Evaluation of C. Albicans and S. Mutans adherence on different provisional crown materials

Gulsum Sayin Ozel,Mehmet Burak Guneser,Ozgur Inan,Ayce Unverdi Eldeniz 대한치과보철학회 2017 The Journal of Advanced Prosthodontics Vol.9 No.5

PURPOSE. Bacterial adhesion on provisional crown materials retained for a long time can influence the duration for which permanent prosthetic restorations can be healthily worn in the oral cavity. The aim of this study was to compare seven different commonly used provisional crown materials with regard to Streptococcus mutans and Candida albicans surface adhesion. MATERIALS AND METHODS. For each group, twenty specimens of the provisional fixed prosthodontic materials TemDent (Schütz), Imıdent (Imıcryl), Tab 2000 (Kerr), Structur Premium (Voco), Systemp (Ivoclar Vivadent), Acrytemp (Zhermack), and Takilon-BBF (Takilon) were prepared (diameter, 10.0 mm; height, 2.0 mm). Surface roughness was assessed by atomic force microscopy. Each group was then divided into 2 subgroups (n=10) according to the microbial suspensions used: S. mutans and C. albicans. The specimens were incubated at 37°C with S. mutans or C. albicans for seven days. Bacterial adherence on surfaces was assessed using the 2,3-bis[2-methyloxy-4-nitro-5-sulfophenyl]-2H-tetrazolium-5-carboxanilide (XTT) assay. RESULTS. S. mutans showed maximum adhesion to Structur, followed by Systemp, Acrytemp, Takilon, Tab 2000, Imident, and TemDent (P<.05). The highest vital C. albicans adhesion was noted on Takilon, followed by Imident and Tab 2000; the lowest adhesion was noted on Systemp (P<.05). CONCLUSION. The materials showed significant differences in the degree of bacterial adhesion. C. albicans showed higher surface adhesion than S. mutans on provisional crown and fixed partial denture denture materials.

Evaluation of C. Albicans and S. Mutans adherence on different provisional crown materials

Ozel, Gulsum Sayin,Guneser, Mehmet Burak,Inan, Ozgur,Eldeniz, Ayce Unverdi The Korean Academy of Prosthodonitics 2017 The Journal of Advanced Prosthodontics Vol.9 No.5

PURPOSE. Bacterial adhesion on provisional crown materials retained for a long time can influence the duration for which permanent prosthetic restorations can be healthily worn in the oral cavity. The aim of this study was to compare seven different commonly used provisional crown materials with regard to Streptococcus mutans and Candida albicans surface adhesion. MATERIALS AND METHODS. For each group, twenty specimens of the provisional fixed prosthodontic materials TemDent ($Sch{\ddot{u}}tz$), Imident (Imicryl), Tab 2000 (Kerr), Structur Premium (Voco), Systemp (Ivoclar Vivadent), Acrytemp (Zhermack), and Takilon-BBF (Takilon) were prepared (diameter, 10.0 mm; height, 2.0 mm). Surface roughness was assessed by atomic force microscopy. Each group was then divided into 2 subgroups (n=10) according to the microbial suspensions used: S. mutans and C. albicans. The specimens were incubated at $37^{\circ}C$ with S. mutans or C. albicans for seven days. Bacterial adherence on surfaces was assessed using the 2,3-bis[2-methyloxy-4-nitro-5-sulfophenyl]-2H-tetrazolium-5-carboxanilide (XTT) assay. RESULTS. S. mutans showed maximum adhesion to Structur, followed by Systemp, Acrytemp, Takilon, Tab 2000, Imident, and TemDent (P<.05). The highest vital C. albicans adhesion was noted on Takilon, followed by Imident and Tab 2000; the lowest adhesion was noted on Systemp (P<.05). CONCLUSION. The materials showed significant differences in the degree of bacterial adhesion. C. albicans showed higher surface adhesion than S. mutans on provisional crown and fixed partial denture denture materials.

In vitro study of fracture strength of provisional crown materials

Karaokutan, Isil,Sayin, Gulsum,Kara, Ozlem The Korean Academy of Prosthodonitics 2015 The Journal of Advanced Prosthodontics Vol.7 No.1

PURPOSE. The purpose of this report was to evaluate the effect of the fabrication method and material type on the fracture strength of provisional crowns. MATERIALS AND METHODS. A master model with one crown (maxillary left second premolar) was manufactured from Cr-Co alloy. The master model was scanned, and the data set was transferred to a CAD/CAM unit (Yenamak D50, Yenadent Ltd, Istanbul, Turkey) for the Cercon Base group. For the other groups, temporary crowns were produced by direct fabrication methods (Imident, Temdent, Structur Premium, Takilon, Systemp c&b II, and Acrytemp). The specimens were subjected to water storage at $37^{\circ}C$ for 24 hours, and then they were thermocycled (TC, $5000{\times}$, $5-55^{\circ}C$) (n=10). The maximum force at fracture (Fmax) was measured in a universal test machine at 1 mm/min. Data was analyzed by non-parametric statistics (${\alpha}$=.05). RESULTS. Fmax values varied between 711.09-1392.1 N. In the PMMA groups, Takilon showed the lowest values (711.09 N), and Cercon Base showed the highest values (959.59 N). In the composite groups, Structur Premium showed the highest values (1392.1 N), and Acrytemp showed the lowest values (910.05 N). The composite groups showed significantly higher values than the PMMA groups (P=.01). CONCLUSION. Composite-based materials showed significantly higher fracture strengths than PMMA-based materials. The CADCAM technique offers more advantages than the direct technique.

In vitro study of fracture strength of provisional crown materials

Isil Karaokutan,Gulsum Sayin,Ozlem Kara 대한치과보철학회 2015 The Journal of Advanced Prosthodontics Vol.7 No.1

PURPOSE The purpose of this report was to evaluate the effect of the fabrication method and material type on the fracture strength of provisional crowns. MATERIALS AND METHODS A master model with one crown (maxillary left second premolar) was manufactured from Cr-Co alloy. The master model was scanned, and the data set was transferred to a CAD/CAM unit (Yenamak D50, Yenadent Ltd, Istanbul, Turkey) for the Cercon Base group. For the other groups, temporary crowns were produced by direct fabrication methods (Imident, Temdent, Structur Premium, Takilon, Systemp c&b II, and Acrytemp). The specimens were subjected to water storage at 37℃ for 24 hours, and then they were thermocycled (TC, 5000×, 5-55℃) (n=10). The maximum force at fracture (Fmax) was measured in a universal test machine at 1 mm/min. Data was analyzed by non-parametric statistics (α=.05). RESULTS Fmax values varied between 711.09-1392.1 N. In the PMMA groups, Takilon showed the lowest values (711.09 N), and Cercon Base showed the highest values (959.59 N). In the composite groups, Structur Premium showed the highest values (1392.1 N), and Acrytemp showed the lowest values (910.05 N). The composite groups showed significantly higher values than the PMMA groups (P=.01). CONCLUSION Composite-based materials showed significantly higher fracture strengths than PMMA-based materials. The CAD-CAM technique offers more advantages than the direct technique.

Effect of surface treatment and luting agent type on shear bond strength of titanium to ceramic materials

Isil Karaokutan,Gulsum Sayin Ozel 대한치과보철학회 2022 The Journal of Advanced Prosthodontics Vol.14 No.2

PURPOSE. This study aimed to compare the effect of different surface treatments and luting agent types on the shear bond strength of two ceramics to commercially pure titanium (Cp Ti). MATERIALS AND METHODS. A total of 160 Cp Ti specimens were divided into 4 subgroups (n = 40) according to surface treatments received (control, 50 μm airborne-particle abrasion, 110 μm airborne-particle abrasion, and tribochemical coating). The cementation surfaces of titanium and all-ceramic specimens were treated with a universal primer. Two cubic all-ceramic discs (lithium disilicate ceramic (LDC) and zirconia-reinforced lithium silicate ceramic (ZLC)) were cemented to titanium using two types of resin-based luting agents: self-cure and dual-cure (n = 10). After cementation, all specimens were subjected to 5000 cycles of thermal aging. A shear bond strength (SBS) test was conducted, and the failure mode was determined using a scanning electron microscope. Data were analyzed using three-way ANOVA, and the Tukey-HSD test was used for post hoc comparisons (P < .05). RESULTS. Significant differences were found among the groups based on surface treatment, resin-based luting agent, and ceramic type (P < .05). Among the surface treatments, 50 μm air-abrasion showed the highest SBS, while the control group showed the lowest. SBS was higher for dual-cure resin-based luting agent than self-cure luting agent. ZLC showed better SBS values than LDC. CONCLUSION. The cementation of ZLC with dual-cure resin-based luting agent showed better bonding effectiveness to commercially pure titanium treated with 50 μm airborne-particle abrasion.