http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
롤투롤 스퍼터를 이용하여 PET 기판 위에 제조된 ITO 박막의 색도(b*) 및 투과도 연구
서성만,강보갑,김후식,임우택,최식영,Seo, Sung-Man,Kang, Bo-Gab,Kim, Hu-Sik,Lim, Woo-Taik,Choi, Sik-Young 한국재료학회 2009 한국재료학회지 Vol.19 No.7
Indium Tin Oxide (ITO) thin films on Polyethylene Terephtalate (PET) substrate were prepared by Roll-to-Roll sputter system with targets of 5 wt% and 10 wt% $SnO_2$ at room temperature. The influence of the chromaticity (b*) and transmittance properties of the ITO Films were investigated. The ITO thin films were deposited as a function of the DC power, rolling speed, and Ar/$O_2$ gas flow ratio, and then characterized by spectrophotometer. Their crystallinity and surface resistance were also analyzed by X-ray diffractometer and 4-point probe. As a result, the chromaticity (b*) and transmittance of the ITO films were broadly dependent on the thickness, which was controlled by the rolling speed. When the ITO films were prepared with the DC power of 300 W and the Ar/$O_2$ gas flow ratio of 30/1 sccm using 10 wt% $SnO_2$ target as a function of the rolling speeds 0.01 through 0.10 m/min, its chromaticity (b*) and transmittance were about -4.01 to 11.28 and 75.76 to 86.60%, respectively. In addition, when the ITO films were deposited with the DC power of 400W and the Ar/$O_2$ gas flow ratio of 30/2 sccm used in 5 wt% $SnO_2$ target, its chromaticity (b*) and transmittance were about -2.98 to 14.22 and 74.29 to 88.52%, respectively.
롤투롤시스템을 이용하여 PET 필름위에 제조된 SiO<sub>2</sub>-ITO 박막의 색도(b*), 면저항과 투과도 연구
박미영,김정수,강보갑,김혜영,김후식,임우택,최식영,Park, Mi-Young,Kang, Bo-Gab,Kim, Jung-Soo,Kim, Hye-Young,Kim, Hu-Sik,Lim, Woo-Taik,Choi, Sik-Young 한국재료학회 2011 한국재료학회지 Vol.21 No.5
This paper has relatively high technical standard and experimental skill. The fabrication of TCO film with high transparency, low resistance and low chromaticity require exact control of several competing factors. This paper has resolved these problems reasonably well, thus recommended for publication. Indium tin oxide(ITO) thin films were by D.C. magnetron roll-to-roll sputter system utilizing ITO and $SiO_2$ targets of ITO and $SiO_2$. In this experiment, the effect of D.C. power, winding speed, and oxygen flow rate on electrical and optical properties of ITO thin films were investigated from the view point of sheet resistance, transmittance, and chromaticity($b^*$). The deposition of $SiO_2$ was performed with RF power of 400W, Ar gas of 50 sccm and the deposition of ITO, DC power of 600W, Ar gas of 50 sccm, $O^2$ gas of 0.2 sccm, and winding speed of 0.56m/min. High quality ITO thin films without $SiO_2$ layer had chromaticity of 2.87, sheet resistivity of 400 ohm/square, and transmittance of 88% and $SiO_2$-doped ITO Thin film with chromaticity of 2.01, sheet resistivity of 709 ohm/square, and transmittance of more than 90% were obtained. As a result, $SiO_2$ was coated on PET before deposition of ITO, their chromaticity($b^*$) and transmittance were better than previous results of ITO films. These results show that coating of $SiO_2$ induced arising chromaticity($b^*$) and transmittance. If the thickness of $SiO_2$ is controlled, sheet resistance value of ITO film will be expected to be better for touch screen. A four point probe and spectrophotometer are used to investigate the properties of ITO thin films.