$CO_2$가스 배관용접부의 파괴인성평가에 관한 연구

나의균,유효선,오석형,Na, Ui-Gyun,Yu, Hyo-Seon,O, Seok-Hyeong 대한기계학회 2000 大韓機械學會論文集A Vol.24 No.7

The purpose of this study is to examine the fracture toughness of the welded pipe from the viewpoint of FATT for the S38 and S42 steels used widely as the pipe material. Post weld heat treatment(PW HT) was carried out like following conditions: temperature of 67$0^{\circ}C$, I hour of holding time and cooling in furnace. Fracture toughness was obtained by measuring the crack opening displacement(COD) of the notched specimens over the range of temperature from -14$0^{\circ}C$ to -$25^{\circ}C$. Hardness values at fusion line near around were the highest and the microstructures at welded zone were coarsened. Regardless of the pipe materials, COD and temperature curves of the as-welds were moved toward higher temperature compared with those of the parents. However, COD and temperature curves of the PWHT specimens were positioned at lower temperature compared with those of the as-welds. The more heat input causes to decrease the COD values at the constant temperature. It was verified through the recrystallization treatment that PWHT was attributed to move toward lower temperature region considerably due to the improved plastic deformation at the same applied COD value of 0.3mm and softening effect. In case of the weldment of S38 steel, cleavage fracture was observed at -105$^{\circ}C$ unlike the structural steels, in which brittle fracture mode was generally shown at - 196$^{\circ}C$.

수열 Hot Press법에 의한 화강암 폐재의 고화체형성 및 평가기술의 개발에 관한 연구

나의균,정세희,Na, Eui-Gyun,Chung, Se-He,Takahashi, Hideaki 한국재료학회 1995 한국재료학회지 Vol.5 No.3

본 연구에서는 석재공장 주변의 오염원으로 되고 있는 화강암 폐재의 고화체의 형성과 평가 기술에 관한 내용을 다루었다. 이를 위해, 최근 고화체의 함성기술로서 높이 평가받고 있는 수열 Hot press법을 이용하여 분말형태의 화강암 폐기물을 고화시키는데 필요한 조건을 찾아내었다. 아울러 고화체의 기계적 성질과 파면의 양상 및 수열실험동안 발생된 생성물 사이의 상호 관계를 고찰하였다. 고화체의 기계적 성질은 수열실험조건에 의존성이 있었으며, 적절한 고화조건은 반응온도 30$0^{\circ}C$, 유지시간 1시간이었다. 또한 고화체의 파면은 반응온도 및 유지시간에 따라 현저히 다른 양상을 보였으며, 수열실험동안 다양한 화합물이 생성되었다. 그 중에서 Xonotlite와 Talc는 고화체의 강도를 저하시키는 주된 화합물이었다.

수열 Hot press법에 의한 화강암폐재의 고화체형성과 AE특성 평가에 관한 연구

나의균,Na, Ui-Gyun,Toshiyuk, Hashida 한국재료학회 1996 한국재료학회지 Vol.6 No.3

본 연구는 화강암 폐재의 재활용을 목적으로 한 기초적인 연구로서, 분말형태의 화강암폐재를 Ca(OH2)와 혼합하여 수열 hot press 법에 의해 고화시켰다. 아울러 고화체의 기계적 성질을 평가하였으며, 미시적 조직구조의 변화 및 파괴거동을 파악하기 위해 음향방출실험을 실시하였다. 고화체의 기계적 성질은 수열온도의 의존성이 있었으며, 28$0^{\circ}C$에서 최대강도를 보였다. 또한 고화체의 파면은 수열온도에 따라 현저히 다른 양상을 보였으며, 수열실험동안 다양한 화합물이 생성되었다. 그 중에서 cyclowollastonite, tobermorite 및 rankinite 등은 강도를 향상시키는 주된 화합물이었고, crossite 및 xonotlite 등은 강도의 저하를 초래하였다. 한편, 기공이 많이 존재할수록 AE counts는 더많이 발생하였으며, 최대하중에서 AE counts는 최대치를 보였고, 강도가 증가함에 따라 AE신호는 보다 많이 방출되었다.

암석폐재의 고화체 합성기술의 개발과 파괴인성평가에 관한 연구

나의균,유효선,김진용,이종기,정세희,Na, Eui-Gyun,Yu, Hyosun,Kim, Jin-Yong,Lee, Jeong-Gee,Chung, Se-Hi 대한기계학회 1997 大韓機械學會論文集A Vol.21 No.9

The hot press apparatus to obtain the solidified rocks with 60mm of diameter against rock waste was developed, and the optimum conditions for solidification were founded out, of which were 300.deg. C of temperature and 1hr of holding time. The solidified rocks reinforced with the fibers (carbon, steel) were made by means of a hydrothermal hot press method. Fracture toughness of those was obtained using the round compact tension(RCT) specimens. Load and displacement behaviours of the solidified rocks reinforced with the fibers were dependent upon the fiber volume fraction and kind of the fibers. Strength and fracture energy of the solidified rocks with steel were much larger than those of the solidified ones with carbon because of the Bridge's effect, multiple cracking and crack branching phenomena.

海水環境에서 鋼 熔接部의 環境强度評價에 關한 硏究 II

나의균,임재규,조규종,정세희 대한용접접합학회 1989 대한용접·접합학회지 Vol.7 No.1

The purpose of this study is to investigate the corrosion fatigue crack growth of PWTHT specimens(SS41, SM53B) which are the compact tension ones extracted from the muti-passed weldment and weld block. The corrosion fatigue test was done at the cyclic stress frequency of 3Hz in 3.5% NaCl solution. The results are as follows. 1. Corrosion fatigue crack growth of as-weld was slower than that of base metal. 2. In the low .DELTA.K region, the effect of corrosion environment on crack growth was obvious. However, the corrosion effect decreased with the .DELTA.K slowly. 3. The behaviour of fatigue and corrosion fatigue crack growth depended on the material, heat treatment as well as experimental conditions. 4. Corrosion fatigue crack growth of PWHT specimens(SS41, SM53B) subjected to 1/4hr, was increased compared with that of as-weld. 5. There was a tendency that the exponent value(m) obtained in 3.5% NaCl solution was decreased in comparison with that in air, and the material constant(C)was increased for Paris equation, da/dN=C((.DELTA.K))$^{m}$ , compared with that in air considerably.

전기화학적 분극법에 의한 1.0Cr-0.5Mo강의 경년열화 평가에 관한 연구

나의균,김훈,이종기,Na, Eui-Gyun,Kim, Hoon,Lee, Jong-Gi 대한기계학회 1998 大韓機械學會論文集A Vol.22 No.1

The contents of this paper include a non-destructive technique for evaluating the degradation of the boiler superheater tube in a fossil power plant through an electrochemical polarization test. Correlation between Ip of polarization parameter and SP-DBTT for the superheater tubes in long-term use was obtained. 1.0Cr-0.5Mo steel was degraded by softening, and the degree of degradation was dependent upon carbides with Cr and Mo elements. Since brittle fracture at low temperature and ductile fracture mode at high temperature were shown, similarity between standard Charpy and small punch tests could be found. In addition, SP-DBTT showing the degree of degradation was higher, as the time-in use of the materials got longer. Electrolyte including picric acid of 1.3 g in distilled water of 100ml at 25.deg. C temperature and sodium tridecylbenzene sulfonate with 1g could be applied to evaluate the degradation of 1.0Cr-0.5Mo steel by means of the electrochemical polarization test. Ip and Ipa values measured through the electrochemical test are the appropriate parameters for representing the degradation of the superheater tube(1.0Cr-0.5Mo steel) for the fossil power plant. It is poassible to evaluate the degradation of materials with different time histories electrochemically, by Ip value only, at field test.

암석폐재의 고화체 합성 기술의 개발과 고화기구의 평가에 관한 연구

나의균,유효선,정세희,Na, Ui-Gyun,Yu, Hyo-Seon,Jeong, Se-Hui 한국재료학회 1997 한국재료학회지 Vol.7 No.4

본 연구에서는 암석폐재를 대상으로 직경이 60mm인 고화체를 얻을 수 있는 수열 hot press 장치를 개발하였고, 고형화를 위한 최적조건을 찾아내는 내용을 다루었다. 이어 고화체의 기계적 성질을 평가하였고, 고화기구와 미시적 파괴거동을 규명하기위하여 SEM관찰 및 음향방출실험을 실시하였다. 고형화를 위한 최적조건은 NaOH용액이 10wt%, 수열온도가 30$0^{\circ}C$이고, 유지시간이 1시간이었다. 또한 수열반응동안에 다양한 제 2화합물들이 생성되었으며, 이들은 고화체의 기계적 성질에 큰 영향을 미쳤다. 아울러 원석의 경우에는 AE Counts가 초기화중에서부터 나타났으나, 고화체는 초기하중에서 전혀 AE Counts가 검출되지 않았다. 이와같은 사실로부터 수열 hot press법에 의해 얻어진 고화체는 원석과는 다르게 암석 입자간의 결합이 보다 치밀하게 이루어지고 있음을 유추할 수 있다.

인가전위 하에서 HT-60강 용접부의 SCC특성 평가

나의균,Na, Ui-Gyun 대한기계학회 2002 大韓機械學會論文集A Vol.26 No.5

The susceptibility of SCC for the weldment and PWHT specimens of HT-60 steel was evaluated using a slow strain rate method under applied potential by means of the potentiostat in synthetic seawater. In case of the parent, anodic polarization voltage was inappropriate in elongating the time to failure(TTF). -0.8V corresponding to cathodic protection range is most effective in improving the SCC resistance against corrosive environment. In case of the weldment, the values of reduction of area(ROA) and TTF at -0.68V corresponding to cathodic polarization value were 45.2% and 715,809sec which were the largest and longest life among other applied potentials. Those were vise versa at -1.1V. In case of the PWHT specimens, TTF and ROA at -0.68V was longest and largest like the weldment. Besides, PWHT is effective in prolonging the time to failure of the welded off-shore structure due to softening of effect. Regardless of the weldment and PWHT specimen, as corrosion rate gets higher, TTF becomes shorter and deformation behaviour for the weldment and PWHT specimen at -1.1V was shown to be irregular. Finally, it was found that specimens showed brittle fracture at -1.1V, but more ductile fracture accompanying the micro-cracks at applied potential of -0.68V.

HT-60강 용접부의 SCC 및 AE신호특성에 관한 연구

나의균,유효선,김훈 한국비파괴검사학회 2001 한국비파괴검사학회지 Vol.21 No.1

인공해수에서 HT-60강 용접부의 응력부식균열(SCC)과 음향방출(AE)신호특성을 알아보기 위하여 SCC와 AE실험을 동시에 실시하였으며, 양 실험결과를 상호 비교ㆍ분석하였다. 모재의 경우, -0.8V에서 보다 긴 파단수명을 보였고, 용해기구 등으로 인하여 -0.8V에 비해 -0.5V에서 AE가 많이 발생하였다. 그러나 시험편에 가해진 전위 값에 관계없이 최대하중 이후의 영역에서 AE 발생과 큰 진폭의 범위(40~100dB)를 나타내었으며 최대하중 이후에도 AE 발생이 활발하였다. 또한, 보다 크고 많은 균열이 파단면에 형성되었음을 SEM관찰을 통하여 관찰할 수 있었으며, 이들 결과로부터 용접부는 인공해수에서 SCC현상이 가장 심하게 일어나고 있음을 확인할 수 있었다. 후열처리는 용접부의 연화를 초래하였고, 용접재에 비해 부식환경에 대한 민감도를 떨어뜨리는 효과를 가져왔다. In order to characterize the microscopic fracture behaviour of the weldment during stress corrosion cracking(SCC) phenomena, SCC and acoustic emission(AE) tests were carried out simultaneously and the correlation between mechanical parameters obtained from SCC and AE tests was investigated. In the case of base metal, much more AE events were produced at -0.5V than at -0.8V because of the dissolution mechanism before the maximum load. Regardless of the applied voltages to the specimens, however, AE events decreased after the maximum load. In the case of weldment, lots of AE events with larger amplitude range(40~100dB) were produced because of the singularities of weld HAZ in comparison to the base metal and post-weld heat-treated (PWHT) specimens. Numerous and larger cracks for the weldment were observed on the fractured surfaces by SEM examination. From these results, it was concluded that SCC for the weldment appeared most severely in synthetic seawater. Weld HAZ was softened by PWHT which also contributed to the reduced susceptibility to corrosive environment in comparison to weldment.

SS41강 다층용접부의 피로균열진전거동 평가에 관한 연구

羅義均 군산대학교 1993 群山水産專門大學 硏究報告 Vol.28 No.1

The purpose of this study is to evaluate the effects of PWHT on fatigue crack growth behaviours for the multi-passed weldments. Multi-passed weld was done using the submerged arc welder. Heat input per each pass was 30KJ/cm. Microstructure was observed by means of the optical microscope. Various kinds of microstructures through the midsection were produced due to the multi- passed welding process. Two kinds of specimens(0.5CT size, weld block) were given to PWHT(post weld heat treatment: PWHT). Fatigue test was conducted at the frequency of 3.3Hz with sine wave. The obtained data were analyzed from the view point of fracture mechanics. The crack growth behaviour was dependent upon PWHT conditions. In Paris's equation da/dN=C(ΔK)n, exponent value(n) for PWHT specimens increases and the vague of material constant(C) decreases compared with that for the as-weld.