http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
강인남,이지훈,Kang In-Nam,Lee Ji-Hoon 한국전기전자재료학회 2006 전기전자재료학회논문지 Vol.19 No.6
We have synthesized a new p-type polymer, poly(9,9'-n-dioctylfluorene-alt-phenoxazine) (PFPO), via the palladium catalyzed coupling reaction. The number average molecular weight ($M_n$) of PFPO was found to be 23,000. PFPO dissolves in common organic solvents such as chloroform and toluene. The UV-visible absorption maximum of the PFPO thin film is clearly blue-shifted with respect to that of F8T2, poly-(9,9'-n-dioctylfluorene-alt-bithiophene). The introduction of the phenoxazine moiety into the polymer system results in better field-effect transistor (FET) performance than that of F8T2. A solution processed PFPO TFT device with a top contact geometry was found to exhibit a hole mobility of $2.7{\times}10^{-4}cm^2/Vs$ and a low threshold voltage of -2 V with high on/off ratio(${\sim}10^4$).
불소 함유된 고분자를 이용한 안정한 청색 발광 유기 EL
강인남,Kang In-Nam 한국전기전자재료학회 2006 전기전자재료학회논문지 Vol.19 No.6
We have synthesized new blue light emitting random copolymers, poly(9,9'-n-dioctylfluorene-co-perfluorobenzene-1,4-diyl)s (PFFBs), via Ni(0)-mediated coupling reactions. The weight-average molecular weights ($M_w$) of the PFFB copolymers ranged from 9,000 to 15,000. The PFFB copolymers dissolved in common organic solvents such as THF and toluene. The PL emission peaks of the PFFB copolymers were at around 420, 440, and 470 nm. EL devices were fabricated in ITO/PEDOT/polymer/Ca/Al configurations using these polymers. These EL devices were found to exhibit pure blue emission with approximate CIE coordinates of (0.15, 0.11) at $100cd/m^2$. The blue emissions of these devices might be due to the restriction of the polymer chains to aggregation by introducing of the highly electronegative fluorine moieties. The maximum brightnesses of the PFFB copolymer devices ranged from 140 to $3600cd/m^2$ with maximum efficiencies from 0.2 to 0.6 cd/A. The enhanced efficiency of the PFFB (8/2) copolymer device results from the inhibition of excimer formation by the introduction of the electronegative fluorine moieties into the copolymers.
피라졸 유도체를 함유한 폴리알킬플루오렌 공중합체의 향상된 EL 특성
강인남,이지훈,Kang, In-Nam,Lee, Ji-Hoon 한국전기전자재료학회 2010 전기전자재료학회논문지 Vol.23 No.7
We have synthesized new blue electroluminescent polyalkylfluorene-based copolymers [poly(F-co-Py)x:y, where x:y = 99:1 or 95:5 mole ratios] containing the hole-injecting pyrazole derivative [3,3'-(4,6-bis(octyloxy)-1,3-phenylene)bis(1,5-diphenyl-4,5-dihydro-1H-pyrazole] through Ni(0) mediated polymerization, and their electroluminescent properties were investigated. Electroluminescent (EL) devices were fabricated with ITO / PEDOT:PSS (110 nm) / copolymers or PF homopolymer (80 nm) / Ca (50 nm) / Al (200 nm) configuration. Each EL device constructed from the copolymer exhibited significantly enhanced brightness and efficiency compared with a device constructed from the PF homopolymer. The EL device constructed with poly(F-co-Py)99:1 exhibited the highest luminous efficiency and brightness (0.95 cd/A and $2,907\;cd/m^2$, respectively). The achieved luminous efficiency was an excellent result, providing almost a 4-fold improvement on the efficiency obtainable with the a PF homopolymer device. This enhanced efficiency of the copolymer devices results from their improved hole injection and more efficient charge carrier balance, which arises from the HOMO level (~5.83 eV) of the poly(F-co-Py)99:1 copolymer, which is higher than that of the PF homopolyme (~5.90 eV).