http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Changes in Physicochemical Properties of Rice Starch Processed by Ultra-Fine Pulverization
한명륜,장문정,김명환 한국응용생명화학회 2007 Journal of Applied Biological Chemistry (J. Appl. Vol.50 No.4
The effects of ultra-fine pulverization on the physicochemical properties of rice starch (RS) were investigated using a high impact planetary mill. After pulverization, RVA characteristics, peak viscosity, break down, and set back values of RS decreased from 274.75 to 9.42 RVU, 214.46 to 6.17 RVU, and 87.80 to 17.00 RVU, respectively. The pasting properties also changed significantly. XRay diffractogram revealed RS had four A-type peaks, which disappeared after pulverization. The peak temperature and gelatinization enthalpy of RS using differential scanning calorimetry (DSC) were 13.99 J/g at 75.14 o C, whereas the pulverized RS (PRS) had two peaks, 0.13 J/g at 63.88 o C and 1.23 J/g at 101.24 o C. DSC measurement showed the retrogradation degree of PRS was lower than that of RS after storage at 4 and 25 o C. The enzymatic ( α -amylase) digestibilities of RS and PRS were 72.7 and 77.3%, respectively
난소화성 전분 제조공정의 최적화 및 이화학적 특성 연구
한명륜(Myung-Ryun Han),김우경(Woo-Kyoung Kim),강남이(Nam-E Kang),이수정(Soo-Jung Lee),김명환(Myung-Hwan Kim) 한국식품영양과학회 2003 한국식품영양과학회지 Vol.32 No.8
아밀로오스 함량이 22%인 일반 옥수수전분과 아밀로오스 함량이 46%인 고아밀로오스 옥수수 전분을 이용하여 난소화성 전분의 제조과정 중 가열온도, 수분함량, 저장온도 및 가열-냉각회수 인자들이 난소화성 전분생성율에 미치는 영향을 반응표면분석법으로 분석한 결과 고아밀로오스 옥수수 전분이 옥수수 전분에 비하여 높은 난소화성 전분의 생성율을 나타내었다. 본 실험조건에서 고아밀로오스 옥수수 전분의 난소화성 전분 생성 최적 제조조건은 6회의 가열-냉각, 20℃의 저장온도, 108℃의 가열온도 및 67%의 수분함량이었으며 생성율은 25% 수준이었다. 난소화성 전분의 제조시 영향을 미치는 순서는 가열-냉각회수, 수분함량, 가열온도, 저장(냉각)온도 순이었다. 난소화성 전분의 제조과정에서 전분입자의 파괴 및 다공성 망상구조를 보였으며 비표면적의 증가와 평균직경의 감소현상이 나타났고 열처리에 의하여 색깔은 어두워지고 노란색상의 증가를 보였다. 가열-냉각 과정에서 옥수수 전분의 경도, 응집성, 탄력성 및 껌성의 감소현상이 두드러졌다. As a result of resistant starch yield depending on heating temperature, moisture content, storage temperature and heating-cooling cycle with RSM (response surface methodology), high amylose corn starch (46%) was appeared higher than normal corn starch in the yield (22%). At the high amylose corn starch, optimum conditions for resistant starch formation were 6 times of heating-cooling cycle, 108℃ heating temperature and 67% moisture content at the 20℃ storage temperature, which resulted in 25% yield with these experiment conditions. Affecting factor for the resistant starch formation was arranged according to heating-cooling cycle, moisture content, heating temperature and storage temperature. Raw corn starch granule was destructive and appeared a porous reticular structure by the resistant starch formation. Color became dark and increased yellowness by caramelization during heating processing. Heating-cooling processing was the result of decreased hardness, cohesiveness, springiness and gumminess.
초미세분쇄를 이용한 옥수수 변성전분의 물리적 특성 변화 구명
한명륜,김애정,장문정,이수정,김희선,김명환 한국산업식품공학회 2009 산업 식품공학 Vol.13 No.4
본 연구는 초미세분쇄기술을 이용하여 옥수수전분의 입자구조파괴가 이루어졌을 때 분자구조적, 물리적 변화가 어떻게 이루어지는지를 구명하고자 하였다. 초미세 분쇄처리 후 옥수수전분의 평균직경은 약 50% 감소가 이루어졌으며 비표면적은 567% 증가하였다. 초미세분쇄처리 전·후의 옥수수전분에 대한 분자량분포를 GPC로 측정한 결과 분쇄 후 저분자량의 Peak II의 면적이 21.0%에서 86.5%로 상승하였다. 손상전분 함량은 각각 9.63%와 83.57%로 초미세분쇄처리에 의하여 크게 증가하였다. 옥수수전분의 경우는 겔(gel)을 형성하였으나 초미세분쇄처리 후에는 전분의 분쇄과정에서 전분입자파괴와 아울러 옥수수전분의 분자량이 저분자화 되면서 겔 형성능력이 크게 저하되었다. This study was performed to analyze changes in the molecular structural and physical properties of modified corn starch, in which particle structure was broken using high impact planetary mill and ultra fine pulverizing techniques. The average diameter and specific surface area of the modditied corn starch after pulverization decreased 50% and increased 567%, respectively. Content of low molecular substances mersured using gel permeation chromatography (GPC) increased from 21.0% to 86.5% after pulverizing corn starch. Damaged starch content also increased from 9.63% to 83.57% after pulverizing corn starch. After pulverization, gel formation capacity corn starch was reduced compared to that of control by structure breakdown.