양생조건에 따른 폴리머 시멘트 모르터의 내마모성에 관한 연구

조영국,소승영,Jo, Young-Kug,So, Seoung-Young 한국건축시공학회 2005 한국건축시공학회지 Vol.5 No.4

In recent years, polymer-modified mortars using polymer dispersions have been widely used as finish and repair materials in the construction industry because of their excellent properties compares to those of ordinary cement mortar. Especially, the adhesion improvement of ordinary cement mortar and concrete has attracted a great deal of attention from researchers, and several unique and simply applicable techniques for the adhesion improvement have been developed. The purpose of this study is to evaluate the abrasion resistance of polymer-modified mortar according various curing methods. The polymer-modified mortar are prepared with various polymer-cement ratios, and are subjected to three curing methods such as dry rure, standard cure and freezing and thawing cure after two curing methods, and then tested for abrasion. From the test results, the polymer-modified mortars with various polymer-cement ratios have some superior abrasion resistance compared with plain mortar. The abrasion resistance of polymer-modified mortars increase with an increase in the polymer-cement ratio, and is better under water cure than any other curing methods. It is concluded that the abrasion resistance of cement mortar is markedly improved by modifying of polymer dispersion.

폴리머 시멘트 복합체의 투수성 및 건조수축에 관한 연구

조영국,Jo, Young-Kug 한국건축시공학회 2009 한국건축시공학회지 Vol.9 No.5

시멘트 혼화용 폴리머 디스퍼션은 시멘트 모르타르 및 콘크리트 내부에서 폴리머 필림을 형성하여 각종 역학적성 질 및 내구성을 향상시킨다. 본 연구는 3종류의 폴리머 디스퍼션을 폴리머 시멘트비 0, 5, 10, 20%로 변환한 폴리머 시멘트 모르타르를 제작, 투수시험을 실시하여 투수성능을 실험하였으며, 더욱이 폴리머 시멘트 슬러리를 폴리머 시멘트 모르타르 표면에 도포하여 방수성능의 개선효과를 평가하였다. 또한 보통시멘트 콘크리트 표면에 폴리머 시멘트 슬러리를 도포하여 시멘트 콘크리트와 폴리머 시멘트 슬러리의 건조수축을 측정하였다. 그리고 기본적인 역학적 성상인 휨강도와 압축강도를 측정하여 보통 시멘트 모르타르와 비교 검토하였다. 연구결과, 폴리머 시멘트 모르타르는 보통 시멘트 모르타르에 비해 방수성능과 강도가 크게 개선되었으며, 폴리머 시멘트 슬러리의 건조수축은 시멘트 콘크리트에 비해 4-5배 크게 나타났다. 또한 향후 건조수축에 따른 접착성능의 영향성에 대한 연구가 진행되어야 할 것이다. In a range of forms, such as latex, water-soluble polymer, liquid resin, and monomer, polymer dispersions have been widely used in the construction industry as cement modifiers because of their excellent properties, such as acid-resistance, water-proofness, and good ductility in mortar and concrete. Polymer cement slurry (polymer-modified slurry) is made of cement and polymer dispersions, with a high polymer-cement ratio of 50% or more. The purpose of this study is to evaluate the water permeability and drying shrinkage of polymer cement mortar (polymer-modified mortar) and cement concrete coated by polymer cement slurry. The polymer cement mortar and cement concrete are prepared with various polymer types, polymer-cement ratios and curing methods, and are tested for water permeability, drying shrinkage and strength. The test results showed thatthe weight of permeable water of polymer cement mortar decreases with an increase in the polymer-cement ratio, reaching a minimum at the polymer-cement ratio of 20%. In particular, the weight of permeable water of St/BA-modified mortar with a polymer-cement ratio of 20% coated with St/BA-modified slurry is about 1/55 that of unmodified mortar. The EVA- and St/BA-modified slurries coated on cement concrete have about 4 or 5 times higher drying shrinkage compared to cement concrete. The strength of polymer cement mortars tends to increase with a higher polymer-cement ratio, and is considerably higher than that of unmodified mortar. It is thus concluded that polymer cement mortars coated by polymer cement slurry are effective for industrial application, and have superior properties such as waterproofness and strengths, compared with conventional cement mortar.

폴리머 디스퍼션을 이용한 강재의 내식성 평가에 관한 연구

조영국,Jo, Young-Kug 한국건축시공학회 2003 한국건축시공학회지 Vol.3 No.4

Reinforced concrete structures under sever conditions such as marine structures, bridges and structural constructed with aggregated(dredged front sea). can be deteriorated from corrosion of the reinforcing bars. The purpose of this study is to evaluate the corrosion reflectance of coated steel using polymer dispersion and polymer cement slurry. Polymer dispersion and polymer cement slurry with various polymer types were coated to the surface of bars and steel plate, and tested for accelerated corrosion tests. Tests include adhesion in tension, bending test, chloride ion spray, penetration of NaCl 10% solution and carbonation. From the test results, the corrosive resistance of steel is considerably improved by using polymer dispersion and polymer cement flurry at surface of steel. The difference of the corrosive resistance is hardly recognized according to types of polymer dispersion. The coated steel using polymer dispersion and polymer foment slurry will be improved to a great extent compared to those of plain steel when increasing content of chloride ion in cement concrete.

압축강도에 따른 수중불분리 콘크리트의 배합설계에 관한 연구

조영국,Jo, Young-Kug 한국건축시공학회 2003 한국건축시공학회지 Vol.3 No.3

At present, the antiwashout underwater concretes are used as popular construction materials in European countries, the United States and Japan. The water-soluble polymers in the antiwashout underwater concretes provide excellent segregation or washout resistance, self-compaction and self-leveling property to the concretes. The purpose of this study is to recommend to optimum mix proportions of antiwashout underwater concretes according to compressive strength of 300kgf/$\textrm{cm}^2$ to 500kgf/$\textrm{cm}^2$. The antiwashout underwater concretes are prepared with various unit cement content, unit water content, sand-aggregate ratio, unit antiwashout agent and superplasticizer content. And they are tested for flowability, and compressive strength. From the test results, it is possible to recommend the optimum mix proportions of antiwashout underwater concretes according to compressive strengths within the range of 300kgf/$\textrm{cm}^2$ to 500kgf/$\textrm{cm}^2$.

도장재의 양생재령과 도장두께가 PCS 도장철근과 시멘트 콘크리트와의 부착강도에 미치는 영향

조영국,Jo, Young-Kug 한국건축시공학회 2017 한국건축시공학회지 Vol.17 No.4

The purpose of this study is to evaluate the effect of curing age and thickness of coating material on the bond strength of polymer cement slurry(PCS)-coated rebar that can replace epoxy-coated rebar. The test specimens were prepared with two types of cement, two types of polymer dispersion as St/BA and EVA, two polymer-cement ratios, two coating thicknesses and three curing ages, and tested for bond strength test to cement concrete. The flexural behavior of RC beam that is made by optimum conditions such as polymer-cement ratio of 80%, coating thickness of $100{\mu}m$ and curing age of 7 days of PCS recommended from the bond strength test is also conducted. From the test results, The maximum bond strength of PCS-coated rebar at curing age of 7-day and coating thickness of $100{\mu}m$ was about 1.52 and 1.58 times respectively, the strength of plain and epoxy-coated rebar. The ultimate loads of RC beam using PCS-coated rebar were range of 81.1% to 102.3% of that of plain rebar, and 98.4% to 124.1% of that of epoxy-coated rebar. It is apparent that PCS-coated rebar with EVA, curing age at 7-day and $100{\mu}m$ can replace epoxy-coated rebar in construction field. 본 연구는 시멘트 종류, 폴리머 종류, 폴리머 시멘트비, 도장두께를 변화시켜 만든 PCS 도장철근의 시멘트 콘크리트에 대한 부착강도 시험을 실시하여 PCS 도장철근의 부착강도에 영향을 미치는 양생재령과 도장두께에 대하여 평가하고자 하였다. 또한 부착강도 시험결과로 얻어진 최적배합으로 만든 PCS 도장철근을 사용하여 철근콘크리트 보를 제작하여 휨 응력 시험을 실시하여 간접적으로 부착성을 평가하였다. 시험결과, PCS 도장철근의 부착강도는 양생재령 7일과 도장두께 $100{\mu}m$에서 최대치를 나타냈는데, 이는 보통 철근의 1.52배 및 에폭시 도장철근의 1.58배였다. 또한 PCS 도장철근을 사용한 철근콘크리트 보의 최대 파괴하중은 보통철근의 최대 파괴하중의 81.1%~102.3% 범위였으며, 에폭시 도장철근의 최대 파괴하중의 98.4%~124.1% 범위로 나타났다. 본 연구결과, 도장두께 $100{\mu}m$, 폴리머 종류 EVA, 폴리머 시멘트비 80%, 양생재령 7일 조건으로 만든 PCS 도장철근은 실제 건설현장의 철근콘크리트 구조물의 도장철근으로 활용할 수 있는 가능성을 확인하였다.

폴리머 시멘트 슬러리 도장철근의 부착강도에 미치는 도장재 배합과 도장두께의 영향

조영국,박동열,장길수,Jo, Young-Kug,Park, Dong-Yeol,Jang, Gil-Su 대한건축학회 2011 대한건축학회논문집 Vol.27 No.6

In general, polymer cement slurry(PCS) that is made from organic polymer dispersion and cement has good adhesion to steel and cement concrete, waterproofness and acid resistance due to being of polymer films formed in cement slurry. The purpose of this study is to evaluate the effects of the mix proportions and coating thickness on the bond strength of coated rebar by PCS. The test pieces are prepared with two types of polymer dispersions such as St/BA and EVA, four polymer-cement ratios, two types of cement and four types of coating thickness, and tested for the bond strength test. From the test results, bond strength of PCS-coated rebar with St/BA and EVA is better than that of plain rebar and epoxy-coated rebar. In general, it is also high bond strength at polymer-cement ratios of 80% or more, and coating thickness of $100{\mu}m$. The maximum bond strength of PCS-coated rebar with ultra high-early strength cement and St/BA at polymer-cement ratio of 80%, and coating thickness of $100{\mu}m$ is about 1.5 and 1.6 times respectively, the strength of plain rebar and epoxy-coated rebar. It is apparent that the choice of polymer type, cement type, polymer-cement ratio and coating thickness is important to improve the bond strength of PCS-coated rebar to cement concrete.

폴리머 콘크리트 오버레이의 수축응력에 관한 연구

조영국,소양섭,Jo, Young-Kug,Soh, Yang-Seob 한국콘크리트학회 1997 콘크리트학회지 Vol.9 No.4

폴리머 콘크리트를 오버레이 콘크리트로서 기존 시멘트 콘크리트 위에 타설할 경우 폴리머 콘크리트의 경화수축으로 말미암아 전단응력, 수직응력 및 축응력이 발생되며 이러한 응력은 폴리머 콘크리트와 기존 시멘트 콘크리트 사이의 접착성능에 영향을 미쳐 결국 역학적 성질 및 내구성이 저하될 수 있다. 오버레이 콘크리트의 수축응력은 본 실험에서 실시한 구속된 오버레이 콘크리트의 구속해제에 의한 수축변형량과 탄성계수로서 구할 수 있다. 본 연구에서는 폴리머 종류, 오버레이 콘크리트 두께, 양생시간과 온도에 따른 폴리머 콘크리트 및 폴리머 시멘트 콘크리트의 수축에 의한 축응력을 측정하여 폴리머 콘크리트를 각종 교량등의 오버레이 콘크리트로 사용하멩 있어서 기초적 자료를 제공하고자 하였다. 연구결과, 폴리머 콘크리트의 경화수축응력은 폴리머의 종류, 양생온도, 재령 및 두께에 의해 영향을 크게 받는 것으로 나타났다. The shrinkage of polymer concrete overlays to cement concrete causes interface shear, normal and axial stresses in the overlays. These can lead to deterioration of the polymer concrete overlays due to affection of adhesion polymer concrete and cement concrete. The shrinkage stress in the polymer concrete cause it to shorten and the shorting is measured: With the modulus of elasticity of the polymer concrete and strain known the stresses can be calculated. The purpose of this study is to provide the basic data of application of polymer concrete overlays such as bridge decks, highway and airport pavement repair and overlay materials. From the test results. It has been found that depending on the type polymer. overlay thickness, time after curing and temperature. the shrinkage stresses are eliminated by relaxation in time ranging from a few hours to a few days.

발포 폴리스티렌 수지를 수축저감제로 이용한 불포화 폴리에스테르 모르타르의 특성

조영국(Young-Kug JO),최낙운(Nak0Un CHOI),소양섭(Yang-Seob SOH) 한국콘크리트학회 2001 콘크리트학회논문집 Vol.13 No.1

플라이애쉬와 SBR을 혼입한 폴리머 시멘트 모르타르의 휨접착강도

조영국 ( Jo Young-kug ) 한국건축시공학회 2019 한국건축시공학회 학술발표대회 논문집 Vol.19 No.2

The purpose of this study is to evaluate the adhesion in flexure of SBR-modified mortar adding Fly Ash(FA). From the test results, the adhesion in flexure is seriously affected by polymer-binder ratios and adding content of FA. The maximum adhesion in flexure of SBR- modified mortar is about 1.46 times, the plain cement mortar. It is apparent that the adhesion in flexure of SBR-modified mortars by polymer-binder ratios is much more improved than that by adding contents of AF.

RC 구조물의 균열보수용 폴리머 시멘트 복합체의 인장강도와 신장률에 관한 연구

조영국 ( Jo Young-kug ),권우찬 ( Kwon Woo-chan ),박동엽 ( Park Dong-yeop ) 한국구조물진단유지관리공학회 2022 한국구조물진단유지관리공학회 학술발표대회 논문집 Vol.26 No.2

RC 구조물의 균열을 보수하는 재료는 거의 유기재료로 균열에 충전되어 빨리 경화된다는 장점으로 널리 사용되고 있다. 그러나 무기재료인 시멘트 콘크리트와의 열팽창계수가 달라 두 재료 사이의 장기 내구성에 대해 문제점이 제시되고 있다. 본 연구에서 사용하고자 하는 폴리머 시멘트 복합체는 시멘트 결합재에 폴리머 디스퍼션을 혼입하여 기존 시멘트계 재료의 접착성과 방수성능을 개선하였으며, 더욱이 균열 변형에 따른 추종성이 뛰어나 장기 내구성이 우수하다고 판단할 수 있다. 이러한 폴리머 시멘트 복합체의 기본적인 성능인 피막 자체의 인장강도와 더불어 인장에 따른 신장률을 폴리머 시멘트비, 피막 두께 및 폴리머 종류에 따라 시험을 실시하여 결과를 고찰하고자 하였다.