전옥철,김윤준,류범영,최재곤,조병욱,홍진후 조선대학교 생산기술연구소 1999 生産技術硏究 Vol.21 No.1
A series of wholly aromatic polyesters with side chains were synthesized by solution polycondensation from 2,5-dialkoxyterephthaloyl chlorides with the corresponding diol. The polymers showed the schlieren textures which is indicative of a nematic phase above their melting temperature. The inherent viscosities (η_(inh)) measured at 35℃ in phenol/p-chlorophenol/1,1,2,2-tetrachloroethane were 0.56-0.98 dℓ/g. The glass transition temperature (T_(g)) and melting temperature (T_(m)) decreased with increasing the length of the alkoxy side chain. Initial decomposition temperatures in TGA occurred at 338 ~ 363℃ in N₂ gas and thermal stability of polymers decreased with increasing the length of the side chain.
조병욱,전옥철,김윤준,한철,최재곤 조선대학교 생산기술연구소 1999 生産技術硏究 Vol.21 No.2
A new thermotropic liquid crystalline copolyester(TLCP) was synthesized by condensation polymerization of 2,6-naphthalene dicarbonyl chloride with the corresponding diol having a tetramethylene and a hexarnethylene group. The blends of the TLCP with PEN were prepared by the coprecipitation from a common solvent. The TLCP and blends (2, 5, 10 and 20wt% TLCP) were characterized in terms of their thermal, mechanical properties and morphology. The TLCP in the melt state showed nematic mesophase identified by thread-like optical texture. The glass transition temperature (T_(g)) and cold crystallization temperature (T_(c)) of PEN in the blends decreased with increasing the content of TLCP and the TLCP acted as anucleating agent for the matrix polymer. Interfacial adhesion between the TLCP and PEN seemed to be poor. The modulus of TLCP/PEN blends was enhanced as the TLCP content increased.