엄영랑,이창규,김철성,Uhm Young-Rang,Rhee Chang-Kyu,Kim Chul-Sung 한국분말야금학회 2006 한국분말재료학회지 (KPMI) Vol.13 No.2
[ $R_{1/3}Sr_{2/3}FeO_{3}$ ](R=Pr, Nd, and Sm) was synthesized and their magnetic properties and charge ordering(CO) transition related with lattice dynamics and oxygen vacancy were systematically investigated. The charge disproportion ation(CD) in $R_{1/3}Sr_{2/3}FeO_{3}$(R=Pr,Nd) was in which two kins of iron with valence state $Fe^{3+}$ and $Fe^{5+}$ were found with ratio of 2:1. In this charge ordering state a sequence of $Fe^{3+}Fe^{3+}Fe^{5+}Fe^{3+}Fe^{3+}Fe^{5+}$ exists aligned along the [111] direction of the pseudocubic perovskite structure. The charge ordering exist in distorted structure involving $t_{pd}$ hybridization. The disordering phases coexist in distorted structure as temprature in creases that is controlled amount of oxygen vacancy. The magnetic hyperfine fields indicate charge tranfering temperature as it dissapeared drastically.
중금속 검출용 고감도 나노표지센서 구현을 위한 볼타메트리 시스템 설계 연구
김주명,이창규,Kim, Ju-Myoung,Rhee, Chang-Kyu 한국분말야금학회 2012 한국분말재료학회지 (KPMI) Vol.19 No.4
In this study, voltammetry system for realizing high sensitivity nano-labeled sensor of detecting heavy metals was designed, and optimal system operating conditions were determined. High precision digital to analog converter (DAC) circuit was designed to control applied unit voltage at working electrode and analog to digital converter (ADC) circuit was designed to measure the current range of $0.1{\sim}1000{\mu}A$ at counter electrode. Main control unit (MCU) circuit for controlling voltammetry system with 150 MHz clock speed, main memory circuit for the mathematical operation processing of the measured current value and independent power circuit for analog/digital circuit parts to reduce various noise were designed. From result of voltammetry system operation, oxidation current peaks which are proportional to the concentrations of Zn, Cd and Pb ions were found at each oxidation potential with high precision.
스텔라이트 합금 용사 코팅의 피로 강도에 미치는 후열처리의 영향
오정석,이창규,Oh Jeong Seong,Komotori Jun,Rhee Chang Kyu 한국분말야금학회 2005 한국분말재료학회지 (KPMI) Vol.12 No.2
The effect of post-heat treatment on the coating characteristics and the fatigue strength of the gas flame thermally sprayed Stellite alloy coatings on $0.35\%$ carbon steel were investigated. The fatigue fracture surfaces of the heat treated samples were observed using SEM (Scanning Electron Microscopy). For as-sprayed samples, there was considerable scattering in the fatigue life due to the presence of the pores in the coating. After the post-heat treatment to improve the microstructural characteristics of the coating layer, the fatigue strength of the specimens was greatly improved, increasing with increasing the coating thickness. For the specimens with the 0.3mm and 0.5mm thick coating, the fatigue cracks originated in the substrate region just below the interface. On the contrary, for the specimens with the 1.0mm thick coating, they nucleated at the pore within the coating, and the fatigue strength was 2.6 times higher than that of the substrate due to the high fatigue resistance of the coating.
이은희,이민구,이창규,Lee Eun-Hee,Lee Min-Ku,Rhee Chang-Kyu 한국분말야금학회 2006 한국분말재료학회지 (KPMI) Vol.13 No.2
In this study, the effects of the dispersants, i.e., Hypermer KD-2 and poly(l-vinyl-2-pyrrolidone) (PVP), and their concentration on the dispersion stability of Ni nanoparticles ($10nm{\sim}40nm$) in ethanol were investigated by using a visual inspection, a transmission profile (Turbiscan), and a zeta potential measurement. The transmission profiles measured by Turbiscan showed that the particle size increased over the entire height of the sample for suspensions with both the dispersants without showing any particle coalescence and sedimentation. The visual inspection also confirmed that the Ni suspensions with Hypermer KD-2 and PVP were very stable for more than a year. The zeta potential values varied from positive to negative with increasing the dispersant's concentration. The dispersion stability of the suspensions was not affected by both the dispersant's concentration and the zeta potential values. The observed suspension stability of Ni nanoparticles was attributed to the steric effect for the Hypermer KD-2 and to the bridging effect for the PVP.
김경호,이민구,이창규,위명용,김흥회,Kim, Kyeong-Ho,Lee, Min-Ku,Rhee, Chang-Kyu,Wey, Myeong-Yong,Kim, Whung-Whoe 대한기계학회 2002 大韓機械學會論文集A Vol.26 No.12
In this research, fretting tests were conducted in air to investigate the wear characteristics of fuel cladding materials with the fretting parameters such as normal load, slip amplitude, frequency and the number of cycles. A high frequency fretting wear tester was designed for this experiment by KAERI. After the experiments, the wear volume and the shape of wear contour were measured by the surface roughness tester. Tribologically transformed structures(TTS) were analysed by means of optical and scanning electron microscopes to identify the main wear mechanisms. The results of this study showed that the wear volume were increased with increasing slip amplitude, and the shape of wear contour was transformed V-type to W-type. Also, it was found that the critical slip amplitude was 168${\mu}{\textrm}{m}$. These phenomena mean that wear mechanism transformed partial slip to gross slip to accelerate wear volume. The wear depth increased with an increase of friction coefficient due to increase of normal load and frequency. The fretting wear mechanisms were believed that, after adhesion and surface plastic deformation occurred by relative sliding motion on the contact between two specimens, TTS creation was induced by surface strain hardening and wear debris were detached from the contact surface which were produced by the micro crack propagation and creation.
전기선 폭발법을 이용하여 제조된 구리 나노유체의 특성평가
김창규,이경자,이창규,Kim, Chang-Kyu,Lee, Gyoung-Ja,Rhee, Chang-Kyu 한국분말야금학회 2010 한국분말재료학회지 (KPMI) Vol.17 No.4
Ethylene glycol-based Cu nanofluids were prepared by pulsed wire evaporation (PWE) method. The structural properties of Cu nanoparticles were studied by X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). The average diameter and Brunauer Emmett Teller (BET) surface area of Cu nanoparticles were about 100 nm and $7.46\;m^2/g$, respectively. The thermal conductivity and viscosity of copper nanofluid were measured as functions of Cu concentration and temperature. As the volume fraction of Cu nanoparticles increased, both the enhanced ratios of thermal conductivity and viscosity of Cu nanofluids increased. As the temperature increased, the enhanced ratio of thermal conductivity increased, but that ratio of viscosity decreased.