열확산법으로 만든 CdTe p-n 다이오드의 특성에 관한 연구
채건식,김영국,설정식,전동성 慶南大學校 附設 基礎科學硏究所 1990 硏究論文集 Vol.2 No.-
Single crystals of CdTe were grown by Bridgman method from a melt. They were contained the element of 0.1, 0.15, 0.2mole % In and 0.1mole % P as a dopant respectively. The crystallographic direction of the grown CdTe have zinc blende structure which is(331) plane 2θ=62.6。 in X-ray method. The etch pits on the (100), (110) and (111) surfaces grown to characteristics shapes with E-Ag or PBr was found to consider with the crystallographic direction denoted by simple Miller indices as is depicted schematically. Here the pits on (100), (110) and (111) show rectangular, triangular and conical shapes respectively. The results of PL measurements of undoped and In-doped CdTe showed the maximum peak at 7475 Å and 7503 Å, and P-doped CdTe by thermal diffusion showed the maximum peak at 6943 Å and 7478 Å , the former was shown by Al and the later by phosphorous. The values of the electrical chracteristics have been compared with the Yamada's and we showed the good agreements between them. The thickness if Al thermal diffusion to the CdTe crystals were propotional to the diffusion time. The properties of these cells have good rectification with forward and reverse voltage.
개선된 Bridgman법으로 성장한 Bi₂Sr₂CaCu₂O_(8+δ) 單結晶의 초전도성
채건식,손인호,설정식,이수대,김영국,전동성,오재근,강성욱 경남대학교 환경문제연구소 1995 환경연구 Vol.17 No.-
The Bi₂Sr₂CaCu₂O_(8)+_(δ) single crystals are grown from the melt using a stoichiometric starting composition fer the cautions. The size and thickness of the Bi₂Sr₂CaCu₂O_(8)+_(δ) crystals depends on the cooling rate. The lower the cooling rate, the bigger and thicker the Bi₂Sr₂CaCu₂O_(8)+_(δ) crystals become. Bi₂Sr₂CaCu₂O_(8)+_(δ) X-ray diffraction(XRD) measurements of the single crystals were carried out using the radiation source of Cu Kα . In these Patterns only the (0,0,2n) diffraction appeared. The result indicated that the cleared surface of the single crystal was of the a-b face, and that the single crystal had a single phase without any undergrowth with 7K and 85K phases. In addition, although the figure is not shown, XRD patterns from (006) to (00□) were observed in the range of 2θ=0 to 60 degrees. The characterization of as-grown single crystals have been analyzed by Laue X-ray backsdattering along the c-axis and X-ray precession experiments. The result of magnetic moment vs Tc in 10 Gauss for a crystals were measurements indicated that the samples have a superconducting transition temperature of 85K.