http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
남영민,이해복 청주대학교 산업과학연구소 2005 産業科學硏究 Vol.22 No.3
The marine benthic algal flora of Jindo Island, south coast of Korea was investigated seasonally at three sites, Nari, Gahakri and Jeopdo during June, 2003 - May, 2004. As the results, a total of 89 species including 7 greens, 25 browns and 57 reds was identified. At three sites, 39 species at Nari, 49 species at Gahakri and 78 species at the most flourishing site Jeopdo were identified. Seasonally, 63 species in spring, 44 species in summer, 46 species in autumn, and 61 species in winter were identified. The floras tic characteristics calculated in (R+C)/P values were 2.56, which express a warm-water floras. The results of the cluster analysis based on the species compositions, of the three sites reveal that the floristic nature of two sites of Nari and Gahakri was different from that of Jeopdo.
HVOF와 LPPS로 제조된 단층 열차폐 코팅의 고온 물성에 관한 연구
남영민,송요승 한국 항공대학교 항공산업기술연구소 2000 航空宇宙産業技術硏究所 硏究誌 Vol.10 No.-
본 연구에서는 HVOF법과 LPPS법으로 제조된 CoNiCrAlY 단층 열차폐 코팅의 미세구조 분석, 고온산화시험, 그리고 열피로시험 등 종합적인 기계적, 열적 물성을 평가하였다. HVOF법과 LPPS법으로 제조된 피막의 두께는 각각 450∼500μm, 350∼450μm 정도였으며 경도는 각각 350Hv∼400Hv, 370Hv∼420Hv의 분포를 보였고 모재와 코팅층의 경계가 확실히 구분되지 않았다. 단면 관찰결과 두 피막 모두에서 열처리에 의한 확산의 영향으로 Al-rich 상이 나타났으며 코팅층 표면은 β상과 γ상으로 이루어져 있었다. 또한 기공도는 1∼2%정도를 나타내었으며 LPPS 시편에서 더 낮은 기공도를 유지하였다. 고온산화시험에서는 코팅층 표면에 10∼20μm 정도의 두께를 가진 oxide scale이 형성되었으며 산화하기 전에 보이는 Al-rich 상들이 점차적으로 사라지는 것이 발견되었다. 열피로시험 결과 표면과 계면부위에 커다란 기공이 형성되었으며 LPPS 시편이 HVOF 시편보다 더 나은 내열피로 특성을 나타내었다. In this study the evaluations of mechanical and thermal properties of FGM-TBC such as oxidation and fatigue at high temperatures have been conducted. The samples of bond coat produced by High Velocity Oxygen Fuel (HVOF) and Low Pressure Plasma Spray (LPPS) method were used. The thickness values of HVOF coating was about 450μm to 500μm and the hardness of coating was about 350Hv to 400Hv. The thickness values of LPPS coating was about 350μm to 450μm and the hardness number of coating was about 370Hv to 420Hv. The XRD analyzes showed that CoNiCrAlY coating layer of HVOF and LPPS was composed of β and γ phase after spraying. The cross sectional image showed Al-rich phase which was influenced by diffusion. After high temperature oxidation test of HVOF and LPPS, the oxide scale with about 10μm to 20μm thickness at coating surface was appeared and under the oxide scale layer the Al-depleted zone was observed. And, Al-rich phase which showed before oxidation test disappeared gradually. After thermal fatigue test of HVOF and LPPS, coarse pores were observed at the surface and interface area. The thermal fatigue resistance of LPPS coating is better than those of HVOF coating.
세라믹/금속 혼합비가 11층 열장벽 피막의 고온특성에 미치는 영향
남영민,송요승 한국항공대학교 2000 論文集 Vol.38 No.-
APS법을 이용하여 Inconel모재 위에 YSZ/NiCrAlY를 다층으로 용사한 열장벽 피막의 종합적인 기계적, 열적 고온물성을 비교 ·평가하였다. 이렇게 얻어진 결과를 바탕으로 가장 우수한 고온물성치를 지닌 열장벽 피막을 Inconel모재 위에 YSZ/NiCrAlY의 혼합비를 선형적, 비선형적으로 11층으로 용사하여 종합적인 기계적, 열적 고온물성을 평가하였다. 용사된 피막의 두께는 500∼600㎛ 범위였고, 기공도는 9∼14%내외였다. Inconel 모재 위에 선형적으로 적층한 피막이 열피로에 가장 우수한 저항성을 보였다. 고온산화시험과 열충격시험에서도 선형적으로 적층한 피막이 비선형적으로 적층한 피막보다 더 우수하였다. 접착강도는 concave형이 614kgf/cm2로 가장 컸으며 파단이 가장 많이 일어난 층은 90(YSZ) : 10(NiCrAlY)층이었다. 이상의 결과를 종합한 결과 Inconel모재 위에 선형적으로 적층한 TBC가 가장 우수한 고온 물성을 보유한 것으로 사료된다. The purpose of this study is to evaluate functional gradient thermal barrier coatings. The malt-layered TBC on Inconel substrate specimens were prepared by APS method. The evaluations of mechanical and thermal properties have been conducted. 11 layered TBC specimens were prepared by APS method in which the mixture ratio of YSZ/NiCrAlY is linear and non-linear. The range of thickness of coated layers was 500 ∼ 600㎛. The average porosity of coatings was 9.4%. The linear-type specimens showed best resistance for thermal fatigue. In the high temperature oxidation test and the thermal shock test, the linear types were better than the non-linear types. The bond strength of the concave type was greater than that of linear types and convex type coatings. The fracture of the coating layers was occurred in the 10th layer (90(Ceramic) : 10 (NiCrAlY)). According to the results of this research, TBC of 11 layer coatings of the linear type on Inconel substrate was the optimum coating.