Kim, Joon-Ho,Yang, Sung-Sig,Hudson, Samuel M. 한국섬유공학회 2011 FIBERS AND POLYMERS Vol.12 No.6
A comparison of poly(trimethylene terephthalate)(PTT) and poly(ethlene terephthalate)(PET) fibers spun at various take-up speeds was presented. Fiber characterization included tensile and thermal properties, optical birefringence, density, sonic modulus, boil-off shrinkage, and wide-angle X-ray diffraction. The phenomenon of stress-induced crystallization was inferred from the X-ray diffraction diagrams for fibers spun with take-up speeds over 4000 m/min. The tenacity and elongation of PTT and PET fiber showed typical results, but the initial modulus of PTT fiber was nearly unchanged over the entire take-up speed range (2000-7000 m/min), whereas that of PET, as expected, increased monotonically with increasing take-up speed. This divergent behavior could be explained by the different molecular deformations in the c-axis as determined from X-ray diffraction patterns. The fiber crystallinity, density, and heat of fusion of both polymers increased with take-up speed. The boil-off shrinkage decreased with increasing take-up speed. The optical birefringence of the two fiber types showed a maximum level at a take-up speed of ca. 5000 m/min. The melting temperature behavior of PTT fiber was different from that of PET fibers. It was found that PTT is less sensitive to stress induced changes at high spinning speeds than is PET.
Chitosan-coated poly(vinyl alcohol) nanofibers for wound dressings
Kang, Yun Ok,Yoon, In-Soo,Lee, So Young,Kim, Dae-Duk,Lee, Seung Jin,Park, Won Ho,Hudson, Samuel M. Wiley Publishers 2010 JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B Vol.b92 No.2
<P>A PVA nanofibrous matrix was prepared by electrospinning an aqueous 10 wt % PVA solution. The mean diameter of the PVA nanofibers electrospun from the PVA aqueous solution was 240 nm. The water resistance of the as-spun PVA nanofibrous matrix was improved by physically crosslinking the PVA nanofibers by heat treatment at 150°C for 10 min, which were found to be the optimal heat treatment conditions determined from chemical and morphological considerations. In addition, the heat-treated PVA (H-PVA) nanofibrous matrix was coated with a chitosan solution to construct biomimetic nanofibrous wound dressings. The chitosan-coated PVA (C-PVA) nanofibrous matrix showed less hydrophilic and better tensile properties than the H-PVA nanofibrous matrix. The effect of the chitosan coating on open wound healing in a mouse was examined. The C-PVA and H-PVA nanofibrous matrices showed faster wound healing than the control. The histological examination and mechanical stability revealed the C-PVA nanofibrous matrix to be more effective as a wound-healing accelerator in the early stages of wound healing than the H-PVA nanofibrous matrix. © 2009 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2010</P>