http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Co-Doped Willemite 파란색 안료의 합성과 생성기구
황동하,한경섭,이병하,Hwang, Dong-Ha,Han, Kyong-Sop,Lee, Byung-Ha 한국세라믹학회 2010 한국세라믹학회지 Vol.47 No.6
Turquoise blue pigment of Vanadium-zircon blue (DCMA number 14-42-2), which was already commercialized, was stable to be reproduced but insufficient to give strong blue. However, it possible to obtain more intense blue by partially substituting cobalt ions into the willemite($Zn_2SiO_4$) lattice classified into DCMA number 7-10-2 for blue ceramic pigment. By the composition of willemite $Co_xZn_{2-x}SiO_4$(X=0.01, 0.03, 0.05, 0.07, 0.09 mole), this study used reagent grade zinc oxide, cobalt oxide and silicon dioxide as starting materials, carrying out the synthesis with solid reaction method by adding $H_3BO_3$ as a mineralizer. The firing temperature was between $1200^{\circ}C$ and $1400^{\circ}C$. The characteristics of synthesized pigment were analyzed by X-ray diffraction, Raman spectroscopy and SEM and the characteristics of color tones were analyzed by UV-Vis spectroscopy and CIE-$L^*a^*b^*$ measurement. As a result, the optimal composition was $Zn_{1.95}Co_{0.05}$ with 1wt% of $H_3BO_3$ as a mineralizer and firing condition was $1350^{\circ}C$/3 h. $L^*a^*b^*$ value was 29.25, 41.03, -59.93 for on glaze pigment and 37.03, 36.41, -60.03 for under glaze pigment.
배동식,김은중,이해원,한경섭,Bae, Dong-Sik,Kim, Eun-Jung,Lee, Hae-Won,Han, Kyong-Sop The Korean Ceramic Society 2002 한국세라믹학회지 Vol.39 No.10
Nanosized $Mn_xFe_2O_4$ powders were prepared in ethylene glycol solution under mild temperature and pressure conditions by precipitation from metal nitrates with aqueous potassium hydroxide. The average size and distribution of the synthesized $Mn_xFe_2O_4$ powders was about 20 nm and broad, respectively. The phase of synthesized particles was crystalline reacted at 200${\circ}C$ for 6h. The magnetic properties of the synthesized $Mn_xFe_2O_4$ powders were about 35-60 (emu/g) with superparamagnetic character.
예비성형체 및 금속복합재료에 미치는 바인더의 영향에 관한 연구
남현욱,민병렬,이종해,한경섭,Nam, Hyun-Wook,Min, Byung-Ryoul,Lee, Jong-Hae,Han, Kyung-Seop 대한기계학회 1999 大韓機械學會論文集A Vol.23 No.6
The effects of binder on the mechanical properties of the preforms and metal matrix composites (MMCs) were studied. Fibers were $9Al_2O_3{\cdot}2B_2O_3(Alborex)$, HTZ and $Al_2O_3$ fibers(Saffil) and binders were organic binder, inorganic binder, polyacrylamide under various PH conditions. Compressive strength of the preform increased with the addition of inorganic binder. The polyacrylamide did not improve the permeability of the preforms. PH of the slurry should be controlled because it affects the viscosity of the slurry. Good preforms were obtained under following conditions : 3 wt% inorganic binder, 0.1 wt% organic binder, 0.1 wt% polyacrylamide and PH 9. Tensile tests of MMCs were conducted at $20^{\circ}C,\;150^{\circ}C,\;250^{\circ}C,\;350^{\circ}C$ using MTS(100KN USA). Wear tests were conducted under various sliding speeds. High temperature($250^{\circ}C$) tensile strengths of Alborex/Saffil/AC8A and HTZ/AC8A are 80% and 75% of the room temperature tensile strengths respectively. The tensile and wear properties of the Alborex/Saffil/AC8A are superior to that of the HTZ/AC8A. The wear behavior of HTZ/AC8A shows more orthotropic characteristic than that of Alborex/Saffil/AC8A.