급격산화법에 의해 제조된 $\delta$-FeOOH의 열분해과정
박영도,이훈하,김태옥 한국세라믹학회 1994 한국세라믹학회지 Vol.31 No.12
The precipitate of FeCl2.4H2O and NaOH, Fe(OH)2 was rapidly made to oxidize by H2O2 to prepare $\delta$-FeOOH. The particle size, surface and morphology of $\delta$-FeOOH, and the shape and structure of thermally decomposed $\delta$-FeOOH were investigated by the use of high resolution STEM. $\delta$-FeOOH prepared under the condition of reaction temperature of Fe(OH)2 at 4$0^{\circ}C$, [OH-][Fe2+]=5 and aging time of 2 hr Fe(OH)2, had 630$\AA$ mean particle size, 4~5 aspect ratio, 20.8 emu/g saturation magnetization and 210 Oe coercivity. The edges of $\delta$-FeOOH were inclined to (001) about 41$^{\circ}$, 60$^{\circ}$ and coincident with (102), (101) respectively. When $\delta$-FeOOH was thermally decomposed at 25$0^{\circ}C$ for 2 hr in vacuo, which had micropores of 0.9 nm thickness and crystallites of 2.4 nm thickness. (001)hex, [10]hex. of $\delta$-FeOOH parallel with (001)hex, [100]hex. of $\alpha$-Fe2O3 respectively. This showed three dimensional topotaxial structure transition, which was investigated by SADP (Selected Area Diffraction Pattern) of STEM.
Ba-Sol을 도포한 $\delta$-FeOOH로부터 Ba-Ferrite 단결정 미리자의 제조와 그 자기적 특성
박영도,이훈하,이재형,오영우,김태옥 한국세라믹학회 1995 한국세라믹학회지 Vol.32 No.12
Hexagonal $\delta$-FeOOH was coated with Ba-Sol, which was produced by hydrolizing Ba(OC2H5)2, Ba-Sol coated $\delta$-FeOOH spread on a stainless plate, dried at 8$0^{\circ}C$ and then heat-treated. In this way, Ba-ferrite fine particles were produced. although there was a difference in a degree of hydrolysis of Ba(OC2H5)2, crystalline phase of Ba-ferrite appeared around 617$^{\circ}C$, and Ba-ferrite single phase was obtained after heat treatment at 80$0^{\circ}C$ for 2 hr. When Ba-ferrite was made from Ba-Sol coated $\delta$-FeOOH, $\delta$-FeOOH was thermally decomposed to $\alpha$-Fe2O3 at $700^{\circ}C$, producing a porous structure which was observed by TEM photographs. But the porous structure was not observed at 80$0^{\circ}C$. Ba-ferrite, heat-treated at 80$0^{\circ}C$ for 2 hr, had mean particle size of 1000$\AA$, lattice parameter of a0=5.889243 $\AA$ and c0=23.214502 $\AA$, a saturation magnetization ($\sigma$8) of 45.3 emu/g and a coercive force (Hc) of 5200Oe.