금민종,김경환,Keum, Min-Jong,Kim, Kyung-Hwan 한국전기전자재료학회 2005 전기전자재료학회논문지 Vol.18 No.8
Al electrode for OLED was deposited by FTS (Facing Targets Sputtering) system which can deposit thin films with low substrate damage. The Al thin films were deposited on the cell (LiF/EML/HTL/Bottom electrode) as a function of working gas such as Ar or Ar+kr mixed gas. Also Al thin films were prepared with working gas pressure (1, 6 mTorr). The film thickness and I-V curve of Al/cell were measured and evaluated. In the results, when Al thin films were deposited using pure Ar gas, the turn-on voltage of Al/cell was about 11 V. And using the Ar:Kr($75\%:25\%$) mixed gas, the turn-on voltage of Al/cell decreased to about 7 V.
대향타겟식 스퍼터링법을 이용한 TOLED용 ITO 박막의 산소 가스 의존성
금민종,김경환,Keum Min-Jong,Kim Kyung-Hwan 한국전기전자재료학회 2006 전기전자재료학회논문지 Vol.19 No.1
In case of preparation of ITO thin film for using top electrode of Top-emitting Organic Light Emitting Diodes(TOLEDs), the ITO thin film should be prepared at room temperature and low oxygen gas flow condition in order to reduced the damage of organic layer due to the bombardment of highly energetic particles such as negative oxygen ions which accrued from the plasma. In this study, the ITO thin film with high optical transmittance and low resistivity prepared as a function of oxygen gas (0 ${\~}$ 0.8 sccm) and Ar gas was fixed at 20 sccm by the Facing Targets Sputtering (FTS) method. The electrical and optical properties of ITO thin films were measured by Hall effect measurement, UV/VIS spectrometer, respectively In the results, we obtained the ITO thin film with lowest resistivity($3{\times}10^{-4} {\Omega}{\cdot} cm$) at oxygen gas flow 0.2 sccm and optical transmittance over $80\%$ at oxygen gas flow over 0.2 sccm.
FBAR용 ZnO/SiO<sub>2</sub>Si 박막의 결정학적 특성에 관한 연구
금민종,손인환,최명규,추순남,최형욱,신영화,김경환 한국전기전자재료학회 2003 전기전자재료학회논문지 Vol.16 No.8
In this study, we prepared ZnO/glass and ZnO/SiO$_2$/Si thin film by Facing Targets Sputtering (FTS) system for Film Bulk Acoustic Resonator (FBAR). When the ZnO thin film applied to piezoelectric thin film, it requires good c-axis preferred orientation. And c-axis orientation has a remarkable difference with preparation conditions. Therefore, c-axis orientation must be significantly evaluated as a function of deposition conditions. Moreover, in order to prepare ZnO thin film with good crystallographic properties and progressive of efficiency of product process, the ZnO thin film should be prepared as low temperature as possible. In this work, we prepared ZnO thin films on slide glass and SiO$_2$/Si substrate. And the crystallographic characteristics of ZnO thin films on sputtering conditions were investigated by alpha-step and X-ray diffraction.
금민종,김영철,서화일,김경환,Keum Min-Jong,Kim Yeong-Cheol,Seo Hwa-Il,Kim Kyung-Hwan 한국반도체디스플레이기술학회 2006 반도체디스플레이기술학회지 Vol.5 No.1
AIN thin films were prepared on amorphous glass and $SiO_2(1{\mu}m)/Si(100)$ substrate by the facing targets sputtering (FTS) apparatus, which can provide high density plasma, a high deposition rate at a low working gas pressure. The AIN thin films were deposited at a different nitrogen gas flow rate ($1.0{\sim}0.3$) and other sputtering parameters were fixed such as sputtering power of 200w, working pressures of 1mTorr and AIN thin film thickness of 800 nm, respectively. The thickness and crystallographic characteristics of AIN thin films as a function of $N_2$ gas flow rate $[N_2/(N_2+Ar)]$ were measured by $\alpha$-step and an X-ray diffraction (XRD) instrument. And the c-axis preferred orientations were evaluated by rocking curve. In the results, we could prepared the AIN thin film with c-axis preferred orientation of about $5^{\circ}$ on substrate temperature R.T. at nitrogen gas flow rate 0.7.
대향타겟스퍼터링법에 의한 FBAR용 AZO(ZnO:Al) 박막의 제작
금민종,김경환 한국전기전자재료학회 2004 전기전자재료학회논문지 Vol.17 No.4
In this study, the AZO thin films were prepared as a function of oxygen gas flow ratio at room temperature by FTS(Facing Targets Sputtering) apparatus using Zn:Al(metal)-Zn:Al(metal) or Zn(metal)-ZnO:Al(ceramic). The film thickness, crystalline and electric properties of AZO thin film was evaluated by $\alpha$-step, XRD and 4-point probe. In the results, the resistivity of AZO thin film was shown the lowest value about 8${\times}$10$^{-2}$ $\Omega$-cm(Zn:Al-Zn:Al), 3${\times}$10$^{-1}$ $\Omega$-cm(Zn-ZnO:Al) at the oxygen gas flow ratio 0.3. And the AZO thin film has good crystalline at oxygen gas flow ration 0.4, using Zn:Al-Zn:Al targets.
FTS법으로 제작한 ZnO/AZO 박막의 결정학적 특성
금민종,강태영,최형욱,박용서,김경환 한국전기전자재료학회 2004 전기전자재료학회논문지 Vol.17 No.9
The ZnO thin films were prepared by the FTS (facing target sputtering) system, which enables to provide high density plasma and a high deposition rate at a low working gas pressure. We introduced the AZO thin film in order to improve the crystallographic properties of ZnO thin film because of the AZO(ZnO:Al) thin film has an equal crystal structure to the ZnO thin film. ZnO/AZO thin films were deposited at a different oxygen gas flow ratio, R.T. 2mTorr working pressure and a 0.8A sputtering current. The film thickness and c-axis preferred orientation of ZnO/AZO/glass thin films were measured by ${\alpha}$-step and an x-ray diffraction (XRD) instrument. In the results, we could prepare the ZnO thin film with c-axis preferred orientation of about 6$^{\circ}$ on substrate temperature R.T. at O$_2$ gas flo rate 0.5.