정전 분무 공정으로 제조된 Fe-Cr-Al 분말 다공체 금속의 고온 산화 특성에 미치는 기공 크기의 영향
오재성,공영민,김병기,이기안,Oh, Jae-Sung,Kong, Young-Min,Kim, Byoung-Kee,Lee, Kee-Ahn 한국분말야금학회 2014 한국분말재료학회지 (KPMI) Vol.21 No.1
Fe-Cr-Al powder porous metal was manufactured by using new electro-spray process. First, ultra-fine fecralloy powders were produced by using the submerged electric wire explosion process. Evenly distributed colloid (0.05~0.5% powders) was dispersed on Polyurethane foam through the electro-spray process. And then degreasing and sintering processes were conduced. In order to examine the effect of cell size ($200{\mu}m$, $450{\mu}m$, $500{\mu}m$) in process, pre-samples were sintered for two hours at temperature of $1450^{\circ}C$, in $H_2$ atmospheres. A 24-hour thermo gravimetric analysis test was conducted at $1000^{\circ}C$ in a 79% $N_2$ + 21% $O_2$ to investigate the high temperature oxidation behavior of powder porous metal. The results of the high temperature oxidation tests showed that oxidation resistance increased with increasing cell size. In the $200{\mu}m$ porous metal with a thinner strut and larger specific surface area, the depletion of the stabilizing elements such as Al and Cr occurred more quickly during the high-temperature oxidation compared with the 450, $500{\mu}m$ porous metals.
공기충전기의 필터 수명 연장을 위한 냉매형 수분제거기에 관한 연구
오재성(Jaesung Oh),김유경(Yukyung Kim),홍승태(Seung-Tae Hong),임우섭(Woo-Sub Lim),정재한(Jae-Han Jung),성시민(Si-Min Sung),지대준(Dea-Jun Ji),박태율(Tae-Yul Park) 대한기계학회 2021 대한기계학회 춘추학술대회 Vol.2021 No.11
An air charger is a device used to fill a respirator container with breathable air at high pressure. It is equipped with an air purification filter to remove harmful components generated during air charging. Among the main components of the filter, the desiccant determines the replacement cycle of the air purification filter. In this study, we are going to develop a refrigerant type moisture eliminator that can remove moisture by using refrigerant gas. We aim to extend the use time of the filter to about 70 hr. The experimental results showed that when the temperature of the injected air is 15 ℃, the moisture eliminator is installed at 2.8 mg/㎥. When the temperature of the injected air was 45 ℃, it is 7.6 mg/㎥. Through this, the moisture level removed by passing through the devices is about 1.5 times more moisture than the state without the eliminator.
정재한(Jae-Han Jung),박승근(Seung-Geun Park),임우섭(Woo-Sub Lim),오재성(Jae-Sung Oh) 한국화재소방학회 2020 한국화재소방학회논문지 Vol.34 No.6
본 연구는 기존 포소화약제(알코올포)와 테스트포를 실험을 통해 성능을 비교·분석하였다. 약제를 1%, 3% 혼합비율로 방출시키기 위하여 라인 프로포셔너 방식을 사용하였다. 프로포셔너의 입/출구 둘레는 40 A이며 폼 조절기를1%, 3%로 각각 사용하였다. 기본 변수인 유량, 압력, 측정시간은 200 LPM, 350 kPa, 60 s로 유지하였으며, 물, 알코올포, 테스트포 순으로 혼합 비율의 변화를 중점적으로 분석하였다. 실험 데이터 처리 방법은 「포소화약제혼합장치 등의 성능인증 및 제품검사 시험세칙」 규정에 따라 진행하였다. 실험 결과는 테스트포 1% 혼합 실험의 경우, 평균 방출 혼합 비율이 1.19%로 1% 포소화약제 혼합 비율 기준인 1~1.3% 범위 내에 있으므로 성능 인증되었다. 테스트포3% 혼합 실험의 경우, 평균 방출 혼합 비율은 3.05%로 3% 포소화약제 혼합 비율 기준인 3~3.9% 범위 내에 있으므로성능 인증되었다. In this study, the performance of foam agents and test foam is compared and analyzed through experiments. The lineproportioner method is used to release the foam agents at a mixing ratio of 1% and 3%. The inlet/outlet circumference ofthe proportioner is 40 A, and foam regulators are used at 1% and 3%, respectively. The basic variables such as flow rate,pressure, and measurement time are maintained at 200 LPM, 350 kPa, and 60 s, and the change in the mixing ratio isanalyzed in the order of water, alcohol foam, and test foam. The experimental data processing method is carried out inaccordance with the regulations of Korea Fire Institute (KFI). In the case of the test foam 1% mixing experiment, theperformance is certified because the average emission mixing ratio is 1.19%, which is within the range of 1~1.3%. In thecase of the test foam 3% mixing experiment, the average emission mixing ratio is 3.05%, which is within the range of3~3.9%.
공기충전기의 필터 수명 연장을 위한 냉각형 수분제거기에 관한 연구
정재한(Jae-Han Jung),성시민(Si-Min Sung),양정모(Jung-Mo Yang),박태율(Tae-yul Park),지대준(Dae-Jun Ji),임우섭(Woo-Sub Lim),오재성(Jaesung Oh) 한국화재소방학회 2022 한국화재소방학회논문지 Vol.36 No.6
공기충전기의 정화필터 수명은 기온 20∼25 ℃, 습도 30∼40% Rh 조건에서는 50 h의 유효 수명을 가지고 있다. 그러나 기온 30∼40 ℃, 습도 60∼90% Rh 조건에서는 유효 수명이 20∼30% 이상 감소한다. 습도 증가에 따른 필터 의 수명 감소는 필터 교체 주기 빈도를 확대시켜 경제적, 환경적 문제까지 야기한다. 따라서 본 연구에서는 환경적 영향을 최소화시킬 수 있는 냉각형 수분제거기에 관하여 연구를 수행하여 필터 수명을 150 h까지 연장하고자 한다. 본 연구에서는 최종 필터 직전에 냉각형 수분제거기를 제작 및 설치하였다. 최적의 냉각시스템을 개발하기 위하여 기초 실험을 실시하였고, 열전달 문제점을 파악하였다. 이를 개선한 수분제거기를 연구 개발하여 수분 한계수치(25 mg/m3) 도달 시간 및 필터 수명을 측정하였으며, 최종적으로 한국소방산업기술원(KFI)에 공기질 의뢰분석을 통해 성능을 확인하였다. 자체 실험을 진행하여 84 h까지 필터 수명이 연장되었다. 최종적으로 150 h까지 가동시킨 공기충전기의 공기질을 분석하였으며, 분석한 모든 수치가 성능 기준 범위 내에 있는 것으로 확인되었다. The life of the purification filter of an air charger is reduced by more than 20-30% under the conditions of 30-40 ℃ temperature and 60-90% Rh. Therefore, this study intends to extend the filter life to 150 h by conducting a study on a cooling type water eliminator that can minimize the environmental impact. In this study, a cooling type water eliminator is manufactured before the final filter. The moisture eliminator is developed to measure the time to reach the moisture level (25 mg/m3) and filter life. Finally, the performance is confirmed through air quality request analysis from the Korea Fire Institute (KFI). The filter life is extended up to 84 h by conducting a self-experiment. Finally, the air quality operated up to 150 h is analyzed. All the analyzed values are confirmed to be within the performance standard range.