유기용제가 무정형 폴리에스테로공중합체의 물성에 미치는 영향
장영욱,조희민 한국공업화학회 1999 응용화학 Vol.3 No.1
A study has been carried out to see the effect of solvent sorption on the mechanical properties of amorphous copolyesters. Sorption and desorption curves indicated that, among the solvents investigated, N,N-dimethylformamide(DMFA) was sorbed greatly by the copolyesters. The effect of solvent environments on the mechanical properties of amorphous copolyesters have been studied by means of the tensile test. From the mechanical behaviour of copolyesters before and after sorption, we found that change of the mechanical properties of copolyesters is explained on the basis of the plasticization, solvent induced crystallization, surface cavitation, and chemical attack.
김상우,석지후,김병현,조희민,조국영,Kim, Sang Woo,Seok, Ji-Hoo,Kim, Byung-Hyun Daniel,Cho, Hee-Min,Cho, Kuk Young 한국전기화학회 2014 한국전기화학회지 Vol.17 No.1
리튬이차전지의 고에너지 밀도화를 위해 전지 구성요소들의 무게 및 부피를 저감하려는 요구가 증가하고 있다. 분리막은 리튬이온의 이동통로를 제공할 뿐만 아니라 양극과 음극의 직접적인 접촉을 방지하는 핵심 부품이다. 본 연구에서는 연신 비율을 달리하여 습식방법을 통해 두께가 16, 12, $9{\mu}m$ 인 폴리에틸렌 분리막을 준비하였고, 각각의 기계적 강도 및 열적특성을 평가하였다. 또한 양극($LiCoO_2$), 음극(Graphite)을 사용한 Coin type full-cell을 제작하여 율속 특성 및 500cycle까지 사이클 수명특성을 평가하였다. 수명특성 평가를 통해 사용된 모든 두께의 분리막에서 500cycle 까지 큰 차이 없이 80% 정도의 용량유지 결과를 확인하였다. 율속 특성에서는 가장 얇은 $9{\mu}m$ 분리막이 가장 우수한 성능을 나타내었다. 흥미롭게도 $9{\mu}m$의 분리막이 $16{\mu}m$ 경우보다 열 수축률 평가에서 우수한 특성을 나타내었다. There is increasing demand on the reducing the weight and the volume of the major components in lithium secondary battery to improve energy density. Separator not only provides pathway for lithium ion movement but also prevents direct contact between anode and cathode. Herein we fabricated polyethylene separator by varying biaxial stretching ratio to obtain membrane thickness of 16, 12, and $9{\mu}m$. Mechanical and thermal properties of the separator with different thickness were investigated. Also rate capability and charge-discharge cycle property up to 500 cycles were studied using coin type full-cell with $LiCoO_2$ and graphite as a cathode and an anode, respectively. All the cells using separator with different thickness demonstrated excellent capacity retention after 500cycles (around 80%). Considering the rate capability, cell using separator with thickness of $9{\mu}m$ showed best performance. Interestingly, separator thickness of $9{\mu}m$ was more resistant to heat contraction compared to that of $16{\mu}m$ separator.