Effect of Annealing on Lattice Strain and Near-Band-Edge Emission of ZnO Nanorods
Musbah Babikier,Jinzhong Wang,Dunbo Wang,Qian Li,Jianming Sun,Yuan Yan,Wenqi Wang,Qingjiang Yu,Shujie Jiao,Shiyong Gao,Hongtao Li 대한금속·재료학회 2014 ELECTRONIC MATERIALS LETTERS Vol.10 No.4
The effect of air and oxygen annealing on the structural and the optical properties of hydrothermally synthesized ZnO nanorods was investigated. After hydrothermal synthesis, the resulting ZnO nanorods were annealed in air and under an oxygen atmosphere at 370°C for 1 h. X-ray diffraction results revealed that the oxygen-annealed nanorods possessed high crystallinity with a hexagonal-wurtzite crystal structure in the (002) plane. Evaluation of strain showed a tensile lattice strain of 0.426% resulting from oxygen annealing. The photoluminescence measurements showed that the relative intensity ratio of the near-band-edge emission (NBE) to the green emission (INBE/IGE) increased from ~2.6 for the as-grown ZnO nanorods to ~68.7 when the nanorods were annealed under oxygen. After annealing, a red shift of ~30 and ~44 meV in the NBE was observed for the nanorods that were annealed in air and under oxygen, respectively. This shift is attributed to the interaction between the neutral acceptors and the adsorbed oxygen atoms.
Synthesis of CdS, ZnS, and CdS/ZnS Core/Shell Nanocrystals Using Dodecanethiol
Jinzhong Niu,Weiwei Xu,Huaibin Shen,Sen Li,Hongzhe Wang,Lin Song Li 대한화학회 2012 Bulletin of the Korean Chemical Society Vol.33 No.2
We report a new route to synthesize high quality zinc blende CdS and ZnS nanocrystals in noncoordinating solvent 1-octadecene, using dodecanethiol (DDT) molecules as both the sulfur source and surface capping ligands. Different reaction temperatures and Cd(Zn)/DDT molar ratios were tested to optimize the synthesis conditions. Absorption photoluminescence (PL) spectroscopy, Fourier transform infrared (FTIR) spectroscopy,X-ray diffraction (XRD) pattern, and transmission electron microscopy (TEM) were used to characterize assynthesized nanocrystals. The narrow half width at the half-maximum on the long wavelength side of the firstexcitonic absorption peak and TEM images demonstrated nearly monodisperse size distributions of asprepared CdS, ZnS, and CdS/ZnS core/shell nanocrystals. Only trap emissions of the nanocrystals were detected when the amount of DDT was excessive, this came from the strong quenching effect of thiol groups on the nanocrystal surfaces. After overcoating with ZnS shells, band-gap emissions of CdS nanocrystals were partially recovered.
Synthesis of CdS, ZnS, and CdS/ZnS Core/Shell Nanocrystals Using Dodecanethiol
Niu, Jinzhong,Xu, Weiwei,Shen, Huaibin,Li, Sen,Wang, Hongzhe,Li, Lin Song Korean Chemical Society 2012 Bulletin of the Korean Chemical Society Vol.33 No.2
We report a new route to synthesize high quality zinc blende CdS and ZnS nanocrystals in noncoordinating solvent 1-octadecene, using dodecanethiol (DDT) molecules as both the sulfur source and surface capping ligands. Different reaction temperatures and Cd(Zn)/DDT molar ratios were tested to optimize the synthesis conditions. Absorption photoluminescence (PL) spectroscopy, Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD) pattern, and transmission electron microscopy (TEM) were used to characterize assynthesized nanocrystals. The narrow half width at the half-maximum on the long wavelength side of the firstexcitonic absorption peak and TEM images demonstrated nearly monodisperse size distributions of asprepared CdS, ZnS, and CdS/ZnS core/shell nanocrystals. Only trap emissions of the nanocrystals were detected when the amount of DDT was excessive, this came from the strong quenching effect of thiol groups on the nanocrystal surfaces. After overcoating with ZnS shells, band-gap emissions of CdS nanocrystals were partially recovered.
A High-Performance Self-Powered UV Photodetector Based on SnO2 Mesoporous Spheres @ TiO2
Yuewu Huang,Qingjiang Yu,Jinzhong Wang,Xiaochao Li,Yuan Yan,Shiyong Gao,Feifei Shi,Dongbo Wang,Cuiling Yu 대한금속·재료학회 2015 ELECTRONIC MATERIALS LETTERS Vol.11 No.6
A novel self-powered UV photodetector (UVPD) based on the photoelectrochemical cell (PECC) has been constructed using the TiO2 coated SnO2 mesoporous spheres (SnO2-MS@TiO2). This self-powered UVPD displays a higher photocurrent density compared to the UVPD with the pure SnO2-MS. By means of external quantum efficiency (EQE), UV-vis absorption, and electrochemical impedance measurements, we scrutinize the intrinsic role of the TiO2 coating layer on the photocurrent enhancement. Under UV irradiation, this UVPD exhibits a high on/off ratio of 11519, a fast rise time of 0.007 s and decay time of 0.006 s, together with the excellent visible-blind characteristic and linear optical signal response. The self-powered photodetector is a promising candidate for application in high-sensitivity and high-speed UVPDs.
Synthesis of CdS Nanocrystals with Different Shapes via a Colloidal Method
Jie Bai,Changsong Liu,Jinzhong Niu,Hongzhe Wang,Shasha Xu,Huaibin Shen,Lin Song Li 대한화학회 2014 Bulletin of the Korean Chemical Society Vol.35 No.2
Size- and shape-controlled monodisperse wurtzite structured CdS nanorods have been successfully synthesized using a facile solution-based colloidal method. Depending on the control of injection/growth temperatures and the variation of Cd-to-S molar ratios, the morphology of the CdS nanocrystals (NCs) can be adjusted into bullet-like, rod-like, and dot-like shapes. X-ray diffraction (XRD), transition electron microscopy (TEM), and absorption spectroscopy were used to characterize the structure, morphology, and optical properties of assynthesized CdS NCs. It was found that uniform CdS nanorods could be successfully synthesized when the injection and growth temperatures were very high (> 360 °C). The aspect ratios of different shaped (bullet-like or rod-like) CdS NCs could be controlled by simply adjusting the molar ratios between Cd and S.
Shan Jiang,Ce Cui,Weijie Wang,Erhui Ren,Hongyan Xiao,Mi Zhou,Jinzhong Tang,Cheng Cheng,Ronghui Guo 한국섬유공학회 2022 Fibers and polymers Vol.23 No.11
Multifunctional flexible conductive materials have attracted significant attention as next-generation portablewearable electronics. However, designing robust electronics fabrics with high-performance electromagnetic interference(EMI) shielding and reliable use in all-weather environments remains a challenge. Herein, a practical and optimizedmethodology was provided to achieve surface metallization of insulating fabrics for conductive devices. The Ag seeds weresuccessfully embedded on the surface of viscose nonwovens as catalytic centers, and ammonia-free silver plating was carriedout at room temperature. Subsequently, the Ag-wrapped fabric was impregnated with 1-octadecanethiol so that the surface ofthe obtained fabric showed super-hydrophobicity and water contact angle can reach 152.3 °. The Ag/viscose exhibitsultrahigh conductivity (up to 538 S/cm) and the EMI shielding effectiveness (SE) reaches as high as 94.1 dB in the range of1-18 GHz. The obtained Ag/viscose possesses outstanding waterproof, strong mechanical durability, excellent Joule heatingeffect and antibacterial, which can be potentially applied for multifunctional wearable electronics and smart clothing.
Synthesis of CdS Nanocrystals with Different Shapes via a Colloidal Method
Bai, Jie,Liu, Changsong,Niu, Jinzhong,Wang, Hongzhe,Xu, Shasha,Shen, Huaibin,Li, Lin Song Korean Chemical Society 2014 Bulletin of the Korean Chemical Society Vol.35 No.2
Size- and shape-controlled monodisperse wurtzite structured CdS nanorods have been successfully synthesized using a facile solution-based colloidal method. Depending on the control of injection/growth temperatures and the variation of Cd-to-S molar ratios, the morphology of the CdS nanocrystals (NCs) can be adjusted into bullet-like, rod-like, and dot-like shapes. X-ray diffraction (XRD), transition electron microscopy (TEM), and absorption spectroscopy were used to characterize the structure, morphology, and optical properties of as-synthesized CdS NCs. It was found that uniform CdS nanorods could be successfully synthesized when the injection and growth temperatures were very high (> $360^{\circ}C$). The aspect ratios of different shaped (bullet-like or rod-like) CdS NCs could be controlled by simply adjusting the molar ratios between Cd and S.