순간금형가열법에 의해 제작된 ABS의 pH 변화에 따른 무전해 Ni 도금 특성
송태환,박소연,이종권,류근걸,이윤배,이미영 한국산학기술학회 2004 한국산학기술학회논문지 Vol.5 No.5
The MmSH is a process of injecting ABS to produce innovated physical properties compared to the conventional injection process. Physical properties such as thickness and adhesion strength of Ni plate electrolessly coated on a conventional and a MmSH injected ABS have been studied in the pH range 4-8. Thickness of the plate on the MmSH and the conventionally injected ABS appeared to be directly proportional to pH. The ABS processed by the conventional injection showed adhesion strength corresponded to ASTM 4B above pH 5. On the other hand, the ABS processed by the MmSH injection showed a superior adhesion strength corresponded to ASTM 5B above pH 6. It was calculated the shielding effectiveness of above 50 ㏈ in all conditions.
금속티타늄 분말로부터 고순도 $TiO_2$ 미분말 합성
조태환,송기세,이용민,송종택 한국세라믹학회 1993 한국세라믹학회지 Vol.30 No.3
In order to obtian TiO2 fine powder of high purity, the new method which is different from the sulfate process and the chloride one was employed. TiO2 was syntehsized by the reaction between elemental titanium particles and H2O2 solutiosn at 30~7$0^{\circ}C$, and then TiO2 powder was characterized using XRD, SEM, TEM, DTA and FT-IR. It was found that the initial reaction rate was fast at a high temperature due to the high generation of activated oxygen associated with thedecomposition of H2O2. However, the reaction was slowly proceeded at a low temperature due to slow decomposition of H2O2. In this experimental range, the optimum temeprature was ocnsidered to be about 5$0^{\circ}C$. The primary particles of the hydrous titanium dioxide (TiO2 gel) before aging were spherical, and their mean sizes were about 50nm. The similar shapes and sizes were observed with calcinatin at 40$0^{\circ}C$. The FT-IR spectrum of Ti-OH in the TiO2 gel powder appeared at around 3380cm-1, 1630cm-1 and 530cm-1. This gel powder was crystallized into the anatase type TiO2 at 300~40$0^{\circ}C$.
순간금형가열법에 의해 제작된 ABS의 pH 변화에 따른 무전해 Ni 도금 특성
송태환(Song Tae-Hwan),박소연(Park So-Yeon),이종권(Lee Jong-Kwon),류근걸(Ryoo Kunkul),이윤배(Lee Yoonbae) 한국산학기술학회 2004 한국산학기술학회 학술대회 Vol.- No.-
새로운 기술인 Momentary mold surface heating(MmSH)은 기존의 사출성형법으로 제조된 Acrylonitrile Butadiene Styrene(ABS)의 단점을 개선한 사출성형법이다. MmSH로 제조된 ABS와 기존의 사출성형법으로 제조된 ABS의 도금특성을 도금욕 pH 변화에 따라 연구하였다. Sodium hypophosphite가 첨가된 무전해 Ni 도금욕의 pH가 증가할수록 도금 두께가 증가하였고 기존의 사출성형법으로 제조원 ABS 의 경우 pH 5이상에서 4B의 밀착력올 가졌다. MmSH로 제조된 ABS 의 경우 pH 6이상에서 5B인 12.3N/25mm 이상의 가장 우수한 밀착력을 나타내였다.
무선부품을 위한 ABS의 무전해 Ni과 Ag 도금 특성
송태환(Song Tae-Hwan),박소연(Park So-Yeon),이종권(Lee Jong-Kwon),류근걸(Ryoo Kunkul),이윤배(Lee Yoonbae) 한국산학기술학회 2004 한국산학기술학회 학술대회 Vol.- No.-
순간금형가열방법(MmSH injection process)과 일반적인 방법으로 사출된 ABS 위에 전자파를 차폐하기 위한 무전해 Ni 과 Ag도금을 하였다. 무전해 Ni의 경우, 알칼리성 도금욕일수록 도금속도가 증가하였고 순간금형가열방법으로 사출된 ABS가 일반적인 방법으로 사출된 ABS 보다 밀착력, 광택, 전자파 차폐효율이 다소 높은 값을 가졌으며 pH 8에서 5B의 밀착력, 509의 광택도와 76dB의 전자파 차폐효과를 나타냈다.