Hbr/O<sub>2</sub> 유도결합 플라즈마를 이용한 폴리실리콘 건식식각
범성진,송오성,이혜영,김종준 한국전기전자재료학회 2004 전기전자재료학회논문지 Vol.17 No.1
Dry etch characteristics of polysilicon with HBr/O$_2$ inductively coupled plasma (ICP) have been investigated. We determined etch late, uniformity, etch profiles, and selectivity with analyzing the cross-sectional scanning electron microscopy images obtained from top, center, bottom, right, and left positions. The etch rate of polysilicon was about 2500 $\AA$/min, which meets with the mass production for devices. The wafer level etch uniformity was within $\pm$5 %. Etch profile showed 90$^{\circ}$ slopes without notches. The selectivity over photoresist was between 2:1∼4.5:1, depending on $O_2$ flow rate. The HBr-ICP etching showed higher PR selectivity, and sharper profile than the conventional Cl$_2$-RIE.
Co/Ni 복합실리사이드의 메탈 콘택 건식식각 안정성 연구
송오성,범성진,김득중,Song Ohsung,Beom Sungjin,Kim Dugjoong 한국재료학회 2004 한국재료학회지 Vol.14 No.8
Newly developed silicide materials for ULSI should have the appropriate electrical property of low resistant as well as process compatibility in conventional CMOS process. We prepared $NiCoSi_x$ silicides from 15 nm-Co/15 nm-Ni/Si structure and performed contact dry etch process to confirm the dry etch stability and compatibility of $NiCoSi_x$ layers. We dry etched the photoresist/SiO/silicide/silicon patterns with $CF_4\;and\;CHF_3$ gases with varying powers from 100 to 200 W, and pressures from 45 to 65 mTorr, respectively. Polysilicon and silicon active layers without silicide were etched $0\sim316{\AA}$ during over etch time of 3min, while silicon layers with proposed $NiCoSi_x$ silicide were not etched and showed stable surfaces. Our result implies that new $NiCoSi_x$ silicides may replace the conventional silicides due to contact etch process compatibility.