Al5083-O MIG 용접부의 기공검사 및 비드형상에 관한 연구
이승용(Seung-Yong Lee),양훈승(Hoon-Seung Yang),정재강(Jae-Kang Chung) 대한기계학회 2001 대한기계학회 춘추학술대회 Vol.2001 No.9
The MIG welding properties according to the mixed shield GAS and the heat input was investigated with A15083-0 aluminium alloy commonly using the LNG tank. From the experiment, the higher He composition of the mixed shied GAS and heat input, the more increased bead width, depth, and area. The grade was evaluated by radiographic inspection that Ar33%+He67% specimens were shown Grade Ⅰ, Ar100%+He0% and Ar67%+He33% specimens were shown Grade Ⅱ for every heat input condition. And Ar50%+He50% specimens were shown Grade Ⅰ for middle heat input and Grade Ⅱ for low and high heat input.
-
Al5083-O 용접부의 보호가스 혼합비율에 따른 저온 인성 평가
이동길,이상열,양훈승,정재강 朝鮮大學校 機械技術硏究所 2002 機械技術硏究 Vol.5 No.1
본 연구에서는 저온용기 등에 많이 사용되고 있는 알루미늄 합금 A15083-O재에 대한 보호가스 혼합비율과 저온인성과의 관계를 규명하고자 혼합가스 비율을 여러 가지로 달리 하여 GMA 용접을 하였다. 시험온도는 상온에서 극저온까지 단계적으로 낮추어가며 계장화 샬피충격시험을 실시하였다. 최대하중은 시험온도가 낮아질수록 증가하였으나 변위는 25℃부터 -85℃까지는 시험온도에 관계가 없었으나 -196℃에서는 크게 감소하였으며, 모든 시험온도 및 불활성가스 혼합비율에서 흡수에너지는 용착금속부, 용융선 및 HAZ 순으로 증가하였다. 용착금속부의 흡수에너지는 시험온도 및 불활성가스 혼합비율에 관계없이 매우 낮게 나타난 반면, 용융선 및 HAZ시험편의 흡수에너지는 모재와 거의 유사한 값을 나타내었다. 또한, 모든 시험온도에서 흡수에너지는 He의 혼합량이 증가할수록 증가하는 경향을 보여 Ar33%+He67%에서 가장 우수한 인성을 나타내었다. In this study, the low temperature toughness was evaluated by using the instrumented Charpy impact testing procedures for A15083-O aluminum alloy used in the LNG carrying and storing tank. The specimens were GMA(Gas Metal Arc) welded with four different mixing shield gas ratios (Ar100% + He0%, Ar67%+He33%, Ar50%+He50%, and Ar33%+He67%), and tested at four different temperatures(+25, -30, -85, and -196℃) in order to investigate the influence of the mixing shielding gas ratio and the low temperature. The specimens were divided into base metal, weld metal, fusion line, and HAZ specimen according to the notch position. From experiment, the maximum load was increased a little up to -85℃, and the maximum load and maximum displacement were shown the highest and the lowest at -196℃ than the test temperatures because of the brittle behavior. The absorption energy of weld metal notched specimens was not nearly depends on test temperature and mixing shield gas ratio because the casting structure was formed in weld metal zone by melting welding wire. In the other hand, the others specimens was shown that the lower temperature, the higher absorption energy slightly up to -85℃ but the energy was decreased so much at -196℃.