 방법 : 콘빔 CT를 이용하여 세기변조방사선치료를 받은 전립선암 환자 9명을 대상으로 실제 치료 시 매일 콘빔 CT로 치료자세 오차를 분석하여 보정한 값을 바탕으로 격일로 콘빔 CT를 시행하는 시나리오를 만들었다. 시나리오에서 콘빔 CT를 시행하지 않은 날의 치료자세 오차 값을 실제 치료 시의 치료중심점에서 이동하여 치료계획시스템(Pinnacle 9.2, Philips, USA)에 적용한 후 실제 치료와 동일한 조건으로 재 치료계획을 수립하였으며, 이를 바탕으로 PTV(Planning Target Volume)와 정상장기의 선량분포를 비교 분석하였다. 결 과 : 매일 콘빔 CT를 시행하였을 때의 치료자세 오차 값을 기준으로 격일로 콘빔 CT를 시행하는 시나리오에서는 X, Y, Z축으로 각각 $0.2{\pm}0.73mm$, $0.1{\pm}0.58mm$, $-1.3{\pm}1.17mm$ 차이가 나타났다. 이를 치료계획에 적용하여 재 치료계획을 수립하여 선량분포를 평가한 결과는 매일 콘빔 CT를 시행한 결과와 비교하여 PTV의 Dmean : -0.17 Gy, $D_{99%}$ : -0.71 Gy, 차이가 나타났다. 정상 장기는 직장 벽의 $V_{66}$ : 1.55%, 방광의 $V_{66}$ : -0.76% 차이가 나타났다. 결 론 : 격일로 콘빔 CT를 시행하였을 경우 콘빔 CT에 의한 피폭선량을 감소시키고 촬영으로 인한 추가적인 치료시간을 줄여 줄 수 있다. 또한 PTV, 정상장기의 선량분포의 차이가 크지 않으므로 환자의 상태의 따라 격일 콘빔 CT의 적용을 고려할 수 있을 것으로 사료된다. Purpose : Cone Beam Computed Tomography(CBCT) in Image Guided Radiation Therapy(IGRT), Set-up error can be reduced but exposure dose of the patient due to CBCT will increase. Through this study, we are to evaluate by making a scenario with the implementation period of CBCT as every other day. Materials and Methods : Of prostate cancer patients, 9 patients who got a Intensity Modulated Radiation Therapy(IMRT) with CBCT in IGRT were analyzed. Based on values corrected by analyzing set-up error by using CBCT every day during actual treatment, we created a scenario that conducts CBCT every other day. After applying set-up error values of the day not performing CBCT in the scenario to the treatment planning system(Pinnacle 9.2, Philips, USA) by moving them from the treatment iso-center during actual treatment, we established re-treatment plan under the same conditions as actual treatment. Based on this, the dose distribution of normal organs and Planning Target Volume(PTV) was compared and analyzed. Results : In the scenario that performs CBCT every other day based on set-up error values when conducting CBCT every day, average X-axis : $0.2{\pm}0.73mm$, Y-axis : $0.1{\pm}0.58mm$, Z-axis : $-1.3{\pm}1.17mm$ difference was shown. This was applied to the treatment planning to establish re-treatment plan and dose distribution was evaluated and as a result, Dmean : -0.17 Gy, D99% : -0.71 Gy of PTV difference was shown in comparison with the result obtained when carrying out CBCT every day. As for normal organs, V66 : 1.55% of rectal wall, V66 : -0.76% of bladder difference was shown. Conclusion : In case of a CBCT perform every other day could reduce exposure dose and additional treatment time. And it is thought to be able to consider the application depending on the condition of the patient because the difference in the dose distribution of normal organs, PTV is not large.

Alcohol섭취가 치은열구상피의 투과성에 미치는 영향

박병석,이동주,한경윤,Park, Byung-Suk,Lee, Dong-Joo,Han, Kyung-Yoon 대한치주과학회 1988 Journal of Periodontal & Implant Science Vol.18 No.2

차량의 가감속 제어기 개발

박병석(Byung-Suk Park),이상엽(Sang Yeob Lee),구본경(BonGeong Koo) 한국자동차공학회 2010 한국자동차공학회 학술대회 및 전시회 Vol.2010 No.11

Recently, ADAS such as SCC, CDM becomes hot issue and done in mass-production in luxury passenger cars. SCC control logic is divided in 2 parts; follow&distance control, acceleration control. CDM control logic is composed of collision warning and auto braking braking. Here develops vehicle acceleration control using vehicle speed and longitudinal acceleration sensor for SCC and CDM, and tests in vehicle state. The test results show that developed controller has good performance for SCC.