TiO<sub>{2-x}</sub>N<sub>x</sub>의 저온제조 및 광화학적 특성
정동운,Jung, Dong-Woon 대한화학회 2010 대한화학회지 Vol.54 No.1
용액침전법에 의해 $TiO_2$ 및 $TiO_{2-x}N_x$를 제조하였다. $TiO_{2-x}N_x$ 시료는 순수한 $TiO_2$의 띠 간격인 3.20 eV (390 nm 흡광)로부터 1.77 eV (700 nm 흡광)까지 띠 간격이 줄어들게 되어 자외선 영역 뿐 아니라 가시광선 전체 영역에서도 흡광이 발생하였다. 가시광선에서의 광촉매 활성에서도 $TiO_{2-x}N_x$ 시료는 순수한 $TiO_2$ 및 P-25보다도 더 높은 활성도를 나타냈다. $TiO_2$ and N-substituted $TiO_{2-x}N_x$ were synthesized by using precipitation method. $TiO_{2-x}N_x$ compound absorbed whole UV light as well as long wavelength of visible light (400 - 700 nm) because of the change of band gap from 3.2 eV to 1.77 eV. Results obtained revealed that $TiO_{2-x}N_x$ showed higher activity than pure $TiO_2$ or P-25 for visible-photocatalytic degradation of 1,4-dichlorobenzene.
제올라이트 분말을 기본 재료로한 전기유변유체의 전기 및 유변학적 특성
정동운,최윤대,김상국,Jeong, Dong-Un,Choe, Yun-Dae,Kim, Sang-Guk 한국재료학회 1994 한국재료학회지 Vol.4 No.2
제올라이트 분말을 기본재료로 하는 전기유변유체의 전기 및 유변학적 특성이 연구되었다. 전기장 인가시 높은 한계응력을 얻기 위하여 비교적 유전상슈가 큰 5종류의 유전유체를 선택하여 제올라이트 분말과 혼합하여 전기유변유체를 준비하였다. Couette형 rheometer를 이용하여 유변유체의 한계응력을 인가된 전기장 및 온도의 함수로서 측정하였다. 이중 chlorinate hydrocabon oil과 제올라이트 분말을 혼합한 전기유변유체의 한계응력은 6KPa(E=4KV/mm, T=$25^{\circ}C$)로서 최대치를 기록하였다. 측정된 한계응력은 온도가 상승하면 점차 감소하는 반면 전류밀도는 온도에 따라 증가하였다. 전류밀도에 대한 Arrhenius 그라프에서 전기전도에 대한 활성화 에너지는 약 0.7eV였으며 이는 제올라이트 분말에 포함된 $Na^{+}$ 이온의 확산에 기인하는 것으로 분석되었다.
How are the Lower Lying Atoms Imaged Brighter than the Higher Lying Once in the STM Experiments?
정동운,Jeong, Dong Un Korean Chemical Society 2001 Bulletin of the Korean Chemical Society Vol.22 No.5
Unexpectedly, the brightest row was known to represents the lowest lying Te atoms in the STM image of NbTe2. Projected density of states and crystal orbital overlap population show that the 5pz orbital of the lowest lying Te(2) atom doe s not interact with the 4d orbital of Nb strongly so that the 5pz band remains in the vicinity of the Fermi energy. Consequently the lowest lying Te(2) atoms contribute higher electron density near the Fermi energy which in turn exhibits brightest image in the STM experiments.
The Application of TiO_2 Hollow Spheres on Dye-sensitized Solar Cells
정동운,H. J. Cho 대한화학회 2011 Bulletin of the Korean Chemical Society Vol.32 No.12
TiO_2 hollow spheres were fabricated by using SiO_2 as an inorganic template. Spherical SiO_2 particles were coated by TiO_2 through the nucleation process, and then the core SiO_2 part was eliminated by using HF solution. Finally, TiO_2 hollow spheres were obtained. The size of the TiO_2 hollow spheres was about 300-400nm and the thickness of the hollow wall was about 20-30 nm. The hollow has several holes whose diameters were within 100-200 nm. Dye-sensitized solar cells fabricated by using the TiO_2 hollow spheres were characterized. The solar conversion efficiency of the cell was 8.45% when TiO_2 hollow spheres were used as a scattering material, while it was 4.59% when TiO_2 hollow spheres were used as a normal electrode material.
정동운 대한화학회 2011 Bulletin of the Korean Chemical Society Vol.32 No.2
The traditional BCS superconductors AOs_2O_6 (A=K, Rb, and Cs) were investigated to find the relationship between their structures and superconducting transition temperatures. The T_c decreases with increasing the unit cell parameter of AOs_2O_6. This is in contrast to the case of conventional BCS superconductivity in a single bond model, where T_c may increase with increasing the the unit cell parameter since the DOS at Fermi level increases as the unit cell parameter increases. Instead, the T_c of a β-pyrochlore oxide is proportional to the lattice softness of the compound.