국산 지르콘사로부터 부분 안정화 지르코니아의 제조 및 그 응용에 관한 연구 I. 국산 지르콘사로부터 고순도 지르코니아 분말의 제조
김환,선우식,신건철,황규홍,Kim. H.,Sunwoo, S.,Shin, K.C.,Hwang, K.H. 한국세라믹학회 1987 한국세라믹학회지 Vol.24 No.2
ZrO2 powders having high purity were prepared from domestic zircon sand using the caustic fusion method and the soda ash sintering process. In the caustic fusion method, ZrO2 recovery was reached to 96% when 100/140 mesh zircon was reacted with NaOH at the NaOH/Zircon mole ratio 6 and at 650$^{\circ}C$ for 2 hours. And in the soda ash sintering process, ZrO2 was recovered to 88.5% when -325 mesh zircon was reacted with Na2CO3 at the Na2CO3/Zircon mole ratio 1.1 and 1050$^{\circ}C$ for 2 hours. In both cases, Zr component was extracted to ZrOCl2, subsequently crystallized to ZrOCl2$.$8H2O to increase the purity, and converted to ZrO2 by precipitation. And to increase the sinter ability of powder, Cl- ion was removed and strong agglomeration was avoided by methanol distribution of Zr(OH)4 precipitates.
국산 지르콘사를 이용한 부분 안정화 지르코니아의 제조 및 그 응용에 관한 연구 : II. 부분 안정화 지르코니아 소결체의 제조 및 그 특성
김환,선우식,강종봉,심규송,신건철,황규홍,Kim, H.,Sunwoo, S.,Kang, J.B.,Shim, K.S.,Shin, K.C.,Hwang, K.H. 한국세라믹학회 1988 한국세라믹학회지 Vol.25 No.2
The microstructural changes in partially stabilized MgO-ZrO2 alloys during heat treatment and mechanical properties of ZrO2(Y2O3)/Al2O3 systems have been studied. 9mol% MgO-ZrO2 powders were sintered at 1800$^{\circ}C$ for 4 hours and these specimens were aged at 1420$^{\circ}C$ and 1100$^{\circ}C$ secondly. These specimens have high thermal shock resistance and high toughness. The bend strength of Y-PSZ/Al2O3 composites conventially sintered were increased by HIP from 650MPa to 980MPa.