저진공 축전 결합형 BCl<sub>3</sub>/N<sub>2</sub> 플라즈마를 이용한 GaAs의 건식 식각
김재권,박주홍,이성현,노호섭,주영우,박연현,김태진,이제원,Kim, Jae-Kwon,Park, Ju-Hong,Lee, Sung-Hyun,Noh, Ho-Seob,Joo, Young-Woo,Park, Yeon-Hyun,Kim, Tae-Jin,Lee, Je-Won 한국재료학회 2009 한국재료학회지 Vol.19 No.3
This study investigates GaAs dry etching in capacitively coupled $BCl_3/N_2$ plasma at a low vacuum pressure (>100 mTorr). The applied etch process parameters were a RIE chuck power ranging from $100{\sim}200W$ on the electrodes and a $N_2$ composition ranging from $0{\sim}100%$ in $BCl_3/N_2$ plasma mixtures. After the etch process, the etch rates, RMS roughness and etch selectivity of the GaAs over a photoresist was investigated. Surface profilometry and field emission-scanning electron microscopy were used to analyze the etch characteristics of the GaAs substrate. It was found that the highest etch rate of GaAs was $0.4{\mu}m/min$ at a 20 % $N_2$ composition in $BCl_3/N_2$ (i.e., 16 sccm $BCl_3/4$ sccm $N_2$). It was also noted that the etch rate of GaAs was $0.22{\mu}m/min$ at 20 sccm $BCl_3$ (100 % $BCl_3$). Therefore, there was a clear catalytic effect of $N_2$ during the $BCl_3/N_2$ plasma etching process. The RMS roughness of GaAs after etching was very low (${\sim}3nm$) when the percentage of $N_2$ was 20 %. However, the surface roughness became rougher with higher percentages of $N_2$.
박연현,주영우,김재권,노호섭,이제원,Park, Yeon-Hyun,Joo, Young-Woo,Kim, Jae-Kwon,Noh, Ho-Seob,Lee, Je-Won 한국재료학회 2009 한국재료학회지 Vol.19 No.2
This study investigated dry etching of acrylic in capacitively coupled $SF_6$, $SF_6/O_2$ and $SF_6/CH_4$ plasma under a low vacuum pressure. The process pressure was 100 mTorr and the total gas flow rate was fixed at 10 sccm. The process variables were the RIE chuck power and the plasma gas composition. The RIE chuck power varied in the range of $25{\sim}150\;W$. $SF_6/O_2$ plasma produced higher etch rates of acrylic than pure $SF_6$ and $O_2$ at a fixed total flow rate. 5 sccm $SF_6$/5 sccm $O_2$ provided $0.11{\mu}m$/min and $1.16{\mu}m$/min at 25W and 150W RIE of chuck power, respectively. The results were nearly 2.9 times higher compared to those at pure $SF_6$ plasma etching. Additionally, mixed plasma of $SF_6/CH_4$ reduced the etch rate of acrylic. 5 sccm $SF_6$/5 sccm $CH_4$ plasma resulted in $0.02{\mu}m$/min and $0.07{\mu}m$/min at 25W and 150W RIE of chuck power. The etch selectivity of acrylic to photoresist was higher in $SF_6/O_2$ plasma than in pure $SF_6$ or $SF_6/CH_4$ plasma. The maximum RMS roughness (7.6 nm) of an etched acrylic surface was found to be 50% $O_2$ in $SF_6/O_2$ plasma. Besides the process regime, the RMS roughness of acrylic was approximately $3{\sim}4\;nm$ at different percentages of $O_2$ with a chuck power of 100W RIE in $SF_6/O_2$ plasma etching.