무가압분말 충전성형법에 의한 다공성 세라믹스의 제조 및 특성 : II. 뮬라이트 & 코디어라이트
박정현,황명익,김동희,최환욱,김용남 한국세라믹학회 1999 한국세라믹학회지 Vol.36 No.6
Porous ceramics were fabricated from pressureless powder packing forming method using mullite and cordierite powders granulate by spray drying. The bending strength and shrinkage of porous ceramics were increased and their porosity were decreased with increasing temperature. It showed homogeneous distribution of 2$\mu\textrm{m}$ intergranular pores of mullite at 1400$^{\circ}C$, 2.5$\mu\textrm{m}$ intergranular pores of cordierite at 1300$^{\circ}C$ respedtively. Above that temperature intragranular particles were sintered and sintering by intergranular necking was extremely proceeded. In the test of thermal shock resistance sudden decrease of bending strength to $\Delta$T was not shown because intergranular large pore prevented sudden crack propagation.
Al-AlN계 질화반응에 대한 표면개질 및 첨가제의 영향
유재영,김용남,황명익,박정현 한국세라믹학회 2003 한국세라믹학회지 Vol.40 No.3
AI, AIN 및 질화반응 촉진을 위한 첨가제로서 Li$_2$CO$_3$, Y$_2$O$_3$, CaCO$_3$를 혼합한 후 성형체를 제조하여 질소 분위기에서 열처리하였고, 용매 및 첨가제의 종류와 질화온도가 AI-AIN계의 질화반응에 미치는 영향에 대하여 고찰하였다. 1.0wt%의 olcic acid.를 첨가한 ethanol을 혼합용매로 사용한 경우 AI과 AIN 입자의 표면개질 효과를 질화반응시 산화물 생성을 최소화시킬 수 있었다. 그리고 AI-AIN계에 Li$_2$CO$_3$ 또는 CaCO$_3$를 첨가한 경우Y$_2$O$_3$를 첨가한 경우에 비하여 질화 열처리시 생성되는 산화물의 생성을 크게 억제시킬 수 있었다. AI, AIN and additives such as Li$_2$CO$_3$, Y$_2$O$_3$ and CaCO$_3$ which promoted nitridation were mixed, formed and heat-treated in nitrogen atmosphere. The effect of solvent, additive and temperature on nitridation of AI-AIN system was studied. When ethanol containing 1 wt% oleic acid was used as a mixing solvent, the formation of oxide was minimized due to surface modification of AI and AIN particles. The addition of Li$_2$CO$_3$ or CaCO$_3$ as an additive extremely diminished the formation of oxide which formed during heat treatment for nitridation compared with the addition of Y$_2$O$_3$.
레이저 도핑된 선택적 에미터 태양전지의 도금 및 열처리 공정의 영향
이준성(Lee, Junsung),경도현(Kyeong, Dohyeon),황명익(Hwang, Myungick),오훈(Oh, Hun),이원재(Lee, Wonjae),조은철(Cho, Eunchul) 한국신재생에너지학회 2010 한국신재생에너지학회 학술대회논문집 Vol.2010 No.11
고효율 실리콘 태양전지 개발은 단파장의 광 응답 특성 개선을 위한 선택적 에미터 형성과 반사 손실 개선을 위한 미세 패턴 전극을 형성하는데 집중적인 연구가 진행되고 있다. 본 실험에서는 레이저 도핑된 선택적 에미터 위에 미세 패턴 Ni/Cu 도금 전극을 형성하였다. 니켈과 동 도금은 무전해 Light induced plating(LIP)으로 진행하였다. 니켈 도금 전극의 접착력 개선과 접촉저항 개선을 위해서 니켈 전극을 질소 분위기에서 열처리하여 니켈실리사이드(NiSi)를 형성하였다. 니켈 도금 두께와 니켈실리사이드 열처리 조건을 최적화하여 충실도 77.4%, 변환효율 18.5%를 달성하였다.