Chun, Hui-Gon,Oskomov, Konstantin V.,Sochugov, Nikolay S.,Lee, Jing-Hyuk,You, Yong-Zoo,Cho, Tong-Yul The Korean Society Of Semiconductor Display Techno 2003 한국반도체장비학회지 Vol.2 No.1
Plasma generator based on non-self-sustained low-pressure arc discharge has been examined as a tool for deposition of highly-adhesive hydrogenated amorphous diamond-like carbon(DLC) films. Since the discharge is stable in wide range of gas pressures and currents, this plasma source makes possible to realize both plasma-immersion ion implantation(PIII) and plasma-immersion ion deposition(PIID) in a unified vacuum cycle. The plasma parameters were measured as functions of discharge current. Discharge and substrate bias voltage parameters have been determined for the PIII and PIID modes. For PIID it has been demonstrated that hard and well-adherent DLC coating are produced at 200-500 eV energies per deposited carbon atom. The growth rates of DLC films in this case are about 200-300 nm/h. It was also shown that short(∼60$\mu\textrm{s}$) high-voltage(> 1kV) substrate bias pulses are the most favorable for achieving high hardness and good adhesion of DLC, as well as for reducing of residual intrinsic stress are.
질소 이온이 주입된 STS 316L 스테인리스 강에서의 상변화와 집합조직이 내식성에 미치는 영향
전신희,공영민,Jun, Shinhee,Kong, Young-Min 한국재료학회 2015 한국재료학회지 Vol.25 No.6
In this study, nitrogen ions were implanted into STS 316L austenitic stainless steel by plasma immersion ion implantation (PIII) to improve the corrosion resistance. The implantation of nitrogen ions was performed with bias voltages of -5, -10, -15, and -20 kV. The implantation time was 240 min and the implantation temperature was kept at room temperature. With nitrogen implantation, the corrosion resistance of 316 L improved in comparison with that of the bare steel. The effects of nitrogen ion implantation on the electrochemical corrosion behavior of the specimen were investigated by the potentiodynamic polarization test, which was conducted in a 0.5 M $H_2SO_4$ solution at $70^{\circ}C$. The phase evolution and texture caused by the nitrogen ion implantation were analyzed by an X-ray diffractometer. It was demonstrated that the samples implanted at lower bias voltages, i.e., 5 kV and 10 kV, showed an expanded austenite phase, ${\gamma}_N$, and strong (111) texture morphology. Those samples exhibited a better corrosion resistance.
TiC 이온 주입 층에 증착된 DLC 박막의 트라이볼로지적 특성
이진우(Jin-Woo Yi),김종국(Jong-KuK Kim),김석삼(Seock-Sam Kim) 대한기계학회 2004 대한기계학회 춘추학술대회 Vol.2004 No.4
Effects of ion implantation and deposition on the tribological properties of DLC film as a function of implanted energies and process times were investigated. TiC ions were implanted and deposited on the Si-wafer substrates followed by DLC coating using ion beam deposition method. In order to study tribological properties such as friction coefficient and behavior of DLC film on the modified surface as a function of implanted energies and process times, we used a ball-on-disc type apparatus in the atmospheric environment. From results of wear test, as the implanted energy was increased, the friction coefficient was more stable below 0.1.