http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
액장 소결한 $\beta-SiC-TiB_2$계 전도성 복합체의 특성
임승혁,신용덕,송준태,Yim, Seung-Hyuk,Shin, Yong-Deok,Song, Joon-Tae 대한전기학회 2000 전기학회논문지C Vol.52 No.10
The mechanical and electrical properties of the hot-pressed and annealed $\beta-SiC-TiB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of Al_2O_3+Y_2O_34. The result of phase analysis of composites by XRD revealed $\alpha-SIC(6H)\;TiB_2,\; and YAG(Al5Y3O12) crystal phase. The relative density and the mechanical properties of composites were increased with increasing $Al_2O_3+Y_2O_34 contents because YAG of reaction between $Al_2O_3\; and\; Y_2O_3$ was increased. The Flexural strength showed the highest value of 432.5MPa for composites added with 12wt% $Al_2O_3+Y_2O_34 additives at room temperature. Owing to crack deflection crack bridging phase transition and TAG of fracture toughness mechanism the fracture toughness showed 7.1MPa.m1/2 for composites added with 12wt% $Al_2O_3+Y_2O_34 additives at room temperature. The electrical resistivity and the resistance temperature coefficient showed the lowest of $6.0\times10-4\Omega.cm\; and\; 3.1\times10-3/^{\circ}C4 respectively for composite added with 12wt% \Omega additives at room temperature. The electrical resistivity of the composites was all positive temperature coefficient resistance (PTCR) in the temperature range of $25^{\circ}C\; to\; 700^{\circ}C$.
液狀 燒結에 의한 ${\beta}$-SIC TiB$_2$系 導電性 複合體의 特性(Ⅱ)
신용덕,임승혁,송준태,Shin, Yong-Deok,Yim Seung-Hyuk,Song Joon-Tae 대한전기학회 2001 전기학회논문지C Vol.50 No.6
The mechanical and electrical properties of the hot-pressed and annealed ${\beta}-SiC-TiB_2$, electroconductive ceramic composites were investigated as function as functions of the liquid forming additives of $Al_2O_3+Y_2O_3$. The result of phase analysis of composites by XRD revealed ${\alpha}$-SiC(6H), $TiB_2$,, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density and the mechanical properties of composites were increased with increasing $Al_2O_3+Y_2O_3$ contents in pressureless annealing method because YAG of reaction between $Al_2O_3$ was increased. The flexural strength showed the highest value of 458.9 MPa for composites added with 4 wt% $Al_2O_3+Y_2O_3$ additives in pressed annealing method at room temperature. Owing to crack deflection, crack bridging, phase transition and YAG of fracture toughness mechanism, the fracture toughness showed 7.1 MPa ${\cdot}\;m^{1/2}$ for composites added with 12 wt% $Al_2O_3+Y_2O_3$ additives in pressureless annealing method at room temperature. The electrical resistivity and the resistance temperature coefficient showed the lowest value of $6.0{\times}10^{-4}\;{\Omega}\;{\cdot}\;cm(25\'^{\circ}C}$ and $3.0{\times}10^{-3}/^{\circ}C$ for composite added with 12 wt% $Al_2O_3+Y_2O_3$ additives in pressureless annealing method at room temperature, respectively. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature ranges from 25 $^{\circ}C$ to 700 $^{\circ}C$.
Ru/$RuO_2$ 금속/산화물 이중전극 위에 증착한 PZT 박막의 전기적 특성
정규원,박영,송준태,Jeong, Kyu-Won,Park, Young,Song, Joon-Tae 한국전기전자재료학회 2001 전기전자재료학회논문지 Vol.14 No.4
PZT thin films (3500$\AA$) have been prepard on the Ru/Ru $O_2$ and Ru $O_2$ bottom electrodes with a RF magnetron sputtering system using P $b_{1.05}$(Z $r_{0.52}$, $Ti_{0.48}$) $O_3$ ceramic target. Ru/Ru $O_2$ bottom electrode was fabricated by in-situ processing controlled the $O_2$ partial pressure. The PZT thin films deposited on the Ru/Ru $O_2$ bottom electrode were preferred oriented (101) plane. The PZT thin films deposited on the Ru/Ru $O_2$ bottom electrodes showed better electrical properties than those with Ru $O_2$ bottom electrodes because Ru $O_2$ prevented oxygen vacancies and impurities from existing withing the interface and substrate.e.