참조응력을 이용한 316LN 스테인리스강의 크리프 해석
김우곤,류우석,Kim, Woo-Gon,Ryu, Woo-Seog 대한기계학회 2002 大韓機械學會論文集A Vol.26 No.10
Creep damage using a reference stress(RS) was analyzed for type 316LN stainless steel. The generalized K-R equation was reconstructed into the RS equation using a critical stress value $\sigma$. The RS equation was derived from the critical stress in failure time $t_f$ instead of material damage parameter $\omega$, which indicates the critical condition of collapse or approach to gross instability of materials during creep. For obtaining the reference stress, a series of creep tests and tensile tests were conducted with at 55$0^{\circ}C$ and $600^{\circ}C$. The stress-time data obtained from creep tests were applied to the RS equations to characterize the creep damage of type 316LN stainless steel. The value of creep constant r with stress levels was about 18 at 55$0^{\circ}C$ and 21 at $600^{\circ}C$. This value was almost similar with r = 24 in the K-R equation, which was obtained by using damage parameter $\omega$. Relationship plots of creep failure strain and life fraction $(t_f /t_r)$ were also obtained with different λ values. The RS equation was therefore more convenient than the generalized K-R equation, because the measuring process to quantify the damage parameter $\omega$ such as voids or micro cracks in crept materials was omitted. The RS method can be easily used by designers and plant operator as a creep design tool.
UNS N06690 제1열 시제전열관의 U-굽힘성형에서 형상변화와 표면잔류응력
김우곤,장진성,국일현,주진원,김성청,Kim, Woo-Gon,Jang, Jin-Sung,Kuk, Il-Hiun,Joo, Jin-Won,Kim, Sung-Chung 대한기계학회 1998 大韓機械學會論文集A Vol.22 No.1
Surface residual stresses as well as wall thickness and ovality changes after U-bending process on UNS N06690 row-1 heat exchanger tubes, were estimated. Surface residual stresses were measured by Hole Drilling Method(HDM), calculating the stresses from relieved strains of 3 rosette strain gages. After bending of the tubes, dimensional tolerances for wall thickness and ovality were satisfied with ASTM requirements. Residual stresses at the extrados were introduced with compressive stress(-) by bending operations, and its maximum value reached-319 MPa in axial direction at ${\phi}=0^{\circ}$ in position. Tensile residual stresses(+) of ${\sigma}_zz=45$ MPa,${\sigma}_zz=25$ MPa were introduced in the intrados surface at position of ${\phi}=0^{\circ}$ Maximum tensile residual stress of 170 MPa was detected on the flank side at position of ,${\phi}=95^{\circ}$i.e., at apex region. It appeared that higher stress gradients were generated at the irregular transition regions. In the trend of residual stress changes with U-bend position, the extrados is related with the changes of ovality and the intrados is related with the changes of wall thickness.