Muhammad Nabeel,Muhammad Ali Nasir,Mariyam Sattar,Rizwan Ahmed Malik,Meshal Alzaid,Muhammad Shoaib Butt,Mohsin Saleem,Hussein Alrobei 대한기계학회 2020 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.34 No.11
Flexural, tensile, and impact strength of hybrid Kevlar/glass reinforced epoxy composite is studied. Six different types of hybrid composite material were manufactured by hand layup process using different compositions of Kevlar and glass fiber. Tensile, flexural and impact strengths of manufactured samples were investigated using standard tests and compared. It is observed that tensile strength is greater for combinations with higher percentage (%) of Kevlar fabric and decreases with an increase in the glass fabric %age. Flexural strength is higher for combinations with greater %age of glass fabric and decreases with an increase in the Kevlar fabric %age. From drop weight test, it is found from visual inspection that damaged area is increased with an increase in the glass fabric percentage. Numerical simulation model incorporated with elastoplastic material data successfully predicts tensile and flexural experimental results.
Corrosion and wear behavior of TiN PVD coated 304 stainless-steel
Awais Awan,Riffat Asim Pasha,Muhammad Shoaib Butt,Rizwan Ahmed Malik,Ibrahim M Alarifi,Meshal Alzaid,무하마드 라티프,Ammar Naseer,Mohsin Saleem,Hussein Alrobei 대한기계학회 2020 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.34 No.8
Ti/TiN multilayered physical vapor deposition (PVD) coatings were deposited on stainless-steel by cathodic arc deposition method. Bare sample of stainless steel 304 was compared with monolithic TiN coating and TiN coating having 2, 4, 6 and 8 Ti interlayers. The properties like corrosion and wear resistance were studied and analyzed comparatively. Potentiodynamic polarization curves showed that highest corrosion resistance was indicated by TiN coating with 8 Ti interlayers. Sample having 8 Ti interlayers have high corrosion potential (E corr ) and low corrosion current density (I corr ) as compared to other samples. This may be attributed to the arrangement of interlayers that prevents the corrosive agents to penetrate surface. All multilayered coatings show better results than the substrate material. Pin on disk wear test revealed that coating having monolithic TiN layer have the lowest coefficient of friction and consequently have less wear volume and wear rate as compared to other coatings with Ti interlayers. These results made the investigated coated stainless steel 304 valuable for wide range of industrial applications that required wear and corrosion resistance.