CREEP 에 의한 못 결합부의 강성도의 변화에 관한 연구
장상식 한국목재공학회 1989 목재공학 Vol.17 No.4
Nailed joints, which are commonly used in Wooden structures, transmit loads from one member to another and induce partial composite actions between members. Long-term loads induce creep slip in nailed joints and affect load sharing and partial composite action, which may reduce joint stiffness. Two theoretical viscous-viscoelastic models were developed far nailed joints to predict creep behavior under long-term variable loads. Those models were also used to predict stiffness changes under long-term variable loads. The stiffness of nailed joint is defined as a Secant modulus which is called the joint modules or slip modules. Input data for the models are the results of constant load tests under three different load levels. To verify the models, nailed joints were also tested under two long-term variable load functions. The predictions of the models were very close to the experimental data. Therefore, the theoretical viscous-viscoelastic models and procedures developed in this study can be applied to predict creep slip and the changes in joint moduli of nailed joints under long-term variable loads.
장상식 한국가구학회 2001 한국가구학회지 Vol.12 No.1
This study was carried out to evaluate the feasibility of using HDF as surface panels as well as core materials for flush door manufacturing. Several core compositions were developed and applied to manufacture door specimens. Core materials were tested under bending load, door manufacturing process was analysed to find better way of using HDF for door manufacturing, and door specimens were tested under bending, twisting and impact loads. From this study, it was concluded that HDF can be used to manufacture quality flush doors. And it was desirable to use light color HDF as surface panels because dark color HDF caused a problem in manufacturing process by shadow shown through finishing veneer. HDF doors were light, and showed good quality and higher resistance against bending twisting and impact loads.