http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
친환경 전통미장재료를 혼입한 사벽용 벽체의 내구성 평가
료효개 ( Liao Xiao-kai ),김동훈 ( Kim Dong-hun ),임남기 ( Lim Nam-gi ) 한국구조물진단유지관리공학회 2017 한국구조물진단유지관리공학회 학술발표대회 논문집 Vol.21 No.1
The In the experiment on flow using sand walls, when white clay + sand was mixed with glutinous rice, traditional paper and seaweed as adherents and preventive measures for cracks, the flow was higher than other sand wall mortars. This indicates that it is effective in improving flow. Moreover, in terms of strength, a mix of white clay+ sand, traditional paper and flour had a greater strength than a mix of white clay + sand, straws and flour. In the experiment to test for cracks and shrinking during drying, a composition of white clay + sand + traditional paper showed fewer cracks and less shrinking than the walls where straws were mixed in.
공동충전재로써 각종 산업부산물을 활용한 CLSM의 현장적용 가능성 평가
료효개(Xiao-kai Liao),김동훈(Dong-Hun Kim) 한국건설순환자원학회 2020 한국건설순환자원학회 논문집 Vol.8 No.4
본 연구에서는 다량의 산업부산물 및 폐기물을 안전하게 유효 활용할 수 있는 CLSM의 기초적 물성시험을 통해 FA 및 잔골재의 대체 재료로써 GBFS 및 FNS, FGB의 적용가능성을 검토하였다. 나아가, 도로 및 노면하부, 포토홀 등의 공동충전재로서의 현장적용 가능성에 대해서도 검토하여 다음과 같은 결론을 얻었다. 첫째, GBFS 및 FNS, FGB를 활용한 CLSM의 경우 GBFS 및 FNS는 각각 30% 이상, FGB는 5% 이내에서 적정 혼합하면 현장적용을 위한 유동성 개선에 유효한 것으로 나타났다. 둘째, GF15B5는 Base 대비 동등 정도의 블리딩율이 GF30B5는 Base 대비 0.17% 정도 블리딩을 억제할 수 있는 것으로 나타났다. 또한, Base 대비 GF15는 0.2%, GF30 및 GF45는 각각 0.26% 및 0.3% 정도 블리딩을 억제할 수 있는 것으로 확인되었다. 셋째, GF15B5 및 GF30B5 모두 7일 강도가 0.4MPa을 초과하여 현장적용을 만족하였고 또한, 초기강도의 증가비율이 Base 대비 각각 323% 및 233% 높게 나타나는 것으로 파악되었다. 또한, GF의 경우도 현장적용을 위한 7일 강도가 0.2MPa 이상을 모두 만족하였고 Base 대비 GF15는 160%, GF30 및 GF45는 각각 237% 및 185% 정도의 높은 강도증가비율이 확인되었다. 넷째, GBFS 및 FNS, FGB를 복합적으로 활용한 CLSM의 경우 Cr의 농도가 비교적 높게 용출되는 것으로 파악되어 대량의 지하수 및 침투수가 유입되는 환경하에서는 Cr의 용출에 의한 환경적 안전성 검토가 이루어져야 할 것으로 판단된다. In this research, a physical property test of CLSM, which can safely and effectively utilize a great number of industrial byproducts and waste types, was used to review the applicability of GBFS, FNS, and FGB, as well as their field applicabilities as cavity fillers, and the following conclusions have been reached. first, For CLSM utilizing GBFS, FNS, and FGB, it was revealed that a proper mixing of over 30% of GBFS and FNS or within 5% of FGB is effective in improving the fluidity for field application. second, It was revealed that GF15B5 can suppress bleeding at a similar level as the base, whereas GF30B5 can do so at about 0.17% compared to the base. It was also verified that GF15, GF30, and GF45 can suppress bleeding at about 0.2%, 0.26%, and 0.3%, respectively, compared to the base. third, Both GF15B5 and GF30B5 exceeded 0.4MPa in 7day strength tests to satisfy the field application and, also, the rates of increase of their initial strengths were found to be 323% and 233% higher than the base, respectively. Meanwhile, the 7day strength test of GF, which utilizes GBFS and FNS, also reached over 0.2MPa for field application, and it was revealed that GF15, GF30, and GF45 show 160%, 237%, and 185% higher strength increase rates, respectively, compared to the base.
친환경 미장재료로서 사벽재료를 혼입한 모르타르 및 벽체의 기초적 물성
료효개 ( Liao Xiao-kai ),김동훈 ( Kim Dong-hun ),임남기 ( Lim Nam-gi ) 한국건축시공학회 2017 한국건축시공학회 학술발표대회 논문집 Vol.17 No.1
The In the experiment on flow using sand walls, when white clay+sand was mixed with glutinous rice, traditional paper and seaweed as adherents and preventive measures for cracks, the flow was higher than other sand wall mortars. This indicates that it is effective in improving flow. Moreover, in terms of strength, a mix of white clay+sand, traditional paper and flour had a greater strength than a mix of white clay+sand, straws and flour. In the experiment to test for cracks and shrinking during drying, a composition of white clay+sand+traditional paper showed fewer cracks and less shrinking than the walls where straws were mixed in.