Sn-3.5Ag 땝납의 Zn첨가가 기계적 특성에 미치는 영향
이도재 ( Lee Do Jae ),이광민 ( Lee Gwang Min ),이경구 ( Lee Gyeong Gu ),오태욱 ( O Tae Ug ),백대화 ( Baeg Dae Hwa ) 한국주조공학회 2003 한국주조공학회지 Vol.23 No.6
N/A Effects of Zn concentration on the mechanical properties of Sn-3.5Ag solder were studied, and compared to those of Sn-40Pb alloy which is widely used currently in electronics industry. Aging treatments were performed at 100 and 150 for up to 120days and then were examined changes of microstructure by optical microscopy, SEM and EDS. Sn-3.5Ag solder was loaded to failure at cross head speed of 0.3 mm. min-1 to measure strength and elongation. Aging treatment changed more or less the tensile properties of the solder itself. In short, Sn-Ag base alloy showed decrease in tensile strength and increase in elongation with prolonged agig time. Sn-3.5Ag alloy showed more sensitive changes in tensile properties than Sn-3.5Ag-1Zn alloy by aging. On the other hand, Sn-40Pb alloy showed decreasing tendances in both tensile strength and elongation by aging.
원료분말과 금속간화합물 분말로 기계적 합금화한 $Al_3$(${Nb_{1-x}}{Zn_x}$) 합금의 미세구조특성
이광민,이지성,안인섭,Lee, Gwang-Min,Lee, Ji-Seong,An, In-Seop 한국재료학회 2001 한국재료학회지 Vol.11 No.5
본 연구에서는 MA 방법을 사용하여 $Al_3$Nb 금속간화합물의 조성에 Zr을 첨가하여 $Al_3$(Nb$_{1-x}$ )Zr$_{x}$ 합금분말을 제조한 후 이에 따른 상변화 거동 및 미세구조특성을 분석하였다. MA는Al$_3$(Nb$_{1-x}$ )Zr$_{x}$의 조성으로 Al, Nb, Zr 원료분말과 arc meltinly된 $Al_3$Nb, $Al_3$Zr 금속간화합물 분말을 사용하여 300rpm의 회전속도로 20시간 동안 MA하였다. 이때의 정상상태의 원료분말은 약 4$\mu\textrm{m}$의 평균입도와 약 12~18nm의 결정립크기를 가졌으며, arc melting된 분말은 약 2$\mu\textrm{m}$의 평균입도와 약 14nm의 결정립크기를 가지는 분말을 얻을 수 있었다 원료분말과 금속간화합물 분말의 MA 기구는 상이한 거동을 나타내었으며, 분말의 내부변형량은 원료분말이 금속간화합 분말보다 내부변형량이 더 많이 축적되었다. 이는 원료분말의 MA 경우 냉간 압접과 파괴가 반복적으로 진행되었지만 금속간화합물 분말은 취약한 화합물상이어서 냉간압접 보다는 파괴가 지배적으로 진행되었기 때문이다. 원료분말을 MA하였을 경우에는 Al (Nb.Zr)$_2$상이 형성되었으나 금속간화합물 분말로 MA하였을 경우에는 3원계 화합물상이나 비정질상으로 상변태 되지 않고 단지 두 합금상이 분쇄되어 나노복합화 되었다. 후속 열처리에 의해 원료분말인 경우에는 $Al_3$(Nb.Zr)의 화합물상이 쉽게 형성되었으나, 금속간화합물 분말의 경우에는 새로운 상 생성은 얼었고 단지 열처리 전의 분말내부에 쌓여있던 내부변형에너지가 약 60% 정도 감소하였다. The present study was carried out to investigate the effect of zirconium addition to $Al_3$Nb intermetallic on the crystal structural modification and microstructural characterization of $Al_3$Nb intermetallic. Elemental Al, Nb, Zr powders and arc melted $Al_3$Nb and $Al_3$Zr intermetallic mixed powders were used as starting materials. MA was carried out in an attritor rotated with 300 rpm for 20 hours. The behavior of MA between two starting materials was some-what different in which the value of internal strain of the elemental powders was higher than that of the intermetallic powder. The intermetallic powder was much more disintegrated during the MA processing. In the case of the elemental powders, AlNb$_2$ phase were transformed to Al(Nb.Zr)$_2$ as a result of ternary addition of Zr element. With the successive heat treatment at 873K for 2 hours, the Al(Nb.Zr)$_2$ phase was transformed to more stable $Al_3$(Nb.Zr) phase. This transformation was clearly confirmed by the identification of X-ray peak position shift. On the other hand, in the carte of the intermetallic powder, there was no evidence of phase transformation to other ternary intermetallic compounds or amorphous phases, even in the case of additional heat treatment. However, nano-sized intermetallic with $Al_3$Nb and $Al_3$Zr were just well distributed instead of phase transformation.
CuO 첨가된 저온소결 (Na,K,Li)(Nb,Sb,Ta)O<sub>3</sub>계 세라믹스의 압전 및 유전 특성
이광민,류주현,이지영,Lee, Gwang-Min,Yoo, Ju-Hyun,Lee, Jie-Young 한국전기전자재료학회 2015 전기전자재료학회논문지 Vol.28 No.4
In this paper, in order to develop outstanding Pb-free piezoelectric composition ceramics, the $(Na_{0.525}K_{0.443}Li_{0.037})(Nb_{0.883}Sb_{0.08}Ta_{0.037})O_3+0.3wt%Bi_2O_3+0.4wt%Fe_2O_3+xwt%CuO$ (x= 0~0.8 wt%)(abbreviated as NKL-NST) lead-free piezoelectric ceramics have been synthesized using the ordinary solid state reaction method. The effects of CuO-doping on the structure and electrical properties of the NKL-NST ceramics were systematically studied. The results show that the ceramics exhibit a pure perovskite structure with orthorhombic phase at room temperature, and secondary phase was found in the ceramics. The 0.4 wt%CuO added ceramics sintered at $950^{\circ}C$ showed the optimum properties of piezoelectric constant($d_{33}$), planar piezoelectric coupling coefficient(kp) and mechanical quality factor(Qm) : $d_{33}=213$[pC/N], kp= 0.43, Qm= 423,respectively.
Fe<sub>2</sub>O<sub>3</sub>첨가에 따른 (Na,K,Li)(Nb,Sb,Ta)O<sub>3</sub>계 세라믹스의 압전 및 유전 특성
이광민,신상훈,류주현,Lee, Gwang-Min,Shin, Sang-Hoon,Yoo, Ju-Hyun 한국전기전자재료학회 2014 전기전자재료학회논문지 Vol.27 No.9
In this paper, in order to develop outstanding Pb-free composition ceramics, the $Fe_2O_3$-doped ($Na_{0.525}K_{0.443}Li_{0.037}$)($Nb_{0.883}Sb_{0.08}Ta_{0.037}$)$O_3$ + 0.3 wt% $Bi_2O_3$ + x wt% $Fe_2O_3$ (x= 0~1.0 wt%)(abbreviated as NKL-NST) lead-free piezoelectric ceramics have been synthesized using the ordinary solid state reaction method. The effect of $Fe_2O_3$-doping on their microstructure and electrical properties were investigated. XRD diffraction pattern studies confirm that $Fe_2O_3$ completely diffused into the NKL-NST lattice to form a new stable soild solution with $Fe^{3+}$ entering the $Nb^{5+}$, $Sb^{5+}$ and $Ta^{5+}$ of B-site. And, phase structure of all the ceramics exhibited pure perovskite phase and no secondary phase was found in the ceramics. The ceramics doped with 0.6 wt% $Fe_2O_3$ have the optimum values of piezoelectric constant($d_{33}$), planar piezoelectric coupling coefficient($k_p$) and mechanical quality factor($Q_m$) : $d_{33}$ = 233 [pC/N], $k_p$= 0.44, $Q_m$= 95. These results indicate that the ($Na_{0.525}K_{0.443}Li_{0.037}$)($Nb_{0.883}Sb_{0.08}Ta_{0.037}$)$O_3$ +0.3 wt% $Bi_2O_3$ + 0.6 wt% $Fe_2O_3$ ceramic is a promising candidate for lead-free piezoelectric ceramics.
기계적 합금화법으로 제조된 Al-(6~3wt.%)Cr-(3~6wt.%)Zr 합금의 열적 안정성
양상선,이광민,Yang, Sang-Seon,Lee, Gwang-Min 한국재료학회 2000 한국재료학회지 Vol.10 No.6
본 연구에서는 고온용 고강도 Al 합금을 제조하기 위해 Al-Cr-Zr 복합금속분말을 attritor에서 300rpm의 회전속도로 20시간 동안 기계적 합금화방법으로 제조한 후 진공 고온 압축성형하였다. Al-Cr-Zr 합금의 미세구조 및 조직관찰은 XRD, TEM 등을 사용하여 분석하였고, 열적 안정성은 열적 노출시간에 따른 미소경도측정을 통하여 조사하였다. 진공 열간 압축성형 되었을 때 MA Al-Cr-Zr 합금의 이론 밀도의 97%에 이르는 조밀화르 f보였으며, $300^{\circ}C$에서 100시간 열처리 한 경우에는 경도변화가 거의 없었고, $500^{\circ}C$에서 100시간 열처리한 경우에도 감소가 6% 이내로 우수한 열적 안정성을 나타내었다. 이와 같은 MA Al-Cr-Zr 합금의 우수한 열적 안정성은 기계적 합금화에 의해 Al 기지 내에 미세하고 균일하게 분산된 Cr과 Zr이 고온 성형과 열처리 과정에 의해 $Al_3Zr,\;Al_{13}Cr_2$의 금속간 화합물들의 형성되었으며, 열처리 후의 이 합금의 최종 결정립 크기는 150mm 크기 이하이었다. The Al-Cr-Zr composite metal powders were prepared by mechanical alloying and consolidated by vacuum hot pressing. The microstructural characteristics and the thermal stability of the MA Al-Cr-Zr alloys were evaluated by means of microhardness measurement, XRD and TEM in order to develop high temperature, high strength aluminum alloys. The mechanical alloying was conducted in attritor with 300rpm for 20 hours. The density of the vacuum hot pressed Al-Cr-Zr alloy reached at 97% of theoretical one. After exposing at $300^{\circ}C$ for 100 hours, there is almost no variation in hardness change of the MA alloys. Even after exposing at $ 500^{\circ}C$ for 100 hours, the hardness of the alloy was decreased within 6% of the initial value. The fine stable $Al_3Zr\;and\; Al_{13}Cr_2$ intermetallics were formed at the stage of consolidation and heat treatment in aluminum matrix. The good thermal stability of the MA Al-Cr-Zr alloy can ab attributed to the role of the dispersoids, inhibiting grain growth of nanocrystalline, and the final grain size after heat treatment was less than 150nm.
Ti-Nb계 합금의 미세조직 및 경도변화에 미치는 열처리 조건의 영향
이도재 ( Lee Do Jae ),이경구 ( Lee Gyeong Gu ),이광민 ( Lee Gwang Min ),황주영 ( Hwang Ju Yeong ) 한국주조공학회 2003 한국주조공학회지 Vol.23 No.4
N/A Ti-3wt.%Nb(αtype), Ti-20wt.%Nb(α+β,type) and Ti-40wt.%Nb(βtype) alloys were melted by vacuum are remelting. The specimens were homogenized at 1050℃ for 24 hr and were then hot rolled to 50% reduction. Each alloys were solution heat treated at β zone and α+β, zone after homogenization, and then aged. The microstructural and hardness changes in Ti-Nb alloys with Nb contents were investigated by SEM, XRD and hardness tester. The microstructural change from equiaxied to acicular and the increase of β phase in Ti-Nb alloys were obtained when the Nb content increased. The higher hardness value of α+βtype alloy was obtained compared to the other alloys.
신상훈,류주현,이광민,신동찬,Shin, Sang-Hoon,Yoo, Ju-Hyun,Lee, Gwang-Min,Shin, Dong-Chan 한국전기전자재료학회 2015 전기전자재료학회논문지 Vol.28 No.7
In this study, in order to develop the capacitor composition ceramics with the good dielectric properties, $(Ba_{0.86}Ca_{0.14})(Ti_{0.85}Zr_{0.12}Sn_{0.03})O_3+xCuO$ (x= 0.006~0.010) ceramics were prepared by the conventional solid-state reaction method. The effects of CuO addition on the microstructure and dielectric properties was investigated. All specimens indicated rhombohedral phase without any secondary phase. As CuO addition increased, the variation width of TCC was increased at more than $40^{\circ}C$. Also, the specimen with x=0.007 sintered at $1,250^{\circ}C$ showed the high dielectric constant of 9,632 in spite of low temperature sintering temperature.