Sputter-texttured Mo 박막이 CoCrTa/Cr 자기기록매체의 자기적 성질에 미치는 영향
조성묵(Jo Sung Mook),남인탁(Nam In Tak) 강원대학교 산업기술연구소 2001 産業技術硏究 Vol.21 No.1
The effect of Mo underlayer on the magnetic properties of CoCrTa/Cr films deposited on glass substrates were investigated. The coercivity increased and the coercivity squareness decreased by introducing Mo underlayer. The coercivity increase was attributed to the increase of in-plane c-axis orientation and magnetic isolation of Co grains deposited on Cr/Mo underlayer. The decrease of coercivity squarenesses seemed to be caused by the increase of magnetic isolation. The increase of magnetic isolation of Co grains was attributed to the diffusion of Mo atoms into grain boundaries of Co films and the physical isolation of Co grains. The coercivity of CoCrTa/Cr/Mo showed maximum values at Mo thickness of 400Å. The appearance of the maximum coercivity at that thickness was attributed to the development of strong Co(1010) and Co(1011) preferred orientation.
-
길상형,이효영,박광열,조경남,백승주,황교민,조성묵,최재혁,Kil, Sang-Hyeong,LEE, Hyo-Yeong,Park, Kwang-Yeol,Jo, Kyung-Nam,Baek, Seung-Jo,Hwang, Kyo-Min,Cho, Seong-Mook,Choi, Jae-Hyeok 대한핵의학기술학회 2014 핵의학 기술 Vol.18 No.1
본 연구의 목적은 고용량 방사성요오드($^{131}I$) 치료 시 완하제(laxatives) 투여가 체내에 불필요한 방사능을 줄이는데 유용한지 알아보고자 하였다. 입원환자 20명(남:여=6:14, 나이 $46.3{\pm}8.1$세)을 대상으로 $^{131}I$ 5,550 MBq을 복용 한 그룹(Group 1)과 $^{131}I$ 5,550 MBq을 복용한 후 16시간 뒤에 완하제(laxatives)를 투여한 그룹(Group 2)으로 나누었다. 16시간, 40시간 후에 감마카메라(Symbia E, Siemens, USA)를 이용하여 전신스캔 하였으며, 위장관부(Gastro-intestinal tract, GI)와 대퇴부(thigh)에 관심영역(region of interest, ROI)을 설정하여 위 장관의 계수 감소율(reduction ratio)를 구하였다. 일정 시간 간격으로 측정기기(RadEye-G10, Thermo Fisher Scientific, USA)를 이용하여 환자로부터 1 m 거리에서 공간선량률(Spatial dose rate)을 측정한 후, Origin 8.5.1 software를 이용하여 그래프로 나타내었다. 완하제(laxatives) 투여에 따른 두 그룹 간 차이는 독립표본 T검정(Independent samples t-test)을 하였다. 방사성요오드($^{131}I$) 복용 후 16시간 $^{131}I$ 전신영상검사에서 위 장관 계수(count)치는 그룹 1은 $2,825{\pm}337$, 그룹 2는 $2,792{\pm}198$였으며(P>0.05), 40시간 $^{131}I$ 전신영상검사에서 그룹 1의 위 장관 계수(count) 치는 $1,623{\pm}179$, 그룹 2의 위 장관 계수(count)치는 $778{\pm}188$였다(P<0.05). 위 장관내 계수 감소율은 그룹 1은 $42.1{\pm}6.3%$, 그룹 2는 $71.2{\pm}7.7%$였다. 일정 시간 간격으로 공간선량률(spatial dose rate)을 측정하여 비교 분석한 결과 완하제(Laxatives)를 투여하기 전에는 두 그룹 간 유의한 차이가 없었으며(P>0.05), 완하제(laxatives) 투여 4시간 후 부터 두 그룹 간 유의한 차이가 있었다(P<0.05). 퇴원 시 측정한 공간선량률(spatial dose rate)은 그룹 1은 $23.8{\pm}6.7{\mu}Sv/h$, 그룹 2는 $8.2{\pm}2.4{\mu}Sv/h$로 완하제(laxatives)를 병용 투여한 환자에서 체내에 남아있는 방사능이 많이 줄어들었다. 완하제(laxatives) 병용 투여는 위 장관에 남아 있는 방사성요오드 ($^{131}I$)의 배출을 원활히 하여 환자의 체내 방사능량을 크게 낮출 수 있었으며 퇴원 시 방사선량률을 효과적으로 낮출 수 있었다. 따라서 퇴원 후 가족 또는 환자 주변의 일반인에 대한 불필요한 방사선 피폭을 줄 일수 있을 것이다. 또한 방사성요오드($^{131}I$)의 생물학적 반감기를 단축시킬 수 있어 환자의 체내에 방사능량이 법적 선량 이하가 되는 시간이 단축되어 효율적인 병실 운영과 관리가 가능하리라 기대 된다. Purpose: Our goals were to evaluate the effect of high dose radioiodine treatment for thyroid cancer by taking in laxatives. Materials and Methods: Twenty patients(M:F=13:7, age $46.3{\pm}8.1\;yrs$) who underwent high dose radioiodine treatment were seperated into Group 1 taking $^{131}I$ 5,500 MBq and Group 2 with the use of laxatives after taking $^{131}I$ 5,500 MBq. The whole body was scanned 16 hours and 40 hours after taking radioactive iodines by using gamma camera, the ROIs were drawn on the gastro-intestinal tract and thigh for calculation of reduction ratio. At particular time during hospitalization, the radioactivity remaining in the body was measured in 1 meter from patient by using survey meter (RadEye-G10, Thermo Fisher Scientific, USA). Schematic presentation of an Origin 8.5.1 software was used for spatial dose rate. Statistical comparison between groups were done using independent samples t-test. P value less than 0.05 was regarded as statistically significant. Results: The reduction ratio in gastro-intestinal 16 hours and 40 hours after taking laxatives is $42.1{\pm}6.3%$ in Group 1 and $72.1{\pm}6.4%$ in Group 2. The spatial dose rate measured when discharging from hospital was $23.8{\pm}6.7{\mu}Sv/h$ in Group 1 and $8.2{\pm}2.4{\mu}Sv/h$ in Group 2. The radioactivity remaining in the body is much decreased at the patient with laxatives(P<0.05). Conclusion: The use in combination with laxatives is helpful for decreasing radioactivity remaining in the body. The radioactive contamination could be decreased at marginal individuals from patients.
-
Sputter-texttured Mo 박막이 CoCrTa/Cr 자기기록매체의 자기적 성질에 미치는 영향
조성묵,남인탁 江原大學校 産業技術硏究所 2001 産業技術硏究 Vol.21 No.A
The effect of Mo underlayer on the magnetic properties of CoCrTa/Cr films deposited on glass substrates were investigated. The coercivity increased and the coercivity squareness decreased by introducing Mo underlayer. The coercivity increase was attributed to the increase of in-plane c-axis orientation and magnetic isolation of Co grains deposited on Cr/Mo underlayer. The decrease of coercivity squarenesses seemed to be caused by the increase of magnetic isolation. The increase of magnetic isolation of Co grains was attributed to the diffusion of Mo atoms into Brain boundaries of Co films and the physical isolation of Co grains. The coerciyity of CoCrTa/Cr/Mo showed maximum values at Mo thickness of 400Å. The appearance of the maximum coercivity at that thickness was attributed to the development of strong Co(10□ Θ) and Co(10□ 1) preferred orientation.
-
남인탁,김동현,조성묵 강원대학교 부설 석재복합신소재 제품연구센터 1999 석재연 논문집 Vol.4 No.-
본 연구에서는 RF/DC 마그네트론 스퍼터링 시스템을 이용 실리카(SiO₂) 박막을 제조하였다. 상온과 250℃의 기판온도에서 O₂ 가스의 분압을 변화시키며 박막을 제조한 후 물리적, 화학적 특성들에 대하여 알아보았다. 250℃에서 증착한 시편의 경우에는 O₂의 유입량이 증가됨에 따라 박막의 증착속도가 증가하였으며, AFM를 이용해 표면을 살펴 본 결과 부드러운 표면이 관찰되었음을 알 수 있었다. 또한, 흘려주는 O₂ 가스의 양을 증가시키며 증착을 하였을 경우에 SiO₂의 피크의 높이와 결합에너지의 값이 증가되었음을 FT―IR 및 ESCA를 이용해 확인할 수 있었다. In this paper, we study the growth of silicon oxide(SiO₂) films. Silicon oxide film layers have been fabricated by RF/DC magnetron sputtering method and examine characteristics of the grown films. The composition of these layers fabricated at varying oxygen injections and substrate temperatures. While the oxygen injection and substrate temperature increased, the oxygen content in these film layers increased considerably. The ESCA and FT-IR analysis prove the silica(SiO₂) thin film layer. The deposition rate depend upon the O₂/Ar ratio and substrate temperature. The binding energy and intensity of Si-O-Si increased with O₂ flow. The results of the study can apply as basic study for development of high ability insulator.