단결정 $YBa_2Cu_3O_{7-y}$ 벌크 초전도체 제조를 위한 경제적 공정의 개발
박순동,김광모,전병혁,한영희,김찬중,Park, Soon-Dong,Kim, Kwang-Mo,Jun, Byung-Hyuk,Han, Young-Hee,Kim, Chan-Joong 한국초전도학회 2011 Progress in superconductivity Vol.13 No.2
To reduce the processing cost of the single grain REBCO (RE: Rare-earth elements) bulk superconductors, a cost-effective process should be developed. One possible way of developing the cost-effective process is the use of low-cost precursor powders. In this study, the single grain YBCO superconductors were fabricated using a home made powder. $YBa_2Cu_3O_{7-y}$ (Y123) powders were synthesized at $850-900^{\circ}C$ in air by the powder calcination method with repeated crushing and heat treatment steps. The processing parameters for the fabrication of single grain Y123 bulk superconductors, $T_{max}$ (maximum temperature), $T_p$ (peritectic temperature) and a cooling rate through $T_p$ were optimized. To enhance the flux pinning capacity of the single grain Y123 samples, $Y_2BaCuO_5$ (Y211) particles were dispersed in the Y123 matrix by adding $Y_2O_3$ powder to the calcined Y123 powder. Applying the optimized processing condition, the single grain Y123 superconductors with $T_c=91\;K$ and $J_c=1.5{\times}10^4\;A/cm^2$ at 2 T were successfully fabricated using a home made powder. The levitation forces and trapped magnetic field at 77 K measured using a Nd-B-Fe permanent magnet of 5300 G were 47 N and 3000 G, respectively, which are comparable to those obtained for the samples fabricated using a commercial grade Y123 powders.
박순동(Soon Dong Park),이재성(Jae Sung Lee),이석준(Sokjoon Lee),김동규(Dong Kyue Kim) 한국멀티미디어학회 2008 한국멀티미디어학회 학술발표논문집 Vol.2008 No.2
USN(Ubiquitous Sensor Network)은 통신 주체인 센서 노드를 이용하여 다양한 정보를 수집하고, 데이터를 송수신 할 수 있도록 구성된 무선 네트워크이다. 무선 통신을 기반으로 한 USN은 공격자가 물리적인 제약 없이 네트워크에 접근할 수 있어 도청 및 데이터 위ㆍ변조 등과 같은 공격에 쉽게 노출될 위험성이 매우 크다. 네트워크의 신뢰성 보장을 위해 앞서 말한 취약점들을 보완할 수 있는 보안 프로토콜의 개발이 필요하며, 다양한 공격 기법의 분석과 시뮬레이션 환경 개발이 선행된다면 안전성 분석 및 취약성 분석에 도움이 될 것으로 보인다. 본 논문에서는 공격 노드를 개발하고 공격 시나리오를 구성하여 다양한 공격 기법을 재현하고, 모든 노드의 상태를 한눈에 파악할 수 있는 모니터링 시스템을 구현하였다.
박순동(Soon Dong Park),김동규(Dong Kyue Kim) 한국멀티미디어학회 2008 한국멀티미디어학회 학술발표논문집 Vol.2008 No.1
처방전 인증 시스템의 필요성은 오래 전부터 제기되어 왔다. 기 제안된 처방전인증 시스템은 인증 서버를 구축하여 인증에 필요한 데이터를 저장하는 방식으로, 의사의 업무 프라이버시 보호에 대한 문제를 고려하지 않아서 현실적인 적용이 불가능 하였다. 본 논문에서 제안한 방법은 2차원 바코드와 공인인증서를 이용하여 오프라인 상태에서 처방전을 발급하는 방법으로, 기존 인증 시스템의 문제에 대한 해결 방법을 제시하였다.
박순동(Soon-Dong Park),김대용(Daeyong Kim) 대한기계학회 2020 대한기계학회 춘추학술대회 Vol.2020 No.7
We perform density functional theory calculations to investigate adhesion of Fe(001)/Al(001) interface. The simulation results show that the bonding strength of interface is strongly dependent on the stack sequence. In particular, bcc-type of Fe(001)/Al(001) interface exhibits the highest work of separation around 4.01 J/m², which is higher than that of pure Al(001).
저 순도 BaCO<sub>3</sub> 분말을 사용한 Yba<sub>2</sub>Cu<sub>3</sub>O<sub>7-y</sub> 초전도체의 합성
김찬중,박순동,최정숙,전병혁,문종백,이상헌,성태현,Kim, Chan-Joong,Park, Soon-Dong,Choi, Jung-Suk,Jun, Byung-Hyuk,Moon, Jong-Baik,Lee, Sang-Heon,Sung, Tae-Hyun 한국분말야금학회 2008 한국분말재료학회지 (KPMI) Vol.15 No.1
[ $YBa_2Cu_3O_{7-y}$ ](123) powders were synthesized by the solid state reaction method using two different purity $BaCO_3$ powders (99.75% and 99.7% purity) and $Y_2O_3$ (99.9%) and CuO (99.9%) powders. The effect of $BaCO_3$ purity on the formation of a 123 phase and the superconducting properties were investigated. The mixtures of raw powders were calcined at temperature ranges of $800^{\circ}C-880^{\circ}C$ in air and finally made into a single grain samples by a melt processing with top seeding. It was found that a 123 phase was well formed at temperature above $870^{\circ}C$, but the purity effect on the 123 formation was negligible. The single-grain 123 samples prepared from the different $BaCO_3$ powders showed the same $T_c$ value of 90.5 K and similar $J_c$ values about $10^4\;A/cm^2$ at 0 T and 77 K, and $10^3\;A/cm^2$ at 2 T and 77 K. This result indicates that the low purity, cheap price $BaCO_3$ powder can be used as a raw material for the fabrication of single-grain, high-$J_c$ superconducting levitator.
웹 트래픽 추이 분석 기반 비정상행위 탐지 모델의 설계 및 구현
장성민,박순동,Jang, Sung-Min,Park, Soon-Dong 한국컴퓨터산업학회 2005 컴퓨터産業敎育學會論文誌 Vol.6 No.5
최근 들어 폐쇄 환경에서 동작하던 많은 주요 시스템들이 웹 서비스를 제공하면서 호스트는 물론 제공되는 웹기반의 서비스들이 쉽게 공격의 주요 대상이 되고 있다. 뿐만 아니라 웹 컨텐츠나 어플리케이션의 다양성은 새로운 공격 기술을 개발하는 원인이 되기도 한다. 반면 기존의 오용기반 탐지 기법으로는 공격 기술의 발전 속도를 따라가지 못할 뿐더러 새로운 보안 위협을 처리하는 능력이 없다. 따라서 기존의 공격 유형과 함께 새롭게 개발되는 공격과 침입을 탐지하고 대처할 수 있는 기술이 연구되고 개발되고 있다. 본 논문에서는 HTTP 트래픽 패턴과 패킷 정보를 분석하여 HTTP 트래픽 모델에서의 비정상 행위 발생을 실험하였으며, 그 실험 결과를 적용하여 비정상행위를 탐지 가능한 HTTP 트래픽 모델을 설계하고 구현하였다. Recently many important systems that used to be operated in a closed environment are now providing web services and these kinds of web-based services are often an easy and common target of attacks. In addition, the great variety of web content and applications cause the development of new various intrusion technologies, while the misuse-based intrusion detection technology cannot keep the peace with the attacks and it seems to lack the capability to deal with such various new security threats, As a result it is necessary to research and develop new types of detection technologies that can detect newly developed attacks and intrusions as well as to be able to deal with previous types of exploits. In this paper, a HTTP traffic model is tested for its anomaly by using a HTTP request traffic pattern analysis and the field information analysis of the HTTP packet. Consequently, the HTTP traffic models by applying anomaly tests is designed and established.
TiCl$_4$ 수용액에서 침전법에 의한 결정상 TiO$_2$ 초미분체 제조
김선재,정충환,박순동,권상철,박성,Kim, Sun-Jae,Jung, Choong-Hwan,Park, Soon-Dong,Kwon, Sang-Chul,Park, Sung 한국세라믹학회 1998 한국세라믹학회지 Vol.35 No.4
Crystalline TiO2 ultrafine powders were prepared simply by heating and stirring aqueous TiOCl2 solution with {{{{ {Ti }^{4+ } }} concentration of 0.5 M from room temperature to 10$0^{\circ}C$ under 1 atmoshpere. The crystallinity and the particle shape of TiO2 ultrafine powders obtained by simple precipitation method were analyzed us-ing XRD(X-ray diffractometer). SEM(scanning electron microscopy) and TEM(transmission electron mi-croscopy) TiO2 crystalline precipitate with rutile phases is fully formed at the temperatures of up to $65^{\circ}C$ and then TiO2 crystalline precipitate with anatase phase starts to be formed above temperatures $65^{\circ}C$ showing its full formation at 10$0^{\circ}C$ These behaviors of TiO2 crystalline precipitate directly from an aqueous TiOCl2 solution would be caused due to the existence of {{{{ OMICRON ^2+ }} ions from distilled water which oxydize TiOCl2 to TiO2 not hydrolyzing it to Ti(OH)4 Here thermodynamically stable TiO2 rutile phase generally formed at higher temperature is practically precipitated at lower temperatures in this study This may be due to the precipitation by very slow reaction enough to make TiO2 particles allocated into stable rutile structure.