OLED 레이저 실링용 글라스 프릿에서 V<sub>2</sub>O<sub>5</sub> 함량 및 가소성 분위기가 접합 특성에 미치는 영향
정현진,이미재,이영진,김진호,전대우,황종희,이정수,양윤성,육수경,박태호,문윤곤,Jeong, HyeonJin,Lee, Mijai,Lee, Youngjin,Kim, Jin-Ho,Jeon, Dae-Woo,Hwang, Jonghee,Lee, Jungsoo,Yang, Yunsung,Youk, Sookyung,Park, Tae-Ho,Moon, Yun-Gon 한국전기전자재료학회 2016 전기전자재료학회논문지 Vol.29 No.8
In this study, the effect of vanadium oxide ($V_2O_5$) content and pre-sintering atmosphere on sealing property of glass frit that consisted of $V_2O_5-BaO-ZnO-P_2O_5-TeO_2-CuO-Fe_2O_3-SeO_2$ was investigated by XPS (X-ray photoelectron spectroscopy). The content of V2O5 was changed to 15, 30, and 45 mol%, and the pre-sintering was carried out in air and $N_2$ condition, respectively. XPS analysis conducted before and after laser irradiation with identical sample. Before laser treatment, glass frits that were pre-sintered at air condition showed both $V^{4+}$ and $V^{5+}$, but the valence state was changed to $V^{5+}$ after laser irradiation when the glass frits contained 30 and 45 mol% $V_2O_5$; this change led to non-adhesive property. On the other hand, glass frits that were pre-sintered at $N_2$ condition exhibited only $V^{4+}$ and it showed fine adhesion irrespective of the $V_2O_5$ content. As a result, the existence of $V^{4+}$ seems to be a major factor for controlling the adhesive property of glass frit for laser sealing.
OLED 레이저 실링용 글라스 프릿에서 V2O5 함량 및 가소성 분위기가 접합 특성에 미치는 영향
황종희,정현진,이미재,이영진,김진호,전대우,이정수,양윤성,육수경,박태호,문윤곤 한국전기전자재료학회 2016 전기전자재료학회논문지 Vol.29 No.8
In this study, the effect of vanadium oxide (V2O5) content and pre-sintering atmosphere on sealingproperty of glass frit that consisted of V2O5-BaO-ZnO-P2O5-TeO2-CuO-Fe2O3-SeO2 was investigated by XPS (X-rayphotoelectron spectroscopy). The content of V2O5 was changed to 15, 30, and 45 mol%, and the pre-sintering wascarried out in air and N2 condition, respectively. XPS analysis conducted before and after laser irradiation withidentical sample. Before laser treatment, glass frits that were pre-sintered at air condition showed both V4+and V5+,but the valence state was changed to V5+ after laser irradiation when the glass frits contained 30 and 45 mol%V2O5; this change led to non-adhesive property. On the other hand, glass frits that were pre-sintered at N2condition exhibited only V4+ and it showed fine adhesion irrespective of the V2O5 content. As a result, theexistence of V4+ seems to be a major factor for controlling the adhesive property of glass frit for laser sealing. 본 연구에서는 XPS 분석법을 이용하여 V2O5-BaO-ZnO-P2O5-TeO2-CuO-Fe2O3-SeO2 조성의 레이저 실링용 글라스 프릿에서 V2O5 함량 및 가소성 분위기가 접합 특성에 미치는 영향에 대해 고찰하였다. 글라스 프릿의 주성분인 V2O5 함량은 15, 30, 45 mol%으로 변화 시켰으며, 각각 대기 및 질소 분위기에서 가소성하였다. 레이저 조사 전, 대기 분위기에서 가소성한 모든 글라스 프릿 내 V은 V4+와 V5+ 상태로 모두 존재하지만, 레이저 조사 후에는 글라스 프릿의 V2O5 함량에 따라 V4+ 또는 V5+만 존재하였다. 특히, 레이저 조사 후, 유리 내 V5+만 존재할 경우에는 접합이 되지 않았다. 반면, 질소 분위기에서 가소성한 모든 글라스 프릿에는 V4+만 존재하는 것을 확인하였으며, 레이저 조사 후에도 V4+만 존재하였고 모두 접합이 잘 되었다. 따라서, 레이저 조사 후 글라스 프릿 내 V4+의 존재가 레이저 실링용 글라스 프릿의 접합 특성을 결정하는 주요한 요소로 작용하는 것으로 판단된다.