1000MPa급 DP강의 Nd:YAG 레이저 용접부의 기계적 성질과 성형성에 미치는 용접 속도의 영향
장진영,최우남,정병훈,강정윤,Jang, Jin-Young,Choi, Woo-Nam,Jung, Byung-Hun,Kang, Chung-Yun 대한용접접합학회 2009 대한용접·접합학회지 Vol.27 No.2
The effects of welding speed were investigated on penetration characteristics, defects and mechanical properties including formability test in Nd:YAG laser welded 1000MPa grade DP steels. A shielding gas was not used and bead-on-plate welding was performed with various welding speeds at 3.5kW laser power. Defects of surface and inner beads were not observed in all welding speeds. As the welding speed increased, the weld cross-section varied from the trapezoid having wider bottom bead, through X type, finally to V type in partial penetration range of welding speeds. The characteristic of hardness distribution was also investigated. The center of HAZ had maximum hardness, followed by a slight decrease of hardness as approaching to FZ. Significant softening occurred at the HAZ near BM. Regardless of the welding speed, the weld showed approximately the same hardness distribution. In the perpendicular tensile test with respect to the weld direction, all specimens were fractured at the softening zone. In the parallel tensile test to the weld direction, the first crack occurred at weld center and then propagated into the weld. Good formability over 80% was taken for all welding conditions.