CM247LC 초내열합금 터빈 블레이드 용접 열영향부의 액화균열 발생 거동 및 민감도 평가

정예선,김경민,이의종,이형수,서성문,천은준 대한금속·재료학회 2020 대한금속·재료학회지 Vol.58 No.12

In this study, the weldability of the as-cast CM247LC superalloy for turbine blade applications was metallurgically evaluated in terms of its hot cracking behavior and susceptibility. For this purpose, a real blade was manufactured using a directional solidification casting process, and gas tungsten arc welding was performed at the tip and cavity of the upper blade. Hot cracking was confirmed in the heat-affected zone (HAZ) of gas tungsten arc welds, and the cracks were characterized as liquation cracks, since a cobble or dropletshaped crack surface consistent with a liquid film was clearly confirmed. Microstructural analysis of the cracking surface and thermodynamic calculations helped elucidate the metallurgical mechanisms of the liquation cracking. In other words, the cracking was attributed to liquation of the γ-γ’ eutectic colony and the constitutional liquation of the MC-type carbides: these phases existed in the as-cast microstructure. In particular, it was calculated that liquation of the γ-γ’ eutectic colony during welding occurs at least at 1488 K and that constitutional liquation of MC-type carbides begins at 1411 K, while the equilibrium solidus temperature of the CM247LC alloy is 1530 K. Finally, the liquation cracking susceptibility was quantitatively evaluated through a spot-Varestraint test, and it was confirmed for the first time that the higher susceptibility of as-cast samples can be suppressed by employing a pre-weld heat treatment such as solution treatment.

CM247LC 초내열합금 용접 열영향부 액화균열 제어를 위한 야금학 및 공정적 검토

정예선,김경민,이형수,서성문,천은준 대한용접·접합학회 2021 대한용접학회 특별강연 및 학술발표대회 개요집 Vol.2021 No.5

가스터빈 블레이드의 일방향 응고 소재로 검토되고 있는 CM247LC 합금은 MAR-M247 합금을 토대로 C함량을 저감시켜, 주조성 및 고온 기계적 성질을 향상시킨 Ni계 초내열합금이다. 블레이드 제조 시에는 용접공정이 수반되고, 특히 CM247LC와 같은 석출경화형 초내열합금 용접 시에는 다양한 종류의 고온균열(응고, 액화, 연성저하 균열 등)이 복합적으로 발생하는 것으로 알려져 있고, 건전한 용접부 제조를 위해서는 해당 고온균열의 면밀한 제어가 필수적이다. 액화균열은 열영향부의 부분용융영역(partial melted zone)에서 발생하고, 모재 2차상 (secondary phase) 부분 액상화 및 불순물 원소의 입계편석 현상과 밀접한 관련이 있는 것으로 알려져 있다. 특히 CM247LC 초내열합금의 다층 용접 및 적층 제조부에서도 액화균열 현상은 상당히 문제시되고 있으나, 야금학적 관점에서 액화균열 민감도 평가 및 제어에 대한 기초연구는 상당히 부족한 실정이다. 따라서 본 연구에서는 CM247LC 초내열합금 블레이드의 용접 건전성을 액화균열 관점에서 면밀히 검토하고, 야금학적 제어 인자를 도출하고자 한다. Varestraint 시험 및 고속열화상 온도 가시화를 통해, CM247LC 합금 용접부의 액화균열 발생 온도범위 (liquation cracking temperature range, LCTR)를 평가하였고, 다양한 열처리 조건을 적용함으로써 LCTR을 최소화할 수 있는 CM247LC 합금 미세조직을 탐색하였다. 해당 결과를 토대로 CM247LC 합금 용접부 액화균열 제어에 대한 야금학적 인자를 도출하였고, 액화 무균열 용접을 위한 공정적 가이드라인도 함께 검토하였다. Spot-Varestraint 시험 결과, CM247LC 주조재의 LCTR은 620 K, 용체화 열처리재 560 K 및 시효 열처리재 66 K 로 각각 평가되었다. CM247LC 합금 용접 열영향부의 액화균열 민감도는 용체화 및 시효 열처리 적용으로 저감 가능하며, 특히 시효 열처리는 주조재의 액화균열 민감도를 약 90% 이상 저감 시키는 것으로 평가되었다. 시효 열처리에 따른 LCTR 축소는 조성적 액화를 일으키는 MC형 탄화물 감소, 저융점 공정 γ/γ’ 조직의 고용 및 γ’ 석출상 형성으로 인한 미세조직 균질화로 인해, 용접 승온 시의 액상화 시작온도가 증가하기 때문인 것으로 확인되었다. 이러한 액화균열 민감도 평가 결과를 바탕으로, 액화 무균열 용접을 위해서는 시효 열처리 적용과 입열량 최소화 (540 J/mm 미만)가 병행되어야 할 것으로 판단되었다. 더불어 입열량 30 J/mm 이하의 레이저 용접 적용 시에는 시효 열처리를 적용하지 않더라도 무균열 용접부 제조가 가능한 것으로 평가되었다.

가스터빈 고온부품용 CM247LC, CM939W, IN792 초내열합금 용접 열영향부의 액화균열 민감도 평가

정예선,박기덕,이의종,이형수,서성문,천은준 대한용접·접합학회 2022 대한용접학회 특별강연 및 학술발표대회 개요집 Vol.2022 No.5

[P1-28] 대체감미료 청가가 sponge cake의 품질 특성에 미치는 영향

정예선,은정화,김대진 한국식품영양과학회 2008 한국식품영양과학회 학술대회발표집 Vol.2008 No.10

Clostridium difficile 분리 균주들에 대한 Arbitrarily Primed-Polymerase Chain Reaction and Polymerase Chain Reaction-Ribotyping에 의한 분자역학적 분석 방법 비교 연구

정예선,정경태,성원근,오희복 대한감염학회 2002 감염 Vol.34 No.3

Evaluation and Control of Liquation Cracking Susceptibility for CM247LC Superalloy Weld Heat-Affected Zone via Visualization-Based Varestraint Test

정예선,김경민,이형수,서성문,천은준 대한금속·재료학회 2021 대한금속·재료학회지 Vol.59 No.7

The metallurgical aspects of weld cracking in Ni-based superalloys remain relatively unexplored in existing research. The present study performed comprehensive metallurgical and manufactural investigations into the weldability of an Ni-based superalloy, CM247LC, from the viewpoint of the liquation cracking behavior and its susceptibility. Metallurgical solutions to suppress the liquation-cracking susceptibility were derived via the visualization-based Varestraint test, and the possibility of liquation crack-free welding was explored by employing pre-weld heat treatments and laser beam welding. The alloy that was subjected to aging treatment exhibited the lowest liquation-cracking susceptibility (liquation cracking temperature range: 66 K), while the as-cast alloy specimen exhibited the highest liquation-cracking susceptibility (liquation cracking temperature range: 620 K). The metallurgical mechanisms of the liquation cracking susceptibility of as-cast CM247LC weld were elucidated via microstructural analyses and thermodynamic calculations. The suppressed liquation cracking susceptibility of the aged CM247LC can be attributed to the MC-type carbide fraction and homogenized matrix phase, as compared with those of as-cast CM247LC. The aged CM247LC specimen was subjected to gas tungsten arc welding to validate its minimal liquation-cracking susceptibility. The results confirmed the suppression of liquation cracking, due to the low susceptibility of the specimen. However, crackfree welds could not be obtained. Finally, metallurgically sound welds without liquation cracks were successfully obtained via laser beam welding. The outcomes of the present study will facilitate the generation of electric power from fossil fuels via a clean and efficient gas turbine-based power generation cycle.

CM247LC 초내열합금 보수용접부 고온균열(2): 재용융에 따른 액화균열 민감도 변화

정예선,정진곤,김경민,이의종,이형수,서성문,천은준 대한용접·접합학회 2021 대한용접학회 특별강연 및 학술발표대회 개요집 Vol.2021 No.11

가스터빈 블레이드 소재로 검토되고 있는 CM247LC 합금은 MAR-M247 합금을 토대로 일부 성분을 조절하여 일방향 응고 주조성 및 고온 기계적 성질을 향상시킨 Ni계 초내열합금이다. 블레이드 제조 및 재생 과정에서 용접 공정은 필수적으로 고려되고 있다. Non-weldable 소재인 CM247LC 합금은 용접 시 고온균열(응고, 액화, 연성저하균열 등) 발생이 상당히 문제시되고 있어, 해당 용접부의 건전성을 고온균열 민감도 관점에서 면밀하게 검토할 필요가 있다. 본 연구에서는 블레이드 제조 및 재생(보수)용접, 두 관점에서 단층 및 다층 용접 열영향부의 액화균열 민감도를 기초적으로 검토하였고, 각 열영향부 균열 민감도 제어 핵심 인자에 대해 고찰하였다. 액화균열 민감도는 Spot-Varestraint 시험 및 다층 용접부에 적용 가능한 수정된 Multi-bead Varestraint 시험을 고안해 평가하였다. Varestraint 시험을 통해 형성된 액화균열은 IR 열화상카메라 측정을 통해 액화균열 발생 온도 범위(LCTR)로 정량화 하였다. 액화균열 발생부의 미세조직 분석은 후방산란전자회절(EBSD) 기법과 전자탐침미세분석기(EPMA)를 이용하였다. 단층 용접의 경우, 용접 전 열처리 적용에 따라 LCTR (주조재 620 K, 용체화 560 K 및 시효 열처리재 66 K)이 축소되지만, 다층 용접 시 LCTR(2nd pass 282 K, 3rd pass 805 K)은 재 확대되는 결과를 보였다. 미세조직 분석과 열역학적 계산(Thermo-Calc)을 통해, 본 결과는 열영향부의 MC 탄화물 분율과 공정 γ-γ’ 조직의 균질화 정도에 기인하는 것으로 판단되었다. 민감도 평가 결과는 실제 아크 및 레이저 용접부의 액화균열 발생 거동과 연계하여 검증함으로써, CM247LC 합금 블레이드 제조 및 재생(보수) 용접 가이드라인을 제시하고자 한다.

장면 기술을 위한 MPEG-4 기반 XMT API 구현

정예선,김규헌,기명석 한국방송공학회 2001 한국방송공학회 학술대회 Vol.1 No.1

Pre-weld Varestraint 시험을 이용한 CM247LC 초내열합금 보수용접부 액화균열 민감도 평가

정예선,정진곤,김세윤,배성환,이의종,이형수,서성문,천은준 대한금속·재료학회 2022 대한금속·재료학회지 Vol.60 No.4

In this study, the liquation cracking susceptibility in the heat-affected zone of CM247LC superalloy gas turbine blades during repair welding was quantitatively evaluated using a newly developed pre-weld Varestraint test method. The repair welding geometry was replicated through Varestraint tests for the preweld bead. The liquation cracking susceptibility, that is, the liquation cracking temperature range (LCTR), could be evaluated through temperature visualization at the time of crack formation during the Varestraint test. The LCTR of CM247LC alloy repair welds (heat-affected zone of the second layer weld) was 280 K. Compared to the LCTR of as-cast (620 K) and aged (65 K) CM247LC, metallurgical mechanisms for controlling the LCTR of repair welds were examined based on the microstructural characterization and Scheil’s solidification calculations for the pre-weld. The LCTR of the CM247LC alloy repair weld was influenced by the MC carbide fraction and the segregated concentration of trace and impurity elements, such as B and S in pre-weld solidification path. A process design capable of reducing the fraction of MC carbides and solidification segregation of trace impurity elements is required. Based on the experimental and theoretical results, the proposed modified Varestraint testing method for dissimilar welds is expected to analyze the solidification cracking behavior effectively in manufacturing high-soundness CM247LC superalloy welds.