http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
황산용액에서 Al7075 합금 표면의 양극산화피막 형성거동
문성모(Sungmo Moon),양철남(Cheolnam Yang),나상조(Sangjo Na) 한국표면공학회 2014 한국표면공학회지 Vol.47 No.4
The present work is concerned with the formation behavior of anodic oxide films on Al7075 alloy under a galvanostatic condition in 20 vol.% sulfuric acid solution. The formation behaviour of anodic oxide films was studied by the analyses of voltage-time curves and observations of colors, morphologies and thicknesses of anodic films with anodization time. Hardness of the anodic oxide films was also measured with anodization time and at different positions in the anodic films. Six different stages were observed with anodiziation time : barrier layer formation (stage I), pore formation (stage II), growth of porous films (stage III), abnormal rapid oxide growth (stage IV), growth of non-uniform oxide films (stage V) and breakdown of the thick oxide films under high anodic voltages (stage VI). Hardness of the anodic oxide films appeared to decrease with increasing anodization time and with the position towards the outer surface. This work provides useful information about the thickness, uniformity, imperfections and hardness distribution of the anodic oxide films formed on Al7075 alloy in sulfuric acid solution.
Effects of Hydroxide and Silicate ions on the Plasma Electrolytic Oxidation of AZ31 Mg Alloy
Sungmo Moon(문성모),Cheolnam Yang(양철남),Sangjo Na(나상조) 한국표면공학회 2014 한국표면공학회지 Vol.47 No.4
Formation behavior of PEO (Plasma Electrolytic Oxidation) films on AZ31 Mg alloy was studied in aqueous solutions containing various concentrations of hydroxide ion (OH<SUP>?</SUP>) and silicate ion (SiO3<SUP>2?</SUP>) by voltage-time curves, and corrosion resistance of the PEO film-covered specimen was investigated by immersion test in 0.5 M NaCl solution. From the analyses of the voltage-time curves, it is suggested that two different types of anions are essentially needed for the formation of PEO films on AZ31 Mg alloy: film formation agent and local film breakdown agent. SiO3 <SUP>2?</SUP> ion acts only as a film formation agent but OH<SUP>-</SUP> ion acts not only as a film formation agent but also film breakdown agent. The PEO films prepared on AZ31 Mg alloy in alkaline silicate solution showed very good corrosion resistance without any pitting or filiform corrosions up to 480 h of immersion in 0.5 M NaCl.
주조용 Al-Si-Cu 알루미늄 합금의 기계가공 및 주조된 표면에서의 양극산화피막 형성
문성모(Sungmo Moon),남윤경(Yoonkyung Nam),양철남(Cheolnam Yang),정용수(Yongsoo Jeong) 한국표면공학회 2009 한국표면공학회지 Vol.42 No.6
The anodic oxidation behaviour of a cast component of AC2A Al alloy with machined surface and ascast surface was investigated in sulfuric acid solution. The anodized specimen showed relatively uniform and thick anodic oxide films on the as-cast surface, while non-uniform and very thin oxide films were formed on the machined surface. Non-anodized as-cast surface was observed to be covered with thick oxide scales and showed a number of second-phase particles containing Si, while non-anodized machined surface showed no oxide scales and relatively very small number of Si particles. Thus, the very limited growth of anodic oxide films on the as-cast surface was attributed to the presence of thick oxide scales and Si-containing second-phase particles on its surface.