http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Nwe Ni Tun,Hee Seung Yang,Jong Min Yu,윤기봉 대한기계학회 2016 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.30 No.12
Creep crack growth at elevated temperatures is a critical consideration in estimating the remaining life of high temperature structural components and in deciding their inspection interval. In this study, creep crack growth analyses for external radial-axial and internal radial-circumferential surface cracks in a pressurized cylinder were conducted by an analytical method. The effect of crack depth and crack length on the variations in C t and remaining life predictions were investigated for surface cracks with various initial aspect ratios. It was observed that the remaining life of an internal radial-circumferential surface crack was approximately 53 times longer than that of an external radial-axial surface crack for the same crack size and loading conditions with 316 stainless steel material. It was also observed that the variations in remaining life, crack propagations, and the C t values were considerably sensitive to the crack location and crack depth. Convergence of crack aspect ratio was not observed when the crack depth ratio was increased. Since the method is independent of material properties and location of the crack geometries, it can be extended to various material properties and various locations of the surface crack geometries.
Effects of Defect Size on Crush Test Load of Butt Fusion Welded MDPE Pipes
Tun, Nwe Ni,Lai, Huan Sheng,Jeon, Gyu Min,Yoon, Kee Bong,Kil, Seong Hee The Korean Society for Energy 2015 에너지공학 Vol.24 No.4
It is expected that the size of welding defect affects the mechanical performance of welded medium density polyethylene (MDPE) pipe joints. In this study, butt fusion welded MDPE pipe joints with a single spherical or planar defect of various sizes were studied using experimental crush testing and also by finite element method. The crush test showed that the mechanical performance of crush was not affected by the size and geometry of a single welding defect when the defect size was increased to 45% of the pipe's wall thickness. The simulation results indicated that the effect of the single welding defect on the Von Mises stress distribution near the defect explained the reason of the test results.
Effect of defects on the burst failure of butt fusion welded polyethylene pipes
Huan Sheng Lai,Nwe Ni Tun,Seong Hee Kil,윤기봉 대한기계학회 2016 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.30 No.5
With the increasing demand of Medium density polyethylene (MDPE) pipes for gas transmission, the safety concern related with welding defects is becoming a serious matter. In this paper, experimental burst tests and finite element analyses were employed to study butt fusion welded MDPE pipe joints with spherical and planar defects of various sizes. These defects were used to simulate lack of bonding during the welding. Test results showed that in all pipe test cases, the failure location originated from pipe substrates, even though the defect size was increased to 45% of the pipe’s wall thickness. The burst pressure could be estimated by the expression employed in the ASME BPVC, and in the burst pressure, the hoop stress was 20.28 MPa. Simulation results showed that the failure position was not only affected by the defect size, but also by the welding bead. It can be argued that a single welding defect whose maximum size is smaller than 15% of the thickness can be used without failure during short-term usage, even when there is no welding bead in the welded joint.