Graphene oxide templated alumina nanosheet for the removal of As(V)
원동신,박인수,박명훈,손연선,김병규,남기석,정강섭,김필 한국물리학회 2014 Current Applied Physics Vol.14 No.9
The current paper demonstrates a simple preparative method of alumina nanosheet through controlled hydrolysis and condensation on the surface of graphene oxide (GO). Taking into account the moisture sensitivity of the alumina precursor, its hydrolysis was carried out after introduction of interaction between the functional groups of GO and the alumina precursor in a non-aqueous solvent. On pyrolysis of the aluminum oxide-GO composite, a free-standing alumina nanosheet was obtained, which was further confirmed by XRD, TEM, STEM-EDX, FE-SEM, TGA, and N2 physisorption. Due to a favorable nanosheet structure, the alumina nanosheets showed a better performance in the removal of As (V) when compared to alumina prepared without GO template, even though the latter had a larger surface area than the alumina nanosheet.
Preparation and characterization of PtNi/C@Pt for oxygen reduction reaction
박명훈,원동신,박진후,이상수,손연선,남기석,김필 한국공업화학회 2015 한국공업화학회 연구논문 초록집 Vol.2015 No.0
고분자 전해질형 연료전지는 공해물질을 배출하지 않고 에너지 효율이 높아 차세대 수송용 전원으로 주목 받고 있으나, 양극에서 발생하는 산소환원반응이 매우 느리기 때문에 고가의 백금이 다량 사용되고 있다. 백금의 경우 가격이 비싸고 매장량의 한계가 있기 때문에 연료전지의 가격 경쟁력을 저하시키는 원인이 된다. 이를 개선하기 위하여 백금 촉매의 활성을 증가시켜 전극 촉매 비용을 절감하려는 연구가 활발히 진행되고 있다. 중공형 구조로 제어된 촉매는 백금의 사용량이 적고 산소환원반응에 대하여 우수한 활성을 갖는다고 보고되고 있다. 본 연구에서는 니켈을 탄소에 담지한 뒤 갈바닉 치환을 통해 중공형 구조의 PtNi/C@Pt 촉매를 제조하여 연료전지의 산소환원반응용 촉매로 적용하였다.