RF Magnetron Sputtering 방법으로 제조한 In<sub>2</sub>O<sub>3</sub> 박막의 미세구조와 전기적 특성
전용수,윤여춘,김성수,Jeon, Yong-Su,Yun, Yeo-Chun,Kim, Seong-Su 한국재료학회 2002 한국재료학회지 Vol.12 No.4
Microstructure and electrical properties of $In_2O_3$ transparent thin films are analyzed on the basis of Structure Zone Model (SZM) proposed by Thornton. Thin films are deposited on glass substrate by RF magnetron sputtering with variation of substrate temperature $(T_s)$ and argon gas pressure $(P_{Ar})$. Microstructure of Zone I of SZM is observed with lowering of substrate temperature or increasing of argon pressure. The higher electrical resistivity of those specimens is due to micro-pores or voids between columnar grains. At the conditions of $T_s=450^{\circ}C$ and $P_{Ar}$=4.2mTorr, the Zone II structure of SZM and the lowest electrical resistivity $(2.1{\times}10^{-2}{\Omega}cm)$ are observed. The dense structure of columnar grains with faceting on growing surface and preferred orientation of (100) plane are observed in those specimens.
전용수(Yong Su Jeon),이종민(Jong Min Lee),권오준(Oh-Jun Kwon) 한국정보보호학회 2005 情報保護學會誌 Vol.15 No.3
차세대 인터넷 주소체계로 IPv6의 표준화가 마무리단계에 이르러 이동성 지원을 위한 MIPv6(mobile ipv6)의 표준화도 RFC3775[1]로 마무리되었다. 하지만 IPv6를 기반으로 한 MIPv6의 보안 문제점은 완전하게 해결되지 않는 연구과제로 남아있는 상태이다. IPv6의 autoconfiguration 과정에서의 주소중복, DoS공격의 취약점은 IPv6를 기반으로 한 MIPv6에서도 적용되는 보안문제이다. 특히 모바일 단말기의 로밍 환경에서의 HA와 MN간의 보안인증 절차문제, 전원공급으로 인한 bootstrapping 관련 추가적인 보안문제가 있어 보안관련 연구단체에서 연구가 진행 중에 있다.
IPv6망에서의 IP 이동성 검증을 위한 테스트베드 구축
전용수(Yong Su Jeon),이종민(Jong Min Lee),권오준(Oh Jun Kwon) 동의대학교 정보통신연구소 2004 정보통신연구지 Vol.6-1 No.-
최근 들어 인터넷의 광범위한 사용과 더불어 이동성은 컴퓨터 사용자들의 컴퓨팅 환경 을 급격하게 변화시키고 있다 이러한 인터넷 사용 환경에서 통신을 하기 위해서는 IP 주소를 각 호스트나 단말에 지정해 주어야 하는데 현재의 IPv4 체계에서는 인터넷 사용에 필요할 IP 주소가 부족한 상황이다 이를 대처하기 위해서 128 비트 주소체계를 사용하는 IPv6 표준이 나오게 되었다 IPv4 체계에서와 마찬가지로 IPv6 체계에서도 IP 이동성 보장 을 위해 IETF 에서 MIPv6 의 표준화를 진행 중에 있다. 본 논문에서는 IPv6 망에서의 R 이 통성 검증 및 성능 평가를 위하여 MIPv6 테스트베드를 구축하고, 이동노드의 외부망 간 이동에 따른 네트워크 지연시간을 측정하여 네트워크 성능을 분석한다,
Indium Tin Oxide (ITO) 투광성 박막의 제조 및 전자파 차폐특성
김영식,전용수,김성수,Kim, Yeong-Sik,Jeon, Yong-Su,Kim, Seong-Su 한국재료학회 1999 한국재료학회지 Vol.9 No.11
투명차폐재를 목적으로 Indium Tin Oxide (ITO) 투광성 박막을 제조하고 전자파 차폐특성에 대해 조사하였다. 박막은 RF magnetron co-sputtering 증착장비를 사용하여 제작하였다. RF 인가전력, Ar 및 $O_2$분압, 기판온도를 변화시키며 전기전도도와 투광성을 겸비한 박막의 조성과 구조에 관한 실험을 진행하였다. 최적의 증착조건은 $300^{\circ}C$의 기판온도, 20sccm의 아르곤 유량, 10sccm의 산소유량, 그리고 In과 Sn의 인가전력이 각각 50W와 30W일 경우였으며, 이때 얻어진 박막은 육안으로 분명할 정도의 투광성을 보였고 5.6$\times10^4$mho/m의 높은 전기전도도를 나타내었다. 이렇게 제조된 ITO 박막의 전자파 차폐효과를 차폐이론에 의해 분석하였다. 박막의 전기전도도, 두께, skin depth로부터 차폐기구(흡수손실, 반사손실, 다중반사 보정항)에 대해 고찰하였다. 계산된 차폐효과는 26dB의 값을 보여 투광성 차폐재로 ITO 박막의 사용 가능성을 제시할 수 있었다. Indium Tin Oxide (ITO) films were fabricated by vacuum deposition technique and their microwave shielding properties were investigated for the application to the transparent shield material. The vacuum coating was conducted in a RF co-sputtering machine. The film composition and structure associated with the sputtering conditions (argon and oxygen pressure. substrate temperature. RF input power) were investigated for the attainment of high electrical conductivity and good transparency. The electrical conductivity of IT0 films fabricated under the optimum deposition conditions (substrate temperature : $300^{\circ}C$. Ar flow rate : 20 sccm, Oxygen flow rate : 10 sccm, In/Sn input power : 50/30 W) showed 5.6$\times10^4$mho/m. The optical transparency is also considerably good. The microwave shielding properties including the dominant shielding mechanism are investigated from the electrical conductivity, thickness and skin depth of the ITO films. The total shielding effectiveness is then estimated to be 26 dB, which provides a suggestion that the IT0 films can be effectively used as the transparent shield material.
고로슬래그를 사용한 무시멘트 알칼리 활성 모르타르의 유동성과 압축강도
고경택,류금성,이장화,강현진,전용수,Koh, Kyung-Taek,Ryu, Gum-Sung,Lee, Jang-Hwa,Kang, Hyun-Jin,Jeon, Yong-Su 한국건설순환자원학회 2011 한국건설순환자원학회지 Vol.6 No.1
포틀랜드 시멘트 제조 시 다량의 이산화탄소를 배출함으로써 많은 문제가 발생하고 있다. 그리고 화력발전소 및 제철소의 산업부산물인 플라이애쉬 및 고로슬래그는 시멘트와 일부 대체하여 콘크리트로 일부 재활용되고 있으나, 42% 정도를 해안 및 육상에 매립함으로써 환경적인 문제를 유발하고 있다. 최근 결합재로 시멘트를 사용하지 않은 알칼리 활성 콘크리트에 대한 연구가 활발히 진행되고 있다. 본 논문에서는 시멘트를 전혀 사용하지 않고 결합재로서 고로슬래그 미분말를 사용한 무시멘트 알칼리 활성 콘크리트를 개발할 목적으로 유동성과 압축강도 측면에서 알칼리 활성화제와 고성능 감수제에 대해 검토에 대해 검토하였다. 그 결과, 알칼리 활성화제의 종류 및 혼합비율, 고성능 감수제의 종류, 투입순서 등은 고로슬래그를 사용한 알칼리 활성 모르타르의 유동성과 압축강도에 큰 영향을 주는 것으로 나타났다. 고로슬래그 무시멘트 알칼리 활성 모르타르를 제조하는데, 9M NaOH과 분말형 쇼듐실리케이트를 1:1의 비율로 제조한 알칼리 활성화제를 사용하고, 고성능 감수제를 먼저 투입한 경우에는 1시간 동안 플로우 180 mm의 유동성과 $20^{\circ}C$의 상온양생조건에서 재령 28일에서 압축강도 50 MPa를 확보할 수 있는 것으로 나타났다. Portland cement production is under critical review due to high amount of $CO_2$ gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. In this study, we investigated the influence of alkali activator and superplasticizer on the flowability and compressive strength of the alkali-activated mortar in oder to develop cementless alkali-activated concrete using blast furnace slag. In view of the results, we found out that the type and mixture ratio of alkali activator, the type and adding order of superplasticizer results to be significant factors. When cementless alkali-activated mortar using blast furnace slag manufactured with 1:1 the mass ratio of 9M NaOH and sodium silicate, and added superplasticizer before alkali activator in the mixer, we can be secured workability with 180 mm of flow during 1 hours and compressive strength of about 50 MPa under $20^{\circ}C$ curing condition at age of 28days.