김길수,조태선,서영익,류우석,김영도,Kim, Gil-Su,Jo, Tae-Sun,Seo, Young-Ik,Ryu, Woo-Seog,Kim, Young-Do 한국재료학회 2006 한국재료학회지 Vol.16 No.5
Short-term high temperature degradation test was conducted on Hastelloy X, a candidate tube material for high temperature gas-cooled reactors (HTGR), to evaluate the variation of microstructure and mechanical property in air at $1050^{\circ}C$ during 2000 h. The dominant oxide layer was Cr-oxide and a very shallow Cr-depleted region was observed below the oxide layer. At the beginning of degradation, the island shape $M_6C$ precipitate (M=Mo-rich, Fe, Ni, Cr) was observed in matrix region. After 2000 h degradation, precipitate shape was changed to the chain shape and increased amount of precipitate. These results influenced mechanical property of the specimen which exposed in high temperature. Yield strength was decreased from 115MPa to 89 MPa after 24 h and 2000 h exposure, respectively.
초저열량 식이요법과 체감의이인탕의 병행치료가 비만 환자의 신체조성에 미치는 영향
김길수,김동열,Kim, Gil-Su,Kim, Dong-Yeol 한방비만학회 2001 한방비만학회지 Vol.1 No.1
Objectives: The aim of this study was to the effect of very low calorie diet with Chegameuiintang to treat obese patients . Methods: We have evaluated 54 obese patients during very low calorie diet with Chegameuiintang weight-reducing regime by determining the body composition before and 1 month, 2 months after treatment by Bioelectrical impedence analysis . Results: In the change of body composition by the treatment, mean weight reduction was 11.59kg(15.57% of initial weight), mean weight reduction after 1month was 7.68kg( 10.31% of initial weight), mean weight reduction after 2 months was 3.91 kg(5.86% of weight after 1 month). Mean reduction in total fat mass was 8.03kg(2914% of the initial fat mass) which constitutes 69.28%. Mean reduction in lean body mass was 3.56kg(7.59%) Conclusions: This study has demonstrated that the compound therapy of very low calorie diet and Chegameuiintang (Tiganyiyiren-tang) is the good way of weight reduction, which reduces total fat mass and preserves lean body mass.
고혈압, 고지혈증, 퇴행성 관절염을 동반한 비만 환자의 증례보고
김길수 ( Gil Su Kim ),김동열 ( Dong Yeol Kim ) 한방비만학회 2001 한방비만학회지 Vol.1 No.1
Obesity is an excess of body fat frequently resulting from an imbalance between energy intake and expenditure, raises the risk of morbidity from chronic diseases such as hypertension, dyslipidemia, type 2 diabetes, coronary heart disease, stroke, fatty liver and osteoarthritis. Recently we experienced a 51 years old obese woman who was accompanied with hypertension, dyslipidemia and osteoarthritis. Through weight reduction program(very low calorie diet, Chegameuiintang, exercise) during 3 months, total weight loss was 17.0kg, her condition was improved.
방전플라즈마 소결법을 이용한 ZnS-SiO<sub>2</sub> 복합재료의 제조와 기계적 특성
신대훈,김길수,이영중,조훈,김영도,Shin, Dae-Hoon,Kim, Gil-Su,Lee, Young-Jung,Cho, Hoon,Kim, Young-Do 한국분말야금학회 2008 한국분말재료학회지 (KPMI) Vol.15 No.1
ZnS-$SiO_2$ composite is normally used for sputtering target. In recent years, high sputtering power for higher deposition rate often causes crack formation of the target. Therefore the target material is required that the sintered target material should have high crack resistance, excellent strength and a homogeneous microstructure with high sintered density. In this study, raw ZnS and ZnS-$SiO_2$ powders prepared by a 3-D mixer or high energy ball-milling were successfully densified by spark plasma sintering, the effective densification method of hard-to-sinter materials in a short time. After sintering, the fracture toughness was measured by the indentation fracture (IF) method. Due to the effect of crack deflection by the residual stress occurred by the second phase of fine $SiO_2$, the hardness and fracture toughness reached to 3.031 GPa and $1.014MPa{\cdot}m^{1/2}$, respectively.
고속 중성자 조사에 의한 원자로 용기재료내의 결함생성이 자기적 특성변화에 미치는 영향
정명모,김길수,장기상,유근배,박덕근,김길무,윤인섭,홍치유,Jeong, Myeong-Mo,Kim, Gil-Su,Jang, Gi-Sang,Yu, Geun-Bae,Park, Deok-Geun,Kim, Gil-Mu,Yun, In-Seop,Hong, Chi-Yu 한국재료학회 1999 한국재료학회지 Vol.9 No.12
In order to assess the effects on the magnetic properties due to the defect in the material irradiated by fast neutron ranging $10^0-10^{18}n/cm^2$, the magnetic properties such as maximum magnetic induction, coercivity, remanence, Barkhausen Noise Amplitude(BNA), Barkhausen Noise Energy(BNE) and hardness were measured. It is shown that the magnetic properties and hardness do not change by the fast neutron irradiation under $10^{17}n/cm^2$. Therefore, in this experiment, it is understood that the magnetic properties decrease by the increase of hardness. This measurement method can be used to evaluate the neutron irradiation embrittlement nondestructively since the magnetic properties and hardness do change by the neutron irradiation over $10^{17}n/cm^2$ consistently. 고속중성자가 조사된 재료내에 생성된 결함이 자기적 특성에 미치는 영향을 평가하기 위해서, 대기압, $70^{\circ}C$에서 고속 중성자(조사량 : $10^0-10^{18}n/cm^2$, E>1 MeV)가 조사된 원자로 용기강재의 자기적 성질(최대 자기유도, 보자력, 잔류자기, Barkhausen noise amplitude (BNA), Barkhausen noise energy (BNE)) 및 경도를 측정하였다. $10^{17}n/cm^2$ 이하의 고속 중성자 조사에서 자기적 특성 및 경도의 변화는 없는 것으로 나타났으나, $10^{17}n/cm^2$ 이상 조사에서는 최대 자기유도, 보자력, 잔류자기, BNA, BNE는 감소하고, 경도는 증가하는 것으로 나타났다. 따라서 경도 증가에 따라 자기적 특성은 감소하는 것을 알 수 있었으며, 측정된 요소들이 전부 $10^{17}n/cm^2$ 이상에서 변화를 보이고 있어 실험결과는 일관성이 있어, 이 방법을 이용하여 중성자 조사취화를 비파괴적으로 평가할 수 있음을 알 수 있었다.