This study aims to present the characteristics of marine physics, water quality, and sediment quality around offshore wind farm near the Gochang and Buan sea areas through the analysis of monitoring data. The relationships between suspended solid and wave height as well as suspended solid and flow velocity were analyzed. We found that Correlation Coefficient values of 0.61~0.69 between wave height and suspended solid, and suspended solid concentration reaches 75 mg/L or higher when wave height of more than 1m occurred in the spring (1 month). The water quality index (WQI) was used to identify the status of the water quality in the study area. Most of the measured points were rated first grade (very good). The variation of chlorophyll-a was relatively hight compared to the other criteria, indicating that it is a major factor affecting the quality index. In the sediment column, all heavy metals were detected below the Threshold Effects Level(TEL), and ignition loss and grain size show a positive correlation. 서남해 해상풍력 실증단지 해역을 중심으로 구축된 모니터링 자료를 분석하여 해양물리, 해양수질, 해저퇴적물의 환경 특성을 파악하고 현황을 제시하였다. 파고와 부유사 농도, 유속과 부유사 농도의 상관관계를 분석하여 연구 해역 토사의 부유 특성을 고찰하였다. 춘계 시(1 개월) 파고와 부유사 농도 사이에는 상관계수 0.61~0.69의 상관성을 보였으며, 1 m 이상의 높은 파고가 발생하면 75 mg/L 이상의 부유사 농도가 관측되었다. 수질평가지수 산정 시 필요한 항목을 중심으로 수질 현황을 분석하였으며 대부분의 정점에서 1등급(매우 좋음)을 보이고 있었다. 클로로필-a의 변동폭이 다른 항목에 비해 상대적으로 높게 나타나 수질평가지수에 영향을 주는 중요 인자로 파악되었다. 해저퇴적물 내 중금속 현황은 모든 항목의 평균값이 해양환경 주의기준 이하로 검출되었으며 강열감량과 입도분포는 높은 연관성을 보였다.
기공구조로 제조된 Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub> 음극활물질의 전기화학적 특성
서진성,나병기,Seo, Jin-Seong,Na, Byung-Ki 한국화학공학회 2019 Korean Chemical Engineering Research(HWAHAK KONGHA Vol.57 No.6
차세대 리튬이차전지용 음극활물질로 각광을 받고있는 $Li_4Ti_5O_{12}$는 높은 수명특성, 낮은 비가역용량 그리고 충방전시 부피팽창이 거의 없는 물질이다. 하지만 낮은 전기전도도로 인하여 높은 전류밀도에서는 용량특성이 현저하게 낮아지는 단점을 가지고 있다. 이 문제점을 해결하기 위해 P123을 첨가한 졸-겔법으로 기공구조의 $Li_4Ti_5O_{12}$를 합성하였다. 제조된 샘플들의 물리적 특성을 분석하기 위해 XRD, SEM, BET를 사용하였고, 전기화학적 특성은 사이클테스트, cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS)로 분석을 하였다. P123/Ti = 0.01mol의 비율로 만들어진 $Li_4Ti_5O_{12}$에서 가장 균일한 입자사이즈, 높은 비표면적, 그리고 상대적으로 높은 기공의 분포를 보였다. EIS분석 결과 기공구조의 $Li_4Ti_5O_{12}$의 경우 저항을 나타내는 반원의 크기가 현저하게 감소하였으며, 전극 내 저항값이 줄어들었음을 알 수 있었다. 율속 테스트결과 0.2C에서 178 mAh/g, 0.5C에서 170 mAh/g, 5C에서 110 mAh/g 그리고 10C에서 90 mAh/g의 용량을 유지하였고 용량회복율 또한 99%로 매우 우수하였다. $Li_4Ti_5O_{12}$ is a promising next-generation anode material for lithium-ion batteries due to excellent cycle life, low irreversible capacity, and little volume expansion during charge-discharge process. However, it has poor charge capacity at high current density due to its low electrical conductivity. To improve this weakness, porous $Li_4Ti_5O_{12}$ was synthesized by sol-gel method with P123 as chelating agent. The physical characteristics of as-prepared sample was investigated by XRD, SEM, and BET analysis, and electrochemical properties were characterized by cycle performance test, cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS). $Li_4Ti_5O_{12}$ synthesized by 0.01mol ratio of P123/Ti showed most unified particle size, high specific surface area, and relatively high porosity. EIS analysis showed that depressed semicircle size was remarkably reduced, which suggested resistance value in electrode was decreased. Capacity in rate performance showed 178 mAh/g at 0.2C, 170 mAh/g at 0.5C, 110 mA/h at 5C, and 90 mAh/g at 10C. Capacity retention also showed 99% after rate performance.
습식 분급으로 입도 조절된 서브 마이크론 크기의 Si 음극활물질의 전기화학적 특성 분석
서진성,김현수,나병기 한국화학공학회 2023 Korean Chemical Engineering Research(HWAHAK KONGHA Vol.61 No.1
In this study, the particle size of Si polycrystals was controlled through wet-sedimentation method, and changes in the capacity and cyclic characteristics of the Si anode material according to the particle size were observed. After wet-sedimentation of Si particles pulverized by a vibration mill, the non-uniform particle distribution of Si was uniformly controlled. The d50 of a sample in which Si was sedimented for 24 hours decreased to 0.50 μm. As a result of the electrochemical characteristic analysis, the Rct value representing the resistance in the electrode was significantly reduced due to the decrease in particle size. The unclassified Si sample exhibited a discharge capacity of 2,869 mAh/g in the first cycle, and decreased to 85.7 mAh/g after 100 cycles. The sample in which Si was classified for 24 hours showed a capacity of 3,394 mAh/g initially, and maintained a capacity of 1,726 mAh/g after 100 cycles. As the size of the Si particles decreased, the discharge capacity increased and the cycle life was also increased.
Chemical Agent를 이용한 추가 활성화 처리가 돼지 단위발생란의 발달에 미치는 영향
서진성,황인선,김세웅,박효숙,김동훈,양병철,공일근,양보석,임기순 한국동물생명공학회(구 한국동물번식학회) 2006 Reproductive & developmental biology Vol.30 No.1
핵이식 방법을 이용하여 성공적인 복제를 이루기 위해서 인위적인 활성화 처리는 필수적인 요소이다. 본 연구는 전기자극에 의해 활성화된 난자를 chemical agent를 이용하여 추가적인 활성화 처리를 하였을 때 돼지 단위발생란의 발달에 미치는 영향을 알아보고자 수행되었다. 체외에서 40~44시간 동안 배양된 난자를 전기자극(E)으로 활성화 처리한 후 Thimerasol + Dithiothreitol(Thi+DTT), 6-Dimethylaminopurine(6-DMAP) 및 Cycloheximide(CH)를 사용하여 추가 활성화 처리를 하였다. 활성화 방법(E, E+Thi+DTT, E+6-DMAP 및 E+CH)에 따른 단위발생란의 배반포까지의 발달율을 조사한 결과, chemical agent에 의해 추가 활성화된 단위발생란이 전기자극만으로 처리된 구의 단위발생란보다 유의적으로 높은 발달율을 보였다(21.5~28.1% vs. 18.0%, P<0.05). 특히, E+Thi+DTT를 이용하였을 때 발달율이 유의적으로 높게 나타났다(28.1%, P<0.05). 활성화 처리별 전핵 형성율을 조사한 결과, chemical agent에 의해 추가 활성화 처리된 구에서 하나의 극체(1PN) 형성률은 처리별로 차이를 보이지 않았으나(59.9~64.7%), 2PN 형성율은 추가 활성화 처리구에서 전기자극만을 사용하였을 때보다 유의적으로 높게 나타났다(7.2~9.7% vs. 4.3%, P<0.05). 이상의 결과를 살펴볼 때, 전기자극 후 chemical agent를 이용한 추가 활성화는 단위발생란의 배반포까지의 발달능력을 증가시키는 것으로 생각된다. Artificial activation of oocytes is a prerequisite for the successful cloning by nuclear transfer. This study investigated the effect of the different combination of activation agents such as electric pulse (E), thimerosal (Thi) + dithiothreitol (DTT), 6-dimethylaminopurine (6-DMAP) or cycloheximide (CH) on the developmental ability of porcine embryos derived from parthenogenetic activation (PA). PA embryos activated with chemicals showed significantly higher developmental rate to the blastocyst stage compared to the embryos activated with E alone (21.5~28.1% vs. 18.0%, respectively). Of chemicals, Thi + DTT supported higher development to the blastoryst stage (28.1%). There was no significant difference in 1 pronucleus (PN) formation rate (59.9~64.7%), but 2PN formation rate was significantly higher in PA embryos with additional activation using chemicals (7.2~9.7%). In conclusion, this study shows that chemical activation after electric pulse can increase the development of porcine PA embryos.
서진성,나병기 한국화학공학회 2021 Korean Journal of Chemical Engineering Vol.38 No.9
Spinel Li4Ti5O12 is an attractive anode material for lithium ion batteries due to its stable electrochemical characteristics. However, its low electrical conductivity is regarded as a critical disadvantage for commercialization. The addition of P123 with Cr3+ doping enhanced the surface area and the electrical conductivity, which improved the electrochemical properties of Li4Ti5O12. As-prepared samples were analyzed by X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, as well as BET and BJH analysis. Electrochemical properties were investigated by cyclic voltammetry, electrochemical impedance spectroscopy, powder conductivity measurement and cycle performance testing. P-Li4Ti4.95Cr0.05O12 showed excellent rate performance of 191, 189, 184, 175, 157, and 137 mAh/g at C-rates of 0.2, 0.5, 1, 2, 5, and 10 and high stable capacity retention of 147mAh/g at a C-rate of 10 after 300 cycles.